Plasma etching of silicon
Assignee: AT&T Inc
•
Filing: 1980-04-07
•
Granted: 1982-01-12
•
Expires: 2000-04-07
Abstract
Abstract By utilizing a fluorine-containing gaseous compound in a plasma etching process, isotropic etching of monocrystalline silicon (48) and doped or undoped polycrystalline silicon (54) is achieved. The etching processes, which are applicable, for example, to pattern delineation in the processing of semiconductor wafers, are substantially free of any proximity effects and are characterized by a high etching rate at relatively low power levels, high selectivity (with respect to, for example, silicon dioxide) and excellent uniformity. By mixing other gases (for example, chlorine) with the fluorine-containing gas, the amount of undercutting achieved during the etching process can be selectively controlled.
Inventors
- 👤 Daniel L. Flamm
- 👤 Dan Maydan
- 👤 David N. Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:16
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/242; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
154 words
A method for fabricating a microminiature device in accordance with a process sequence that includes at least one step in which a silicon surface of the device is to be etched with high selectivity relative to other surfaces of the device in a dry etching apparatus that comprises a plasma established between anode and cathode electrodes one of which electrodes holds the device to be etched, the plasma resulting from imposition of an electric field across a gaseous environment introduced between said electrodes, CHARACTERIZED IN THAT the gaseous environment comprises a fluorine-containing gaseous compound that provides in said apparatus under the influence of said electric field silicon-etching fluorine species and reaction products that do not etch said other surfaces of said device to any substantial extent relative to the etching of said silicon surface, wherein said gaseous compound is selected from the group consisting of chlorine trifluoride, nitrogen trifluoride, bromine trifluoride and iodine trifluoride.
Claim 2
Independent Claim
154 words
A method for fabricating a microminiature device in accordance with a process sequence that includes at least one step in which a silicon surface of the device is to be etched with high selectivity relative to other surfaces of the device in a dry etching apparatus that comprises a plasma established between anode and cathode electrodes one of which electrodes holds the device to be etched, the plasma resulting from imposition of an electric field across a gaseous environment introduced between said electrodes, CHARACTERIZED IN THAT the gaseous environment comprises a fluorine-containing gaseous compound that provides in said apparatus under the influence of said electric field silicon-etching fluorine species and reaction products that do not etch said other surfaces of said device to any substantial extent relative to the etching of said silicon surface, wherein said gaseous compound is selected from the group consisting of chlorine trifluoride, nitrogen trifluoride, bromine trifluoride and iodine trifluoride.
Claim 3
Dependent Claim
43 words
A method as in claim 1, wherein the silicon surfce of said device has a patterned masking layer thereon, said device is mounted on the cathode electrode of said apparatus, and the etching of said silicon surface is controlled to be completely isotropic.
Claim 4
Dependent Claim
31 words
A method as in claim 1 wherein the gaseous environment comprises said fluorine-containing gaseous compound and an additional constituent selected from the group consisting of an inert gas, chlorine, and fluorine.
Claim 5
Dependent Claim
47 words
A method as in claim 3 wherein the gaseous environment comprises said fluorine-containing gaseous compound and chlorine, and the etching of said silicon surface is controlled to be isotropic with the maximum extent of lateral undercutting decreasing as the volume percent of said chlorine constituent is increased.
Claim 6
Dependent Claim
39 words
A method as in claim 1 wherein a pressure of approximately 2-to-500 microns is established in said apparatus and a power density of 0.01-to-1 watt per square centimeter is established at the surface of the device to be etched.
Claim 7
Dependent Claim
62 words
A method as in claim 1 wherein the device to be etched is mounted on the driven cathode electrode of a multifaceted plasma-assisted etching apparatus, said gaseous environment comprises chlorine trifluoride, a pressure of 50 microns is established in said apparatus and a power density of 0.04 watts per square centimeter is established at the surface of the device to be etched.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-11 | 1985-07-13 | 1986-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-11 | 1989-07-13 | 1990-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-11 | 1993-07-13 | 1994-01-12 | $7700.00 | Window Closed / Lapsed |