Line-of-sight deposition method
Assignee: United States Department of Energy
•
Filing: 1980-04-16
•
Granted: 1981-12-15
•
Expires: 2000-04-16
Abstract
Abstract A line-of-sight method of depositing a film having substantially 100% of theoretical density on a substrate. A pressure vessel contains a target source having a surface thereof capable of emitting particles therefrom and a substrate with the source surface and the substrate surface positioned such that the source surface is substantially parallel to the direction of the particles impinging upon the substrate surface, the distance between the most remote portion of the substrate surface receiving the particles and the source surface emitting the particles in a direction parallel to the substrate surface being relatively small. The pressure in the vessel is maintained less than about 5 microns to prevent scattering and permit line-of-sight deposition. By this method the angles of incidence of the particles impinging upon the substrate surface are in the range of from about 45° to 90° even when the target surface area is greatly expanded to increase the deposition rate.
Inventors
- 👤 James W. Patten
- 👤 Edwin D. McClanahan
- 👤 Michael A. Bayne
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:54
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/04; C23C14/042; C23C14/22
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
129 words
In a method of depositing a dense film of material on a substrate from a source of material at low pressure, said method comprising providing a source of material having a surface thereof capable of emitting particles therefrom and a substrate within a pressure vessel maintained at a pressure of less than about 5 microns, positioning the surface of the substrate receiving the particles substantially perpendicular to the source surface, and causing particles of the material to leave the source surface and impinge upon said substrate surface, the improvement comprising interposing a mask having an opening therein between said source and substrate so that all particles impinging on said substrate surface directly from said source have an angle of incidence to the substrate surface of between 60° to 90°.
Claim 2
Dependent Claim
129 words
In a method of depositing a dense film of material on a substrate from a source of material at low pressure, said method comprising providing a source of material having a surface thereof capable of emitting particles therefrom and a substrate within a pressure vessel maintained at a pressure of less than about 5 microns, positioning the surface of the substrate receiving the particles substantially perpendicular to the source surface, and causing particles of the material to leave the source surface and impinge upon said substrate surface, the improvement comprising interposing a mask having an opening therein between said source and substrate so that all particles impinging on said substrate surface directly from said source have an angle of incidence to the substrate surface of between 60° to 90°.
Claim 3
Dependent Claim
25 words
The method of claim 1, wherein said source and said substrate are maintained at pressures less than about 3 microns during deposition of the film.
Claim 4
Dependent Claim
41 words
The method of claim 1, and further providing relative movement between said source and said substrate surface while interposing said mask therebetween so that said particles impinge upon the substrate surface at an incidence angle substantially perpendicular to said substrate surface.
Claim 5
Independent Claim
173 words
A method of depositing a dense film of material on a substrate from a source of the material at a pressure of less than about 5 microns, said method comprising providing a source of material having a surface capable of emitting particles therefrom and a substrate within a pressure vessel maintained at said pressure, the substrate surface receiving the particles and the source surface being positioned substantially perpendicular to each other and such that θ is in the range of about 1° to about 5° and θ is the angle between A and B where: A is a straight line between a point on the substrate surface most remote from the source surface and a point on the source surface most remote from the substrate surface and B is a straight line between a point on the substrate surface most remote from the source surface and a point on the source surface closest to the substrate surface, and causing particles of the material to leave said surface and impinge upon said substrate surface.
Claim 6
Independent Claim
173 words
A method of depositing a dense film of material on a substrate from a source of the material at a pressure of less than about 5 microns, said method comprising providing a source of material having a surface capable of emitting particles therefrom and a substrate within a pressure vessel maintained at said pressure, the substrate surface receiving the particles and the source surface being positioned substantially perpendicular to each other and such that θ is in the range of about 1° to about 5° and θ is the angle between A and B where: A is a straight line between a point on the substrate surface most remote from the source surface and a point on the source surface most remote from the substrate surface and B is a straight line between a point on the substrate surface most remote from the source surface and a point on the source surface closest to the substrate surface, and causing particles of the material to leave said surface and impinge upon said substrate surface.
Claim 7
Dependent Claim
47 words
The method of claim 4, wherein the pressure within said pressure vessel is less than about 3 microns, and an ion plasma is established and maintained within the pressure vessel sufficient to cause an adatom flux to leave the source surface and impinge upon the substrate surface.
Claim 8
Dependent Claim
33 words
The method of claim 4, wherein the substrate surface and the source surface are positioned such that the source surface is substantially parallel to the directions of the particles impinging the substrate surface.
Claim 9
Independent Claim
169 words
A method of depositing a dense film material on a substrate from a source of the material, said method comprising providing a pressure vessel housing a source of material having a plane surface thereof capable of emitting an adatom flux therefrom and a substrate, positioning the source surface and the substrate surface such that the plane of the source surface is substantially parallel to the direction of the particles impinging upon the substrate surface, the distance between the most remote point of said substrate surface receiving the adatom flux and the plane of said source surface emitting the adatom flux as measured in a direction perpendicular to the source surface being about 1/8 inch, and establishing and maintaining an ion plasma within said pressure vessel at a pressure of less than about 5 microns sufficient to cause an adatom flux to leave said source surface and impinge upon said substrate surface to deposit a coating at close to theoretical density at a rate of about 1 mil per hour.
Claim 10
Independent Claim
169 words
A method of depositing a dense film material on a substrate from a source of the material, said method comprising providing a pressure vessel housing a source of material having a plane surface thereof capable of emitting an adatom flux therefrom and a substrate, positioning the source surface and the substrate surface such that the plane of the source surface is substantially parallel to the direction of the particles impinging upon the substrate surface, the distance between the most remote point of said substrate surface receiving the adatom flux and the plane of said source surface emitting the adatom flux as measured in a direction perpendicular to the source surface being about 1/8 inch, and establishing and maintaining an ion plasma within said pressure vessel at a pressure of less than about 5 microns sufficient to cause an adatom flux to leave said source surface and impinge upon said substrate surface to deposit a coating at close to theoretical density at a rate of about 1 mil per hour.
Claim 11
Dependent Claim
40 words
The method of claim 7, wherein the source surface and the substrate surface are positioned such that the angles of incidence of the particles impinging upon the substrate surface are in the range of from about 60° to about 90°.
Claim 12
Dependent Claim
100 words
The method of claim 7, wherein the substrate surface and the source surface are positioned such that θ is in the range of about 1° to about 5° and θ is the angle between A and B where: A is a straight line between a point on the substrate surface most remote from the source surface and a point on the source surface most remote from the substrate surface and B is a straight line between a point on the substrate surface most remote fromm the source surface and a point on the source surface closest to the substrate surface.
Claim 13
Dependent Claim
32 words
The method of claim 7, wherein the distance between the source surface and the substrate surface in a direction perpendicular to the substrate surface is up to about two means free paths.
Claim 14
Dependent Claim
32 words
The method of claim 7, wherein relative movement is provided between said source and said substrate and a mask is provided intermediate said source and said substrate having a defined opening therein.
Claim 15
Dependent Claim
16 words
The method of claim 11, wherein relative movement is provided between said mask and said source.
Claim 16
Dependent Claim
33 words
The method according to claim 1 wherein said particles impinge on said substrate surface at a rate sufficient to deposit source material at about 1 mil per hour at close to theoretical density.
References Cited (Backward Citations)
US3494852A
Cited
US3494853A
Cited
US3654123A
Cited
US3669860A
Cited
US3711398A
Cited
US3925187A
Cited
US3779891A
Cited
US3761375A
Cited
US3829373A
Cited
US4014779A
Cited
US3939052A
Cited
US4022947A
Cited
US4119881A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-14 | 1989-06-15 | 1989-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-14 | 1993-06-15 | 1993-12-15 | $7700.00 | Window Closed / Lapsed |