US4305973A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laser annealed double conductor structure
Assignee: Raytheon Co
•
Filing: 1979-07-24
•
Granted: 1981-12-15
•
Expires: 1999-07-24
Abstract
Abstract In double conductor micro-electronic structures, prior to the low temperature deposition or growth of an insulating layer over a polycrystalline or amorphous surface, the surface is annealed using a beam of radiant energy, which causes it to become very smooth, thereby removing any surface spikes. The insulating layer placed thereover has remarkably improved insulation qualities heretofore unattainable at low temperatures. The beam of radiant energy is preferably applied in bursts of energy lasting for a sufficiently short duration so that implanted impurities in the silicon substrate do not redistribute.
Inventors
- 👤 Giora Yaron
- 👤 LaVerne D. Hess
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 13:50
CPC Classifications
H; H10; H10P; H10P95/00; H10D; H10D64/00; H10D64/01; H10D64/031; H10D64/035; H10P34/00; H10P34/40; H10P34/42; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/067; H10W20/068; Y; Y10; Y10S; Y10S148/00; Y10S148/091; Y10S148/093; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
116 words
A method for growing improved oxide over a polycrystalline silicon layer overlying a silicon substrate, said substrate having dopant impurities, comprising: depositing a polycrystalline silicon layer over said substrate; exposing said polycrystalline silicon layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said polycrystalline silicon layer, said energy beam being of sufficiently short duration to prevent substantial redistribution of said impurities; and, growing silicon dioxide over said polycrystalline silicon layer at a sufficiently low temperature to prevent substantial redistribution of said impurities, said silicon dioxide having a susceptibility to leakage current therethrough which is reduced in proportion to the previous removal of said surface defects by said exposing step.
Claim 2
Independent Claim
116 words
A method for growing improved oxide over a polycrystalline silicon layer overlying a silicon substrate, said substrate having dopant impurities, comprising: depositing a polycrystalline silicon layer over said substrate; exposing said polycrystalline silicon layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said polycrystalline silicon layer, said energy beam being of sufficiently short duration to prevent substantial redistribution of said impurities; and, growing silicon dioxide over said polycrystalline silicon layer at a sufficiently low temperature to prevent substantial redistribution of said impurities, said silicon dioxide having a susceptibility to leakage current therethrough which is reduced in proportion to the previous removal of said surface defects by said exposing step.
Claim 3
Dependent Claim
23 words
The method of claim 1 further comprising initially growing a lower layer of silicon dioxide on said silicon substrate before said depositing step.
Claim 4
Independent Claim
31 words
The method of claims 1 or 2 wherein said exposing step comprises directing a pulsed laser beam having a pulse duration of less than 100 nanoseconds at said polycrystalline silicon layer.
Claim 5
Dependent Claim
54 words
The method of claim 3 wherein said exposing step comprises directing a pulsed ruby laser beam at said polycrystalline silicon layer, said beam having a wavelength of approximately 6943 angstroms, an energy density of approximately one joule/cm 2 , a beam diameter of approximately 6 millimeters and a pulse duration of approximately 20 nanoseconds.
Claim 6
Independent Claim
134 words
A method for fabricating a metal oxide semiconductor device having a polycrystalline silicon layer and a conductor overlying said layer, said device having improved insulation between said polycrystalline silicon layer and said overlying conductor, comprising: forming a layer of polycrystalline silicon; exposing said polycrystalline silicon layer to a beam of energy of sufficient magnitude to smooth surface defects in said polycrystalline silicon layer; growing a film of silicon dioxide over said polycrystalline silicon layer at a sufficiently low temperature to prevent substantial thermal changes in said metal oxide semiconductor device, said silicon dioxide film having a susceptibility to leakage currents therethrough which is reduced in proportion to the previous smoothing of said surface defects by said exposing step; and depositing a conductor on said silicon dioxide layer, said conductor overlying said polycrystalline silicon layer.
Claim 7
Independent Claim
134 words
A method for fabricating a metal oxide semiconductor device having a polycrystalline silicon layer and a conductor overlying said layer, said device having improved insulation between said polycrystalline silicon layer and said overlying conductor, comprising: forming a layer of polycrystalline silicon; exposing said polycrystalline silicon layer to a beam of energy of sufficient magnitude to smooth surface defects in said polycrystalline silicon layer; growing a film of silicon dioxide over said polycrystalline silicon layer at a sufficiently low temperature to prevent substantial thermal changes in said metal oxide semiconductor device, said silicon dioxide film having a susceptibility to leakage currents therethrough which is reduced in proportion to the previous smoothing of said surface defects by said exposing step; and depositing a conductor on said silicon dioxide layer, said conductor overlying said polycrystalline silicon layer.
Claim 8
Independent Claim
117 words
A method for placing improved insulation over a material layer overlying a substrate wherein said material layer comprises one of an amorphous material and a polycrystalline material, said method comprising: first placing said material layer over said substrate; exposing said material layer to a beam of energy of sufficient magnitude to smooth surface defects in said material layer; second placing an insulating film over said material layer at a sufficiently low temperature to prevent substantial thermal changes in said substrate, said insulating film having a susceptibility to leakage currents therethrough which is reduced in proportion to the previous smoothing of said surface defects by said exposing step; and third placing a conductor layer over said insulating film.
Claim 9
Independent Claim
117 words
A method for placing improved insulation over a material layer overlying a substrate wherein said material layer comprises one of an amorphous material and a polycrystalline material, said method comprising: first placing said material layer over said substrate; exposing said material layer to a beam of energy of sufficient magnitude to smooth surface defects in said material layer; second placing an insulating film over said material layer at a sufficiently low temperature to prevent substantial thermal changes in said substrate, said insulating film having a susceptibility to leakage currents therethrough which is reduced in proportion to the previous smoothing of said surface defects by said exposing step; and third placing a conductor layer over said insulating film.
Claim 10
Dependent Claim
24 words
The method of claim 6 further comprising initially growing a lower layer of silicon dioxide on said silicon substrate before said first placing step.
Claim 11
Dependent Claim
28 words
The method of claim 6 wherein said exposing step comprises directing a pulsed laser beam having a pulse duration of less than 100 nanoseconds at said material layer.
Claim 12
Dependent Claim
53 words
The method of claim 8 wherein said exposing step comprises directing a pulsed ruby laser beam at said material layer, said beam having a wavelength of approximately 6943 angstroms, an energy density of approximately one joule/cm 2 , a beam diameter of approximately 6 millimeters and a pulse duration of approximately 20 nanoseconds.
Claim 13
Independent Claim
27 words
The method of claims 6, 7, 8 or 9 wherein at least one of said first and third placing steps comprises depositing a layer of polycrystalline silicon.
Claim 14
Independent Claim
26 words
The method of claims 6, 7, 8 or 9 wherein at least one of said first and third placing steps comprises depositing a layer of polycide.
Claim 15
Independent Claim
27 words
The method of claims 6, 7, 8 or 9 wherein at least one of said first and third placing steps comprises depositing a layer of metal silicide.
Claim 16
Independent Claim
26 words
The method of claims 6, 7, 8 or 9 wherein at least one of said first and third placing steps comprises depositing a refractory metal layer.
Claim 17
Independent Claim
21 words
The method of claims 6, 7, 8 or 9 wherein said second placing step comprises depositing a layer of silicon dioxide.
Claim 18
Independent Claim
21 words
The method of claims 6, 7, 8 or 9 wherein said second placing step comprises growing a layer of silicon dioxide.
Claim 19
Independent Claim
21 words
The method of claims 6, 7, 8 or 9 wherein said second placing step comprises depositing a layer of silicon nitride.
Claim 20
Independent Claim
20 words
The method of claims 6, 7, 8 or 9 wherein said second placing step comprises depositing a layer of polymide.
Claim 21
Independent Claim
25 words
The method of claims 6, 7, 8 or 9 wherein at least one of said first and third placing steps comprises depositing an aluminum layer.
Claim 22
Independent Claim
24 words
The method of claims 6, 7, 8 or 9 further comprising depositing an aluminum layer over said insulating film after said second placing step.
Claim 23
Dependent Claim
20 words
The method of claim 6 wherein said exposing step comprises directing a pulsed electron beam source at said material layer.
Claim 24
Dependent Claim
28 words
The method of claim 6 wherein said exposing step comprises directing a continuous electron beam source at said material layer and scanning said beam across said material layer.
Claim 25
Dependent Claim
20 words
The method of claim 6 wherein said exposing step comprises directing a pulsed ion beam source at said material layer.
Claim 26
Dependent Claim
28 words
The method of claim 6 wherein said exposing step comprises directing a continuous ion beam source at said material layer and scanning said beam across said material layer.
Claim 27
Dependent Claim
20 words
The method of claim 6 wherein said exposing step comprises directing a scanning continuous laser beam at said material layer.
Claim 28
Independent Claim
40 words
The method of claims 6, 7, 8 or 9 wherein said second placing step comprises growing an insulating layer over said material layer at a temperature sufficiently low so as to avoid substantially altering the radiation hardness of said substrate.
Claim 29
Independent Claim
103 words
A method for placing improved insulation over an amorphous material overlying a substrate, comprising: first placing an amorphous material layer over said substrate; exposing said amorphous material layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said amorphous layer; and second placing an insulating film over said amorphous material layer at a sufficiently low temperature so as to prevent thermal changes from occuring in said substrate during said second placing step, said insulating film having a susceptibility to leakage currents which is reduced in proportion to said removal of said surface defects by said exposing step.
Claim 30
Independent Claim
103 words
A method for placing improved insulation over an amorphous material overlying a substrate, comprising: first placing an amorphous material layer over said substrate; exposing said amorphous material layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said amorphous layer; and second placing an insulating film over said amorphous material layer at a sufficiently low temperature so as to prevent thermal changes from occuring in said substrate during said second placing step, said insulating film having a susceptibility to leakage currents which is reduced in proportion to said removal of said surface defects by said exposing step.
Claim 31
Independent Claim
103 words
A method for placing improved insulation over a polycrystalline material overlying a substrate, comprising: first placing a polycrystalline material layer over said substrate; exposing said polycrystalline material layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said polycrystalline material layer; and second placing an insulating film over said polycrystalline material layer at a temperature sufficiently low so as to substantially prevent thermal changes in said substrate during said second placing step, said insulating film having a susceptibility to leakage currents which is reduced in proportion to said removal of said surface defects by said exposing step.
Claim 32
Independent Claim
103 words
A method for placing improved insulation over a polycrystalline material overlying a substrate, comprising: first placing a polycrystalline material layer over said substrate; exposing said polycrystalline material layer to a beam of energy of sufficient magnitude to cause removal of surface defects in said polycrystalline material layer; and second placing an insulating film over said polycrystalline material layer at a temperature sufficiently low so as to substantially prevent thermal changes in said substrate during said second placing step, said insulating film having a susceptibility to leakage currents which is reduced in proportion to said removal of said surface defects by said exposing step.
References Cited (Backward Citations)
US3475234A
Cited
US4151008A
Cited
US4131487A
Cited
US4187126A
Cited
US4214918A
Cited
US4198246A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-14 | 1989-06-15 | 1989-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-14 | 1993-06-15 | 1993-12-15 | $7700.00 | Window Closed / Lapsed |