Method of producing silicon-iron sheet material with annealing atmospheres of nitrogen and hydrogen
Assignee: General Electric Co
•
Filing: 1981-01-12
•
Granted: 1982-07-06
•
Expires: 2001-01-12
Abstract
Abstract Silicon-iron sheet products having good magnetic properties can be produced from low nitrogen alloy sheet material by heating in a nitrogen-bearing hydrogen atmosphere to a temperature sufficient to effect secondary recrystallization and thereafter heating to a higher temperature in a hydrogen atmosphere to effect removal of residual carbon, nitrogen, and sulfur.
Inventors
- 👤 Howard C. Fiedler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:28
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/12; C21D8/1244; C21D8/1272; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; C21D8/1277; C21D8/1283
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
145 words
The method of producing grain oriented silicon-iron sheet comprising the steps of: (a) providing fine-grained, decarburized, and primary recrystallized silicon-iron intermediate product sheet material, said material containing from about 2.2% to about 4.5% silicon, boron, manganese up to about 0.10%, said material having a manganese-to-sulfur ratio of at least 2.1 and less than about 20 parts per million solute nitrogen; (b) covering said sheet with an electrically insulating boron-containing adherent coating; (c) heating said coated sheet in a first atmosphere comprising hydrogen and at least about 20 volume percent nitrogen to a first temperature developing thereby a cube-on-edge secondary recrystallization texture in said sheet; and (d) increasing the temperature of said sheet to a second temperature and holding said sheet at said second temperature in a second atmosphere consisting essentially of hydrogen for a predetermined time effecting thereby substantial removal of carbon, sulfur and nitrogen.
Claim 2
Independent Claim
145 words
The method of producing grain oriented silicon-iron sheet comprising the steps of: (a) providing fine-grained, decarburized, and primary recrystallized silicon-iron intermediate product sheet material, said material containing from about 2.2% to about 4.5% silicon, boron, manganese up to about 0.10%, said material having a manganese-to-sulfur ratio of at least 2.1 and less than about 20 parts per million solute nitrogen; (b) covering said sheet with an electrically insulating boron-containing adherent coating; (c) heating said coated sheet in a first atmosphere comprising hydrogen and at least about 20 volume percent nitrogen to a first temperature developing thereby a cube-on-edge secondary recrystallization texture in said sheet; and (d) increasing the temperature of said sheet to a second temperature and holding said sheet at said second temperature in a second atmosphere consisting essentially of hydrogen for a predetermined time effecting thereby substantial removal of carbon, sulfur and nitrogen.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said nitrogen in said first atmosphere is about 55% by volume.
Claim 4
Dependent Claim
47 words
The method of claim 1 wherein the boron content of said sheet material is from about 8 parts per million to about 13 parts per million and the amount of boron in said adherent coating available to said sheet is less than about 12 parts per million.
Claim 5
Dependent Claim
38 words
The method of claim 1 wherein the boron content of said sheet is about 12 parts per million and the boron in said adherent coating available to said sheet is between about 12 and 36 parts per million.
Claim 6
Dependent Claim
35 words
The method of claim 1 in which the total amount of boron in said sheet and the boron in said adherent coating available to said sheet is between about 20 and 50 parts per million.
Claim 7
Dependent Claim
13 words
The method of claim 1 wherein said first temperature is about 1050° C.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein said second temperature is about 1175° C. and said predetermined time is about three hours.
References Cited (Backward Citations)
US2413949A
Cited
US3054732A
Cited
US3905843A
Cited
US3905842A
Cited
US3930906A
Cited
US3957546A
Cited
US4010050A
Cited
US4168169A
Cited
US4186038A
Cited
US4173502A
Cited
US4116730A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-05 | 1986-01-04 | 1986-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-05 | 1990-01-04 | 1990-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-05 | 1994-01-04 | 1994-07-06 | $7700.00 | Window Closed / Lapsed |