Insulating tape for fabricating an insulating sleeve for electric conductors impregnated with a thermo-setting epoxy resin/acid anhydride mixture
Assignee: Siemens AG
•
Filing: 1981-02-11
•
Granted: 1982-06-22
•
Expires: 2001-02-11
Abstract
Abstract An insulating tape containing mica serves for manufacturing an insulating sleeve of electric conductors, impregnated with a thermo-setting epoxy resin mixture. The binder for cementing the mica is a self-hardening mixture with an accelerator for the impregnating resin mixture. In order that all kinds of epoxy resins can be used as impregnating resins, quaternary onium salts are added as accelerators to the epoxy resin used as the binder.
Inventors
- 👤 Walter Ihlein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:44
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/40; C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; H01B3/02; H01B3/04; H02; H02K; H02K3/00; H02K3/30; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/251; Y10T428/29; Y10T428/2911; Y10T428/31504; Y10T428/31511; Y10T428/31525; Y10T428/31529
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
147 words
An insulating tape for manufacturing an insulating sleeve for electric conductors and intended to be impregnated with a thermo-setting epoxy resin/acid anhydride hardener mixture, said tape comprising at least one layer of inorganic, breakdown-proof planar material, selected from the group consisting of mica flakes and thin mica films, applied to a flexible substrate, said layer or layers being cemented to the substrate and to each other with an epoxy resin binder containing as an accelerator for promoting the hardening reaction of the resin used for impregnation, a quaternary onium salt, said mixture of binder and accelerator forming a system which is self-hardening at the setting temperature of the thermo-setting impregnating resin, said epoxy resin binder and said accelerator being present, respectively, in amounts from about 3 to about 10% and from about 0.05 to about 3%, percents by weight of the total weight of the insulating tape.
Claim 2
Dependent Claim
147 words
An insulating tape for manufacturing an insulating sleeve for electric conductors and intended to be impregnated with a thermo-setting epoxy resin/acid anhydride hardener mixture, said tape comprising at least one layer of inorganic, breakdown-proof planar material, selected from the group consisting of mica flakes and thin mica films, applied to a flexible substrate, said layer or layers being cemented to the substrate and to each other with an epoxy resin binder containing as an accelerator for promoting the hardening reaction of the resin used for impregnation, a quaternary onium salt, said mixture of binder and accelerator forming a system which is self-hardening at the setting temperature of the thermo-setting impregnating resin, said epoxy resin binder and said accelerator being present, respectively, in amounts from about 3 to about 10% and from about 0.05 to about 3%, percents by weight of the total weight of the insulating tape.
Claim 3
Dependent Claim
79 words
The insulating tape according to claim 1 wherein said accelerator is a quaternary onium salt having the following structural formula: ##STR2## where: M is an atom of the fifth main group of the periodic system of the elements; R 1 , R 2 , R 3 and R 4 are the same or different aliphatic, aromatic, heterocyclic or arylaliphatic radicals and in which 3-radicals may belong jointly or also in pairs to heterocyclic rings, and X is an anion.
Claim 4
Dependent Claim
57 words
The insulating tape according to claim 2 wherein M is selected from the group consisting of nitrogen and phosphorous and X is an anion selected from the group consisting of Cl - , Br - , I - , F - , NO 3 - , ClO 4 - , an organic acid radical, and complex anions.
Claim 5
Dependent Claim
16 words
The insulating tape according to claim 1 wherein said accelerator is a polymeric quaternary onium salt.
Claim 6
Dependent Claim
59 words
The insulating tape according to claim 1 wherein said mixture of binder and accelerator further contains an admixture acting as a hardener which becomes effective only at the setting temperature of the thermo-setting epoxy resin/acid anhydride hardener mixture, the amount of said admixture being from about 0.05 to about 10% by weight, referred to the weight of the binder.
Claim 7
Dependent Claim
34 words
The insulating tape according to claim 5, wherein said admixture is insoluble in the binder to approximately 80° C. and has a sufficiently high melting point relative to the setting temperature of the resin.
Claim 8
Dependent Claim
13 words
The insulating tape according to claim 6 wherein said admixture is 2-phenyl-4,5-dihydroxymethyl imidazole.
Claim 9
Dependent Claim
28 words
The insulating tape according to claim 5 wherein said admixture is a complex compound or adduct which is decomposed only at the setting temperature into a hardening-effective component.
Claim 10
Dependent Claim
32 words
The insulating tape according to claim 5 wherein said admixture is an encapsulated hardener system which is released and becomes effective only at the setting temperature or through exchange with other compounds.
Claim 11
Dependent Claim
40 words
The insulating tape according to claim 5 wherein said admixture is a hardener system adsorbed on a substance having a large surface area which is released and becomes effective only at the setting temperature or through exchange with other compounds.
References Cited (Backward Citations)
US3647611A
Cited
DE2142571B1
Cited
US3841959A
Cited
US3868613A
Cited
US4026862A
Cited
US4128598A
Cited
US4168331A
Cited
US4265966A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |