Heat treatment of steel and method for monitoring the treatment
Assignee: LAir Liquide SA pour lEtude et lExploitation des Procedes Georges Claude
•
Filing: 1979-12-28
•
Granted: 1982-03-30
•
Expires: 1999-12-28
Abstract
Abstract The present invention relates to improvements in processes for treatment of steel under a controlled atmosphere. Use is made of an atmosphere formed by a carrier gas comprising or containing industrially pure nitrogen and by an active gas formed by a hydrocarbon such as: CH 4 , C 4 H 10 , C 3 H 8 , C 2 H 4 , C 2 H 2 , C 2 H 6 , and by carbon monoxide fed in under the form of pure gas or obtained by decomposition of methanol, the treatment being performed between 750° and 1150° C. The invention is applicable to heating prior to hardening, to annealing, to carburization and to carbo-nitriding of steels.
Inventors
- 👤 Michel Kostelitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:11
CPC Classifications
C; C23; C23C; C23C8/00; C23C8/06; C23C8/28; C23C8/30; C23C8/32; C21; C21D; C21D1/00; C21D1/74; C21D1/76; C23C8/08; C23C8/20; C23C8/22
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
233 words
A process for the heat treatment of steel within a furnace, comprising the steps of forming a mixture of a carrier gas, an active gas and carbon monoxide, said carrier gas including nitrogen and having a proportion of O 2 less than 10 ppm, a proportion of H 2 O less than 10 ppm and a proportion of CO 2 less than 10 ppm, said active gas containing a hydrocarbon in a volumetric proportion between 0.2 and 30 percent of the mixture, selected from the group of compounds consisting of CH 4 , C 4 H 10 , C 3 H 8 , C 2 H 4 , C 2 H 2 and C 2 H 6 , said carbon monoxide being present in the mixture in a volumetric proportion between 0.1 and 30 percent; continuously directing a constant flow of said mixture into said furnace; maintaining the temperature of the steel in said furnace between 750° and 1150° C.; measuring the residual contents of hydrocarbon, of steam and of carbon dioxide gas in the atmosphere issuing from the furnace; predetermining the proportion of hydrocarbon in the atmosphere penetrating into the furnace in accordance with the relationship between the residual contents of hydrocarbon, steam and carbon dioxide gas, and the proportions of carbon introduced in the steel; and controlling the delivery of hydrocarbon penetrating into the furnace in accordance with the predetermined proportion.
Claim 2
Dependent Claim
233 words
A process for the heat treatment of steel within a furnace, comprising the steps of forming a mixture of a carrier gas, an active gas and carbon monoxide, said carrier gas including nitrogen and having a proportion of O 2 less than 10 ppm, a proportion of H 2 O less than 10 ppm and a proportion of CO 2 less than 10 ppm, said active gas containing a hydrocarbon in a volumetric proportion between 0.2 and 30 percent of the mixture, selected from the group of compounds consisting of CH 4 , C 4 H 10 , C 3 H 8 , C 2 H 4 , C 2 H 2 and C 2 H 6 , said carbon monoxide being present in the mixture in a volumetric proportion between 0.1 and 30 percent; continuously directing a constant flow of said mixture into said furnace; maintaining the temperature of the steel in said furnace between 750° and 1150° C.; measuring the residual contents of hydrocarbon, of steam and of carbon dioxide gas in the atmosphere issuing from the furnace; predetermining the proportion of hydrocarbon in the atmosphere penetrating into the furnace in accordance with the relationship between the residual contents of hydrocarbon, steam and carbon dioxide gas, and the proportions of carbon introduced in the steel; and controlling the delivery of hydrocarbon penetrating into the furnace in accordance with the predetermined proportion.
Claim 3
Dependent Claim
21 words
A process according to claim 1, wherein said carbon monoxide is fed into said mixture in the form of pure gas.
Claim 4
Dependent Claim
28 words
A process according to claim 1, wherein said carbon monoxide is fed into said mixture in the form of a partial nitrogen-carbon monoxide mixture in the gaseous state.
Claim 5
Dependent Claim
28 words
A process according to claim 1, wherein said carbon monoxide is fed into said mixture in the form of a partial nitrogen-carbon monoxide mixture in the liquid state.
Claim 6
Dependent Claim
35 words
A process according to claim 1, wherein said carbon monoxide originates from the decomposition under heat of methanol in accordance with the reaction CH 3 OH→CO+2H 2 , said methanol being fed into said mixture.
Claim 7
Dependent Claim
40 words
A process according to claim 1, wherein, in the case of a carbo-nitriding operation, said atmosphere is produced by admixing ammonia in a proportion of 0.1 to 30% by volume, apart from the aforesaid carrier gas, hydrocarbon and carbon monoxide.
Claim 8
Dependent Claim
143 words
The process for the heat treatment of steel within a furnace, according to claim 1, wherein said forming step includes forming a mixture consisting essentially of a carrier gas, an active gas and carbon monoxide, said carrier gas including nitrogen and having a proportion of O 2 less than 10 ppm, a proportion of H 2 O less than 10 ppm and a proportion of CO 2 less than 10 ppm, said active gas containing a hydrocarbon in a volumetric proportion between 0.2 and 30 percent of the mixture, selected from the group of compounds consisting of CH 4 , C 4 H 10 , C 3 H 8 , C 2 H 4 , C 2 H 2 and C 2 H 6 , and said carbon monoxide being present in the mixture in a volumetric proportion between 0.1 and 30 percent.
Claim 9
Dependent Claim
159 words
The process for the heat treatment of steel within a furnace, according to claim 1, wherein said forming step includes forming a mixture of a carrier gas, an active gas and carbon monoxide, said mixture being free of O 2 , H 2 O and CO 2 , except for said carrier gas which includes nitrogen and has a proportion of O 2 less than 10 ppm, a proportion of H 2 O less than 10 ppm, and a proportion of CO 2 less than 10 ppm, said active gas containing a hydrocarbon in a volumetric proportion between 0.2 and 30 percent of the mixture, selected from a group of compounds consisting of CH 4 , C 4 H 10 , C 3 H 8 , C 2 H 4 , C 2 H 2 and C 2 H 6 , and said carbon monoxide being present in the mixture in a volumetric proportion between 0.1 and 30 percent.
References Cited (Backward Citations)
US3011873A
Cited
US3240636A
Cited
US3693409A
Cited
US4035203A
Cited
GB1471627A
Cited
US4211584A
Cited
US3946817A
Cited
US4188242A
Cited
US4049472A
Cited
US4154629A
Cited
ZA782403B
Cited
US4145232A
Cited
US4175986A
Cited
US4208224A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-29 | 1985-09-28 | 1986-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-29 | 1989-09-28 | 1990-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-29 | 1993-09-28 | 1994-03-30 | $7700.00 | Window Closed / Lapsed |