Atmosphere compositions and methods of using same for surface treating ferrous metals
Assignee: Air Products and Chemicals Inc
•
Filing: 1975-12-22
•
Granted: 1977-09-20
•
Expires: 1995-12-22
Abstract
Abstract Atmosphere compositions and processes utilizing the compositions for heat treating ferrous metal articles under a controlled furnace atmosphere to either maintain or change the surface chemistry of the article being treated are disclosed in the following specification. The invention features atmosphere compositions or mixtures which are blended from normally gaseous components outside the furnace and the mixture or blend is injected into the furnace to provide a carburizing, decarburizing, carbonitriding or neutral hardening atmosphere inside the furnace.
Inventors
- 👤 Edward J. Arndt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:00
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/74; C21D1/76; C23; C23C; C23C8/00; C23C8/06; C23C8/08; C23C8/20; C23C8/22; C23C8/28; C23C8/30; C23C8/32
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
123 words
A gaseous mixture prepared at ambient temperature suitable for injecting into a ferrous metal treating furnace maintained at a temperature in excess of 1500° F. wherein ferrous metal parts are heated in a furnace atmosphere created by the gas mixture injected into the furnace, the atmosphere being variable to perform a treatment selected from the group consisting of carburizing, decarburizing, neutral hardening and carbonitriding, said mixture consisting essentially of 62 to 98% by volume substantially pure nitrogen; 1.5 to 30% by volume natural gas being substantially methane; 0.2 to 15% by volume substantially pure carbon dioxide; the natural gas and carbon dioxide being present in a ratio of 0.5 to 15.0 natural gas/carbon dioxide; and 0.0 to 10% by volume substantially pure ammonia.
Claim 2
Dependent Claim
123 words
A gaseous mixture prepared at ambient temperature suitable for injecting into a ferrous metal treating furnace maintained at a temperature in excess of 1500° F. wherein ferrous metal parts are heated in a furnace atmosphere created by the gas mixture injected into the furnace, the atmosphere being variable to perform a treatment selected from the group consisting of carburizing, decarburizing, neutral hardening and carbonitriding, said mixture consisting essentially of 62 to 98% by volume substantially pure nitrogen; 1.5 to 30% by volume natural gas being substantially methane; 0.2 to 15% by volume substantially pure carbon dioxide; the natural gas and carbon dioxide being present in a ratio of 0.5 to 15.0 natural gas/carbon dioxide; and 0.0 to 10% by volume substantially pure ammonia.
Claim 3
Dependent Claim
24 words
A mixture according to claim 1 wherein the quantity of methane plus carbon dioxide is between 2 and 23% by volume of the mixture.
Claim 4
Dependent Claim
58 words
A mixture according to claim 1 suitable for carburizing ferrous metal articles heated to a temperature of between 1600° and 1750° F. consisting essentially of 78.0 to 92.0% by volume nitrogen; 6.5 to 20.0% by volume methane; 1.4 to 14.0% by volume carbon dioxide; and wherein the methane/carbon dioxide ratio of the mixture is between 1.4 and 8.0.
Claim 5
Dependent Claim
19 words
A mixture according to claim 3 wherein the methane plus carbon dioxide is between 9.5 and 20% by volume.
Claim 6
Dependent Claim
58 words
A mixture according to claim 1 suitable for neutral hardening ferrous metal articles heated to a temperature between 1500° and 1650° F. consisting essentially of: 91.0 to 98.0% by volume nitrogen; 1.5 to 7.5% by volume methane; 0.2 to 2.0% by volume carbon dioxide; and wherein the methane/carbon dioxide ratio of the mixture is between 1.7 and 9.0.
Claim 7
Dependent Claim
19 words
A mixture according to claim 5 wherein the methane plus carbon dioxide is between 2 and 9.0% by volume.
Claim 8
Dependent Claim
57 words
A mixture according to claim 1 suitable for decarburizing ferrous metal articles heated to a temperature in excess of 1550° F. consisting essentially of: 82.0 to 90.0% by volume nitrogen; 3.3 to 15.0% by volume methane; 1.7 to 12.0% by volume carbon dioxide; and wherein the ratio of methane to carbon dioxide in between 0.5 and 5.0.
Claim 9
Dependent Claim
22 words
A mixture according to claim 7 wherein the methane plus carbon dioxide is between 10 and 18% by volume of the mixture.
Claim 10
Dependent Claim
36 words
A mixture according to claim 1 suitable for carbonitriding ferrous metal articles heated to a temperature between 1550° and 1650° F. consisting essentially of: 62.0 to 90% by volume nitrogen; 6.0 to 29.0% by volume methane;
Claim 11
Dependent Claim
27 words
0 to 3.5% by volume carbon dioxide; 1.5 to 10.0% by volume ammonia; and wherein the ratio of methane to carbon dioxide is between 3.0 and 13.5.
Claim 12
Dependent Claim
27 words
0 to 3.5% by volume carbon dioxide; 1.5 to 10.0% by volume ammonia; and wherein the ratio of methane to carbon dioxide is between 3.0 and 13.5.
Claim 13
Dependent Claim
19 words
A composition according to claim 9 wherein the methane plus carbon dioxide in between 9.6 and 30.0% by volume.
Claim 14
Independent Claim
199 words
A method of heat treating ferrous articles in a furnace raised to an elevated temperature and under a furnace atmosphere that can be varied to be classified as carburizing, decarburizing, neutral or carbonitriding in character comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F.; b. mixing outside the furnace at ambient temperature a gas composition consisting essentially of 65 to 98% by volume nitrogen, 1.5 to 30% by volume natural gas being substantially methane; 0.2 to 15% by volume substantially pure carbon dioxide, 0.0 to 10% by volume substantially pure ammonia, the natural gas and carbon dioxide being present in a ratio of 0.5 to 15.0 natural gas/carbon dioxide; c. injecting said mixture into said furnace to form a furnace atmosphere as the articles are being heated; d. maintaining said articles at a temperature in the presence of said furnace atmosphere until said parts are in thermal equilibrium with said furnace; e. continuing said heating under atmosphere until said parts have been treated by said atmosphere according to the nature of the atmosphere present in said furance; and f. cooling said articles to ambient temperature.
Claim 15
Independent Claim
199 words
A method of heat treating ferrous articles in a furnace raised to an elevated temperature and under a furnace atmosphere that can be varied to be classified as carburizing, decarburizing, neutral or carbonitriding in character comprising the steps of: a. charging the articles to be treated into a furnace maintained at a temperature in excess of 1500° F.; b. mixing outside the furnace at ambient temperature a gas composition consisting essentially of 65 to 98% by volume nitrogen, 1.5 to 30% by volume natural gas being substantially methane; 0.2 to 15% by volume substantially pure carbon dioxide, 0.0 to 10% by volume substantially pure ammonia, the natural gas and carbon dioxide being present in a ratio of 0.5 to 15.0 natural gas/carbon dioxide; c. injecting said mixture into said furnace to form a furnace atmosphere as the articles are being heated; d. maintaining said articles at a temperature in the presence of said furnace atmosphere until said parts are in thermal equilibrium with said furnace; e. continuing said heating under atmosphere until said parts have been treated by said atmosphere according to the nature of the atmosphere present in said furance; and f. cooling said articles to ambient temperature.
Claim 16
Dependent Claim
24 words
A method according to claim 11 wherein substantially pure nitrogen is injected into said furnace until said articles reach the temperature of the furnace.
Claim 17
Dependent Claim
26 words
A method according to claim 11 wherein the ratio of methane to carbon dioxide in the mixture injected into the furnace is between 1.2 and 15.0.
Claim 18
Dependent Claim
65 words
A method according to claim 11 wherein the articles are subjected to a carburizing treatment by maintaining the furnace at a temperature of between 1650° and 1750° F. and injecting an atmosphere into the furnace consisting essentially of 80 to 90% by volume nitrogen balance, a mixture of methane, plus carbon dioxide wherein the ratio of methane to carbon dioxide is between 1.4 and 8.0.
Claim 19
Dependent Claim
65 words
A method according to claim 11 wherein the articles are subjected to a neutral hardening treatment by maintaining the furnace at a temperature between 1500° and 1650° F. and injecting an atmosphere into the furnace consisting essentially of 91 to 98% by volume nitrogen balance a mixture of methane and carbon dioxide wherein the ratio of methane to carbon dioxide is between 1.7 and 9.0.
Claim 20
Dependent Claim
64 words
A method according to claim 11 wherein the articles are subjected to a decarburizing treatment by maintaining the furnace at a temperature between 1550° and 1750° F. and injecting into the furnace an atmosphere consisting essentially of 82 to 90% by volume nitrogen, balance a mixture of methane and carbon dioxide wherein the ratio of methane to carbon dioxide is between 0.5 and 5.0.
Claim 21
Dependent Claim
69 words
A method according to claim 11 wherein the articles are subjected to a carbonitriding treatment by maintaining the furnace at a temperature of between 1550° and 1650° F. and injecting into the furnace an atmosphere consisting essentially of 62 to 90% by volume nitrogen, 1.5 to 10.0% by volume ammonia, balance methane plus carbon dioxide present in a ratio of methane to carbon dioxide of between 3.0 and 13.5.
Claim 22
Dependent Claim
35 words
A method according to claim 17 wherein the articles being treated are brought to the temperature of the furnace under an atmosphere of substantially nitrogen gas and then heated under the carbonitriding atmosphere at temperature.
Claim 23
Dependent Claim
26 words
A method according to claim 11 wherein a gas selected from the group consisting of argon, helium and rare inert gases is substituted for the nitrogen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-19 | 1981-03-21 | 1981-09-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-19 | 1985-03-21 | 1985-09-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-19 | 1989-03-21 | 1989-09-20 | $7700.00 | Window Closed / Lapsed |