Clay compositions
Assignee: ACI Australia Ltd
•
Filing: 1977-03-09
•
Granted: 1978-10-03
•
Expires: 1997-03-09
Abstract
Abstract A method of preparing a reinforced clay based article is described. A mixture of clay and reinforcement is shaped, dried and then fired at a temperature and for a time sufficient to stabilize the clay against redispersion in water, without forming a ceramic article.
Inventors
- 👤 Clive Arnold Erskine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:04
CPC Classifications
C; C04; C04B; C04B33/00; C04B33/36
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
171 words
A method of producing reinforced thin sectioned clay based articles, such as sheets, pipes or the like, having a modulus of rupture of at least 10 MPa and a modulus of elasticity no greater than 16 GPa, including the steps of forming a shaped mixture comprising the following ingredients in substantially the proportions specified by percentage weight of the total solids in the composition: Fibrous reinforcement selected from the group consisting of glass fibre, carbon fibre, mineral wool, ceramic fibre, asbestos or mixtures of two or more thereof -- 1% to 30% Clay selected from the group consisting of montmorillonitic clay, kaolinitic clay, illitic clay, or mixtures of two or more thereof -- 5% to 95% Fillers -- 0% to 90% Water -- 20% to 100% drying the shaped mixture, and firing the dried shapes at a temperature in the range of 500° C. to 800° C. for a time sufficient to produce substantial stabilisation against redispersion in water of the clay in the composition without forming a ceramic article therefrom.
Claim 2
Independent Claim
171 words
A method of producing reinforced thin sectioned clay based articles, such as sheets, pipes or the like, having a modulus of rupture of at least 10 MPa and a modulus of elasticity no greater than 16 GPa, including the steps of forming a shaped mixture comprising the following ingredients in substantially the proportions specified by percentage weight of the total solids in the composition: Fibrous reinforcement selected from the group consisting of glass fibre, carbon fibre, mineral wool, ceramic fibre, asbestos or mixtures of two or more thereof -- 1% to 30% Clay selected from the group consisting of montmorillonitic clay, kaolinitic clay, illitic clay, or mixtures of two or more thereof -- 5% to 95% Fillers -- 0% to 90% Water -- 20% to 100% drying the shaped mixture, and firing the dried shapes at a temperature in the range of 500° C. to 800° C. for a time sufficient to produce substantial stabilisation against redispersion in water of the clay in the composition without forming a ceramic article therefrom.
Claim 3
Dependent Claim
13 words
A method according to claim 1, wherein the composition contains 0% montmorillonitic clay.
Claim 4
Dependent Claim
14 words
A method according to claim 1, wherein the composition includes one or more deflocculants.
Claim 5
Dependent Claim
19 words
A method according to claim 1 wherein the firing temperature falls within the range 600° C. to 725° C.
Claim 6
Dependent Claim
27 words
A method according to claim 4 wherein the composition is dried for at least 11/2 hours at a temperature in excess of 100° C. prior to firing.
Claim 7
Dependent Claim
25 words
A method according to claim 1 wherein the maximum particle size of at least 95% of the composition solid components does not exceed 200 microns.
Claim 8
Dependent Claim
20 words
A method according to claim 6 wherein at least 20% of the particles are less than 2 microns in diameter.
Claim 9
Dependent Claim
20 words
A method according to claim 7 wherein 30% to 60% of the particles are less than 2 microns in diameter.
Claim 10
Dependent Claim
21 words
A method according to claim 1 wherein a glaze is applied to the clay based article after drying prior to firing.
Claim 11
Independent Claim
130 words
A method of producing a reinforced clay based article comprising forming a shaped mixture consisting essentially of the following ingredients in the proportions specified by percentage weight of the total solids in the composition:- Fibrous reinforcement -- 3% to 15% Montmorillonitic Clay -- 0% to 7% Kaolinitic Clay -- 20% to 80% Illitic Cay -- 20% to 80% Fillers -- 0% to 40% Water -- 30% to 35% drying the shaped mixture, and firing the dried shape at a temperature in the range 500° C. to 800° C., for a time sufficient to substantially stabilise the clay in the composition against redispersion in water, without forming a ceramic article therefrom, the sum total of clay in the composition falling within the range 40% to 80% by weight of total solids.
Claim 12
Independent Claim
130 words
A method of producing a reinforced clay based article comprising forming a shaped mixture consisting essentially of the following ingredients in the proportions specified by percentage weight of the total solids in the composition:- Fibrous reinforcement -- 3% to 15% Montmorillonitic Clay -- 0% to 7% Kaolinitic Clay -- 20% to 80% Illitic Cay -- 20% to 80% Fillers -- 0% to 40% Water -- 30% to 35% drying the shaped mixture, and firing the dried shape at a temperature in the range 500° C. to 800° C., for a time sufficient to substantially stabilise the clay in the composition against redispersion in water, without forming a ceramic article therefrom, the sum total of clay in the composition falling within the range 40% to 80% by weight of total solids.
Claim 13
Dependent Claim
29 words
A method according to claim 10 wherein the fibrous reinforcement is chosen from textile glass fibre, wool glass, carbon fibre, mineral wool, ceramic fibre and asbestos and mixtures thereof.
Claim 14
Dependent Claim
13 words
A method according to claim 11 wherein the fibrous reinforcement is E-glass fibre.
Claim 15
Dependent Claim
28 words
A method according to claim 10 wherein the fillers are chosen from talc, pulverized fuel ash, fine silica, diatomaceous earth, feldspars and blast furnace slag and mixtures thereof.
Claim 16
Dependent Claim
14 words
A method according to claim 10 wherein the composition includes one or more deflocculants.
Claim 17
Dependent Claim
27 words
A method according to claim 14 wherein the deflocculants are chosen from the group consisting of sodium hexametaphosphate, sodium silicate, sodium metasilicate, Dispex N40 and Orotan 850.
Claim 18
Dependent Claim
25 words
A method according to claim 10 wherein the composition includes one or more fluxes to increase surface hardness and reduce the rate of water absorption.
Claim 19
Dependent Claim
27 words
A method according to claim 16 wherein the flux or fluxes are present in the proportions 0.5% to 2% by weight of total solids in the composition.
Claim 20
Dependent Claim
19 words
A method according to claim 16 wherein the flux or fluxes are chosen from boric acid and lithium carbonate.
Claim 21
Dependent Claim
25 words
A method according to claim 10 wherein the composition includes water soluble cellulose derivatives and/or solutions of polyethylene oxide to improve plasticity and extrusion properties.
Claim 22
Dependent Claim
12 words
A method according to claim 10 wherein the montmorillonitic clay is bentonite.
Claim 23
Dependent Claim
124 words
A clay based article, in which total clay content falls within the range of 5% to 95% of total solids by weight prepared by forming a shaped mixture consisting essentially of the following ingredients in the proportions specified by percentage weight of the total solids in the composition: Fibrous reinforcement -- 1% to 30% Montmorillonitic Clay -- 0% to 14% Kaolinitic Clay -- 0% to 95% Illitic Clay -- 0% to 95% Fillers -- 0% to 90% Water -- 20% to 100% of drying the shaped mixture, and firing the dried shape at a temperature in the range 500° to 800° C., for a time sufficient to substantially stabilise the clay in the composition against redispersion in water, without forming a ceramic article therefrom.
Claim 24
Dependent Claim
124 words
A clay based article, in which total clay content falls within the range of 5% to 95% of total solids by weight prepared by forming a shaped mixture consisting essentially of the following ingredients in the proportions specified by percentage weight of the total solids in the composition: Fibrous reinforcement -- 1% to 30% Montmorillonitic Clay -- 0% to 14% Kaolinitic Clay -- 0% to 95% Illitic Clay -- 0% to 95% Fillers -- 0% to 90% Water -- 20% to 100% of drying the shaped mixture, and firing the dried shape at a temperature in the range 500° to 800° C., for a time sufficient to substantially stabilise the clay in the composition against redispersion in water, without forming a ceramic article therefrom.
Claim 25
Dependent Claim
43 words
A clay based article as claimed in claim 21 wherein the composition components, firing time and firing temperature are chosen such that a flat sheet produced thereby having a thickness of 4.5 mm has a modulus of rupture of at least 10 MPa.
Claim 26
Dependent Claim
23 words
A clay based article as claimed in claim 22 wherein the flat sheet has a modulus of rupture of at least 20 MPa.
Claim 27
Dependent Claim
15 words
A clay based article as claimed in claim 19 in the form of an extrusion.
Claim 28
Dependent Claim
36 words
A clay based article as claimed in claim 21 wherein the fibrous reinforcement is chosen from the group consisting of textile glass fibre, wool glass, carbon fibre, mineral wool, ceramic fibre and asbestos and mixtures thereof.
Claim 29
Dependent Claim
35 words
A clay based article as claimed in claim 21 wherein the fillers are chosen from the group consisting of talc, pulverised fuel ash, fine silica, diatomaceous earth, feldspars and blast furnace slag and mixtures thereof.
References Cited (Backward Citations)
GB1050985A
Cited
US2388060A
Cited
US2904267A
Cited
US2956893A
Cited
US3130063A
Cited
US3458329A
Cited
US4013476A
Cited
US3785838A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-02 | 1982-04-03 | 1982-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-02 | 1986-04-03 | 1986-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-02 | 1990-04-03 | 1990-10-03 | $7700.00 | Window Closed / Lapsed |