Process for electrolytic graining of aluminum sheet
Assignee: Polychrome Corp
•
Filing: 1976-12-02
•
Granted: 1977-10-04
•
Expires: 1996-12-02
Abstract
Abstract A method for electrolytically graining the surface of aluminum sheets useful in the production in lithographic printing plates which comprises subjecting said aluminum sheets to the action of an electric current in an aqueous electrolytic solution containing, in combination, small but effective amounts of both hydrochloric and tartaric acids.
Inventors
- 👤 Robert Gumbinner
- 👤 Jen-Chi Huang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:55
CPC Classifications
B; B41; B41N; B41N3/00; B41N3/03; B41N3/034; C; C25; C25F; C25F3/00; C25F3/02; C25F3/04; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12993
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
86 words
A method for electrolytically graining aluminum which comprises immersing the aluminum in an aqueous electrolytic solution containing hydrochloric acid and tartaric acid as electrolytes, applying thereto an electric current having a current density in excess of 40 amperes per square foot and maintaining the electrolytic solution at a temperature of about 45° C wherein the tartaric acid is present in a concentration of from 0.2% to 1.0% by weight and wherein the hydrochloric acid is present in a concentration of from 0.75% to 3.5% by weight.
Claim 2
Independent Claim
86 words
A method for electrolytically graining aluminum which comprises immersing the aluminum in an aqueous electrolytic solution containing hydrochloric acid and tartaric acid as electrolytes, applying thereto an electric current having a current density in excess of 40 amperes per square foot and maintaining the electrolytic solution at a temperature of about 45° C wherein the tartaric acid is present in a concentration of from 0.2% to 1.0% by weight and wherein the hydrochloric acid is present in a concentration of from 0.75% to 3.5% by weight.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the electric current is applied at a current density of 50 to 500 amperes per square foot.
Claim 4
Dependent Claim
54 words
The method of claim 1 wherein the hydrochloric acid is present in a concentration of from 1.5% to 2.5% by weight; the tartaric acid is present in a concentration of from 0.3% to 0.75% by weight; and the current is applied at a current density of from 200 to 500 amperes per square foot.
Claim 5
Dependent Claim
24 words
The method of claim 1, wherein the temperature of the electrolytic solution is maintained at a temperature of from 45° C. to 75° C.
Claim 6
Dependent Claim
12 words
The grained aluminum product manufactured according to the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-10-03 | 1981-04-04 | 1981-10-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-10-03 | 1985-04-04 | 1985-10-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-10-03 | 1989-04-04 | 1989-10-04 | $7700.00 | Window Closed / Lapsed |