Ceramic products and method of drying same
Assignee: Owens Corning Fiberglas Technology Inc
•
Filing: 1980-11-07
•
Granted: 1982-12-21
•
Expires: 2000-11-07
Abstract
Abstract Ceramic products are produced containing a network of glass filaments having a hydrophilic surface. This network of filaments aids the transfer of water from the center of wet ceramic bodies to the surface thereof to speed up dewatering of slip cast materials while in the mold to thereby permit increased production from the molds. In addition, the fibers speed up oven drying of the green ware to give a further increase in production.
Inventors
- 👤 Richard F. Shannon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:33
CPC Classifications
C; C04; C04B; C04B33/00; C04B33/36
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
154 words
A method of producing clay, alumina or silica base ceramic products, comprising: adding chopped strand of mineral filaments having a hydrophilic surface into a green ware forming formulation that includes water, said filaments being bonded together into the strand by binder that is sufficiently water soluble that the strand is completely filamentizable when agitated in water; mixing the strand and formulation together under conditions which break the strand apart into individual monofilaments and disperse the monofilaments throughout the green ware forming formulation to give a three dimensional network of from 300 to 150,000 inches of filament per cubic inch; molding the mixture to form green ware under conditions preserving said three dimensional network; drying the green ware under conditions allowing the filaments to aid in moving water from the interior of the green ware to its surface; and firing the products above a temperature which fuses the green ware into a hard ceramic product.
Claim 2
Independent Claim
154 words
A method of producing clay, alumina or silica base ceramic products, comprising: adding chopped strand of mineral filaments having a hydrophilic surface into a green ware forming formulation that includes water, said filaments being bonded together into the strand by binder that is sufficiently water soluble that the strand is completely filamentizable when agitated in water; mixing the strand and formulation together under conditions which break the strand apart into individual monofilaments and disperse the monofilaments throughout the green ware forming formulation to give a three dimensional network of from 300 to 150,000 inches of filament per cubic inch; molding the mixture to form green ware under conditions preserving said three dimensional network; drying the green ware under conditions allowing the filaments to aid in moving water from the interior of the green ware to its surface; and firing the products above a temperature which fuses the green ware into a hard ceramic product.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein the monofilaments comprise from 0.05% to 0.5% by weight of the mixture solids.
Claim 4
Dependent Claim
11 words
The method of claim 2 wherein the monofilaments are glass fibers.
Claim 5
Dependent Claim
16 words
The method of claim 3 wherein the monofilaments have a length between 1/4 and 1 inch.
Claim 6
Independent Claim
155 words
A method of producing dried and fired clay, alumina or silica base products, comprising: adding chopped strand of mineral filaments having a hydrophilic surface into a green ware forming formulation that includes water, said filaments being bonded together into the strand by binder that is sufficiently water soluble that the strand is completely filamentizable when agitated in water; mixing the strand and formulation together under conditions which break the strand apart into individual monofilaments and disperse the monofilaments throughout the green ware forming formulation to give a three dimensional network of from 300 to 150,000 inches of monofilaments per cubic inch; molding the mixture to form green ware under conditions preserving said three dimensional network; drying the green ware under conditions allowing the filaments to aid in moving water from the interior of the green ware to its surface; and firing the green ware at a sufficiently elevated temperature to produce a hard fired product.
Claim 7
Independent Claim
155 words
A method of producing dried and fired clay, alumina or silica base products, comprising: adding chopped strand of mineral filaments having a hydrophilic surface into a green ware forming formulation that includes water, said filaments being bonded together into the strand by binder that is sufficiently water soluble that the strand is completely filamentizable when agitated in water; mixing the strand and formulation together under conditions which break the strand apart into individual monofilaments and disperse the monofilaments throughout the green ware forming formulation to give a three dimensional network of from 300 to 150,000 inches of monofilaments per cubic inch; molding the mixture to form green ware under conditions preserving said three dimensional network; drying the green ware under conditions allowing the filaments to aid in moving water from the interior of the green ware to its surface; and firing the green ware at a sufficiently elevated temperature to produce a hard fired product.
References Cited (Backward Citations)
US2681863A
Cited
US3062670A
Cited
US3289371A
Cited
US3147127A
Cited
US3948673A
Cited
US4187275A
Cited
US4118236A
Cited
US4185138A
Cited
US4200487A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-20 | 1986-06-21 | 1986-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-20 | 1990-06-21 | 1990-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-20 | 1994-06-21 | 1994-12-21 | $7700.00 | Window Closed / Lapsed |