Carboxylic acid storage stabilizers for latent catalyst cured epoxy resins
Assignee: Westinghouse Electric Corp
•
Filing: 1974-02-11
•
Granted: 1977-05-31
•
Expires: 1994-02-11
Abstract
Abstract A resinous composition, suitable for insulating electrical members, is made from a mixture containing about 100 parts of an epoxy resin, about 55 to 165 parts of an acid anhydride, an effective amount of a latent catalyst and about 1 to 20 parts of a carboxylic acid stabilizer selected from the group of acetic, propionic, butyric, isobutyric, valeric, caproic, heptanoic and hexanoic acids.
Inventors
- 👤 James D. B. Smith
- 👤 Robert N. Kauffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:57
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/40; C; C08; C08G; C08G59/00; C08G59/14; C08G59/1433; C08G59/1438; C08G59/145; C08G59/18; C08G59/20; C08G59/22; C08G59/226; C08G59/40; C08G59/42; C08G59/4292; C08G59/68; C08G59/688
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
156 words
A resinous composition suitable for insulating electrical members comprising by weight: (A) 100 parts of an epoxy resin containing more than one 1,2 epoxy group per molecule, (B) 55 to 165 parts of an anhydride of a polycarboxylic acid as a curing agent, (C) 1 to 20 parts of a mono-carboxylic acid selected from the group consisting of acetic, propionic, butyric, isobutyric, valeric, caproic, heptanoic and hexanoic acids as a stabilizer and, (D) an effective amount of a latent catalyst selected from the group consisting of amines, imidazoles and quaternary organic onium salts having the structural formula: ##EQU6## where M is selected from the group consisting of N and P, R 1 , R 2 , R 3 and R 4 are selected from the group consisting of alkyl and aryl radicals having 1 to 21 carbon atoms and X is selected from the group consisting of halogen, propionate, acetate, butyrate, isobutyrate and dimethyl phosphate radicals.
Claim 2
Dependent Claim
156 words
A resinous composition suitable for insulating electrical members comprising by weight: (A) 100 parts of an epoxy resin containing more than one 1,2 epoxy group per molecule, (B) 55 to 165 parts of an anhydride of a polycarboxylic acid as a curing agent, (C) 1 to 20 parts of a mono-carboxylic acid selected from the group consisting of acetic, propionic, butyric, isobutyric, valeric, caproic, heptanoic and hexanoic acids as a stabilizer and, (D) an effective amount of a latent catalyst selected from the group consisting of amines, imidazoles and quaternary organic onium salts having the structural formula: ##EQU6## where M is selected from the group consisting of N and P, R 1 , R 2 , R 3 and R 4 are selected from the group consisting of alkyl and aryl radicals having 1 to 21 carbon atoms and X is selected from the group consisting of halogen, propionate, acetate, butyrate, isobutyrate and dimethyl phosphate radicals.
Claim 3
Dependent Claim
40 words
The composition of claim 1, wherein the composition contains a latent catalyst selected from the group consisting of about 0.02 to 0.70 parts quaternary organic onium salt, about 0.05 to 0.3 parts amine and about 0.05 to 0.3 parts imidazole.
Claim 4
Dependent Claim
28 words
The composition of claim 1 wherein the epoxy resin comprises a resin selected from the group consisting of bisphenol A epoxy resins, novolac epoxy resins and mixtures thereof.
Claim 5
Dependent Claim
28 words
The composition of claim 3 also containing up to about 200 parts filler particles, of average particle sizes from about 10 to 300 microns, for 100 parts (A).
Claim 6
Dependent Claim
18 words
The composition of claim 3, wherein the epoxy resin contains up to about 70 parts epoxy reactive diluent.
Claim 7
Dependent Claim
92 words
The composition of claim 5 wherein the bisphenol A epoxy resin has an epoxy equivalent weight of from about 130 to 1200, the novolac epoxy resin has an epoxy equivalent weight of from about 100 to 500, the acid anhydride curing agent is selected from the group consisting of hexahydrophthalic anhydride, 1-methyl hexahydrophthalic anhydride, tetrahydrophthalic anhydride, 1-methyltetrahydrophthalic anhydride, phthalic anhydride, NADIC anhydride, NADIC methyl anhydride, pyromellitic dianhydride, polyazelaic polyanhydride, benzophenone tetracarboxylic acid dianhydride and mixtures thereof and the epoxy resin contains about 20 to 50 parts neopentyl glycol diglycidyl ether reaction diluent.
Claim 8
Dependent Claim
31 words
The combination of an electrical member and a cured body of resinous insulation applied to the member, wherein the improvement comprises the insulation comprising the cured resinous composition of claim 3.
Claim 9
Dependent Claim
45 words
The combination of an insulated electrical transformer comprising a magnetic core, electrical windings disposed about the magnetic core and having a body of cured resinous insulation applied to the electrical windings, wherein the improvement comprises the insulation comprising the cured resinous composition of claim 3.
Claim 10
Dependent Claim
154 words
A resinous composition suitable for insulating electrical members consisting essentially of by weight: (A) 100 parts of an epoxy resin containing more than one 1,2 epoxy group per molecule, (B) 55 to 165 parts of an anhydride of a polycarboxylic acid as a curing agent, (C) 0.02 to 0.70 parts of quaternary organic onium salt acting as a latent catalyst and having the structural formula: ##EQU7## where M is selected from the group consisting of N and P, R 1 , R 2 , R 3 and R 4 are selected from the group consisting of alkyl and aryl radicals having 1 to 21 carbon atoms and X is selected from the group consisting of halogen, propionate, acetate, butyrate, isobutyrate and dimethyl phosphate radicals, and (D) about 1 to 20 parts of a mono-carboxylic acid selected from the group consisting of acetic, propionic, butyric, isobutyric, valeric, caproic, heptanoic and hexanoic acids as a stabilizer.
Claim 11
Dependent Claim
154 words
A resinous composition suitable for insulating electrical members consisting essentially of by weight: (A) 100 parts of an epoxy resin containing more than one 1,2 epoxy group per molecule, (B) 55 to 165 parts of an anhydride of a polycarboxylic acid as a curing agent, (C) 0.02 to 0.70 parts of quaternary organic onium salt acting as a latent catalyst and having the structural formula: ##EQU7## where M is selected from the group consisting of N and P, R 1 , R 2 , R 3 and R 4 are selected from the group consisting of alkyl and aryl radicals having 1 to 21 carbon atoms and X is selected from the group consisting of halogen, propionate, acetate, butyrate, isobutyrate and dimethyl phosphate radicals, and (D) about 1 to 20 parts of a mono-carboxylic acid selected from the group consisting of acetic, propionic, butyric, isobutyric, valeric, caproic, heptanoic and hexanoic acids as a stabilizer.
Claim 12
Dependent Claim
80 words
The resinous composition of claim 9, wherein the epoxy resin comprises a resin selected from the group consisting of bisphenol A epoxy resins, novolac epoxy resins and mixtures thereof, said resin containing about 20 to 50 parts of at least one epoxy reactive diluent selected from the group consisting of phenyl glycidyl ether, butyl glycidyl ether, alkyl glycidyl ethers wherein the alkyl group contains from 5 to 12 carbons, vinyl cyclohexone dioxide, endodicyclopentadione dioxide, octylene oxide and neopentyl glycoldiglycidyl ether.
Claim 13
Dependent Claim
45 words
The composition of claim 9 wherein the acid anhydride curing agent is selected from the group consisting of hexahydrophthalic anhydride, 1-methyl hexahydrophthalic anhydride, tetrahydrophthalic anhydride, 1-methyltetrahydrophthalic anhydride, phthalic anhydride, NADIC anhydride, NADIC methyl anhydride, pyromellitic dianhydride, polyazelaic polyanhydride, benzophenone tetracarboxylic acid dianhydride and mixtures thereof.
Claim 14
Dependent Claim
31 words
The combination of an electrical member and a cured body of resinous insulation applied to the member, wherein the improvement comprises the insulation comprising the cured resinous composition of claim 9.
Claim 15
Dependent Claim
45 words
The combination of an insulated electrical transformer comprising a magnetic core, electrical windings disposed about the magnetic core and having a body of cured resinous insulation applied to the electrical windings, wherein the improvement comprises the insulation comprising the cured resinous composition of claim 9.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-30 | 1980-11-29 | 1981-05-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-30 | 1984-11-29 | 1985-05-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-30 | 1988-11-29 | 1989-05-31 | $7700.00 | Window Closed / Lapsed |