Titanium trichloride catalyst component and the process for the production thereof
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-09-26
•
Granted: 1981-10-20
•
Expires: 1998-09-26
Abstract
Abstract A titanium trichloride catalyst component containing a minor amount of prepolymerized alpha-olefin and useful in the polymerization of alpha-olefins is produced by reducing titanium tetrachloride with an organoaluminum compound at low temperatures and then treating the resulting reduced solids product with about 1 to 1,000 wt. % alpha-olefin so as to obtain a prepolymerized titanium trichloride reduced solid. The prepolymerized reduced solid can thereafter be activated to a highly active prepolymerized titanium trichloride by treating the prepolymerized reduced solid with a halogenated hydrocarbon and a Lewis base complexing agent or titanium tetrachloride and a Lewis base complexing agent. The prepolymerized reduced solid and the prepolymerized activated titanium trichloride manifests substantially no evidence of friability upon being subjected to mechanical shearing forces. The resulting prepolymerized activated titanium trichloride composition, when employed in combination with an organo-metal compound results in an unexpectedly highly active catalyst obtaining polymers with high heptane insolubles.
Inventors
- 👤 Harry J. Wristers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:02
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 49
Claim 1
Independent Claim
145 words
A non-friable, highly active Ziegler-type TiCl 3 catalyst composition obtained by: (1) contacting TiCl 4 with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl 3 reduced solid product, (2) contacting the reduced solid TiCl 3 product with a minor amount of an α-olefin having at least three carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solid product containing about 1 to about 1,000 wt.% of prepolymerized α-olefin based on the weight of TiCl 3 , (3) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.
Claim 2
Dependent Claim
145 words
A non-friable, highly active Ziegler-type TiCl 3 catalyst composition obtained by: (1) contacting TiCl 4 with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl 3 reduced solid product, (2) contacting the reduced solid TiCl 3 product with a minor amount of an α-olefin having at least three carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solid product containing about 1 to about 1,000 wt.% of prepolymerized α-olefin based on the weight of TiCl 3 , (3) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.
Claim 3
Dependent Claim
62 words
The TiCl 3 composition of claim 1 wherein said α-olefin contains from 3 to 22 carbon atoms said α-olefin containing no branching on the vinylic carbon atom and is present in amounts so as to provide a reduced solid TiCl 3 product prepolymerized with about 3 wt.% to about 100 wt.% of said α-olefin based on the weight of TiCl 3 .
Claim 4
Dependent Claim
51 words
The TiCl 3 composition of claim 2 wherein said α-olefin has from 3 to 8 carbon atoms and is present in amounts so as to provide a reduced solid TiCl 3 product prepolymerized with about 6 wt.% to 30 wt.% of said α-olefin based on the weight of TiCl 3 .
Claim 5
Dependent Claim
26 words
The TiCl 3 catalyst composition of claim 1 wherein said prepolymerized TiCl 3 reduced solid is treated with the chlorinated hydrocarbon and Lewis base complexing agent.
Claim 6
Dependent Claim
26 words
The TiCl 3 catalyst composition of claim 1 wherein said prepolymerized TiCl 3 reduced solid product is treated with TiCl 4 and Lewis base complexing agent.
Claim 7
Dependent Claim
69 words
The TiCl 3 catalyst composition of claim 4 wherein the treatment is at a temperature in the range of about 50° C. to about 100° C. for about 1 to about 10 hours, the chlorinated hydrocarbon being present in an amount at least about 0.2 mol per gram atom of titanium and the Lewis base being present in an amount of at least 0.1 mol per mol of titanium.
Claim 8
Dependent Claim
55 words
The TiCl 3 catalyst composition of claim 6 wherein the halogenated hydrocarbon is present in an amount of about 0.5 mol to about 1.5 mol per gram atom of titanium in the prepolymerized reduced solid and the Lewis base is present in a range of about 0.1 mol to about 2.5 mols per mol titanium.
Claim 9
Dependent Claim
16 words
The TiCl 3 catalyst composition of claim 1 wherein said organoaluminum compound is an organo-aluminum halide.
Claim 10
Dependent Claim
50 words
The TiCl 3 catalyst composition of claim 8 wherein said organoaluminum halide is of the general formula R n AlX 3-n wherein R is an alkyl or aryl group having from 1 to 18 carbon atoms, X is a halogen and n is an integer of from 1 to 3.
Claim 11
Dependent Claim
29 words
The TiCl 3 catalyst composition of claim 9 wherein said organoaluminum halide is a dialkyl aluminum chloride wherein said alkyl group can have from 2 to 6 carbon atoms.
Claim 12
Dependent Claim
23 words
The TiCl 3 catalyst composition of claim 9 wherein the organoaluminum halide is a mixture of diethyl aluminum chloride and ethyl aluminum dichloride.
Claim 13
Dependent Claim
35 words
The TiCl 3 catalyst composition of claim 1 or 6 wherein said organoaluminum compound is present in a ratio of from about 1 to 5 gm atoms of aluminum to 1 gm atom of titanium.
Claim 14
Dependent Claim
27 words
The TiCl 3 catalyst composition of claim 1 wherein the prepolymerized TiCl 3 reduced solid product is filtered and washed in the presence of a liquid hydrocarbon.
Claim 15
Dependent Claim
27 words
The TiCl 3 catalyst composition of claims 4 or 5 wherein said Lewis base complexing agent is an organic electron-donor compound containing phosphorous, sulfur, nitrogen and/or oxygen.
Claim 16
Dependent Claim
35 words
The TiCl 3 catalyst composition of claim 14 wherein said Lewis base complexing agent is selected from the group consisting of ethers, thioethers, thiols, organo phosphorous compounds, organo nitrogen compounds, ketones, esters and mixtures thereof.
Claim 17
Dependent Claim
18 words
The TiCl 3 catalyst composition of claim 15 wherein said Lewis base complexing agent is a dialkyl ether.
Claim 18
Dependent Claim
32 words
The TiCl 3 catalyst composition of claim 4 wherein said chlorinated hydrocarbon has from 2 to 8 carbon atoms and is selected from chlorinated saturated hydrocarbons, chlorinated unsaturated hydrocarbons or mixtures thereof.
Claim 19
Dependent Claim
24 words
The TiCl 3 catalyst composition of claim 17 wherein said chlorinated hydrocarbon is selected from chlorinated aliphatic hydrocarbons, chlorinated aromatic hydrocarbons or mixtures thereof.
Claim 20
Dependent Claim
28 words
The TiCl 3 catalyst composition of claim 18 wherein said chlorinated hydrocarbon is selected from hexachloroethane, pentachloroethane, tetrachloroethane, trichloroethane, dichloroethane, monochloroethane, hexachloropropane, pentachloropropane, tetrachloropropane, dichlorobutane and mixtures thereof.
Claim 21
Dependent Claim
33 words
The TiCl 3 catalyst composition of claim 16 wherein said complexing agent is selected from the group consisting of di-n-butyl ether, di-n-amyl ether, diisoamyl ether, di-n-heptyl ether, di-2-ethyl hexyl ether, or mixtures thereof.
Claim 22
Dependent Claim
14 words
The TiCl 3 catalyst composition of claim 19 wherein the chlorinated hydrocarbon is hexachloroethane.
Claim 23
Dependent Claim
15 words
The TiCl 3 catalyst composition of claim 20 wherein said complexing agent is di-n-butyl ether.
Claim 24
Dependent Claim
126 words
The TiCl 3 catalyst composition of claim 1 wherein said TiCl 4 is mixed with said organoaluminum compound in a ratio of from 1 to 5 gm atoms as aluminum of said organoaluminum compound per gm atom of said TiCl 4 at a temperature of from about -50° C. to about +30° C. for a period of time of from about 30 minutes to about 3 hours and said prepolymerized reduced solid TiCl 3 is contacted with the chlorinated hydrocarbon in a ratio of about 0.2 to about 3.0 mols chlorinated hydrocarbon per 1 gm atom of said TiCl 3 and with said complexing agent in a ratio of about 0.1 to about 2.5 mols complexing agent per 1 gm atom of said TiCl 3 .
Claim 25
Dependent Claim
163 words
A Ziegler-type catalyst composition for use in the polymerization of alpha-olefins, said composition comprising: (a) an organometal compound co-catalyst, and (b) a titanium trichloride catalyst composition obtained by; (i) contacting TiCl 4 with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl 3 reduced solid product, (ii) contacting the reduced solid TiCl 3 product with a minor amount of an alpha-olefin having at least 3 carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solid product containing about 1 to about 1,000 wt.% of prepolymerized alpha-olefin based on the weight of TiCl 3 , and (iii) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.
Claim 26
Dependent Claim
163 words
A Ziegler-type catalyst composition for use in the polymerization of alpha-olefins, said composition comprising: (a) an organometal compound co-catalyst, and (b) a titanium trichloride catalyst composition obtained by; (i) contacting TiCl 4 with an organoaluminum compound at a temperature in the range of about -50° C. to about 30° C. to produce a TiCl 3 reduced solid product, (ii) contacting the reduced solid TiCl 3 product with a minor amount of an alpha-olefin having at least 3 carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solid product containing about 1 to about 1,000 wt.% of prepolymerized alpha-olefin based on the weight of TiCl 3 , and (iii) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.
Claim 27
Dependent Claim
67 words
The Ziegler-type catalyst composition of claim 24 wherein said alpha-olefin employed in the prepolymerization step contains from 3 to 22 carbon atoms, said alpha-olefin containing no branching on the vinylic carbon atom and is present in amounts so as to provide a reduced solid TiCl 3 product prepolymerized with about 3 wt.% to about 100 wt.% of said alpha-olefin based on the weight of TiCl 3 .
Claim 28
Dependent Claim
56 words
The Ziegler-type catalyst component of claim 25 wherein said alpha-olefin employed in the prepolymerization step has from 3 to 8 carbon atoms and is present in an amount so as to provide a reduced solid TiCl 3 product prepolymerized with about 6 wt.% to 30 wt.% of said alpha-olefin based on weight of TiCl 3 .
Claim 29
Dependent Claim
26 words
The Ziegler-type catalyst composition of claim 24 wherein said prepolymerized TiCl 3 reduced solid is treaded with the chlorinated hydrocarbon and a Lewis base complexing agent.
Claim 30
Dependent Claim
25 words
The Ziegler-type catalyst composition of claim 24 wherein said prepolymerized TiCl 3 reduced solid product is treated with TiCl 4 and Lewis base complexing agent.
Claim 31
Dependent Claim
41 words
The Ziegler-type catalyst composition of claim 24 wherein the prepolymerized reduced solid is treated with at least about 0.2 mol of chlorinated hydrocarbon per gram atom of titanium and at least 0.5 mol of the Lewis base per mol of titanium.
Claim 32
Dependent Claim
46 words
The Ziegler-type catalyst composition of claim 29 wherein the halogenated hydrocarbon is present in an amount of about 0.5 mol to about 1.5 mol/gm atom of titanium and the Lewis base is present in a range of about 0.1 mol to about 2.5 mol/mol of titanium.
Claim 33
Dependent Claim
24 words
The Ziegler-type catalyst composition of claim 24 wherein said organometal compound co-catalyst is one of monoalkyl aluminum dichloride, dialkylaluminum monochloride, trialkyaluminum or mixtures thereof.
Claim 34
Dependent Claim
19 words
The Ziegler-type catalyst composition of claim 24 wherein said organoaluminum compound contacted with TiCl 4 is an organoaluminum halide.
Claim 35
Dependent Claim
48 words
The Ziegler-type catalyst composition of claim 32 wherein said organoaluminum halide is of the general formula R n AlX 3-n wherein R is an alkyl or aryl group having from 1 to 18 carbon atoms, X is a halogen and n is an integer from 1 to 3.
Claim 36
Dependent Claim
27 words
The Ziegler-type catalyst composition of claim 33 wherein said organoaluminum halide is a dialkylaluminum chloride wherein said alkyl group can have from 2 to 6 carbon atoms.
Claim 37
Dependent Claim
20 words
The Ziegler-type catalyst composition of claim 33 wherein the organoaluminum halide is a mixture of diethylaluminum chloride and ethylaluminum dichloride.
Claim 38
Dependent Claim
40 words
The Ziegler-type catalyst composition of claim 24 wherein said organoaluminum compound which is contacted with the TiCl 4 is present in a ratio of from about 1 to about 5 gram atoms of aluminum to 1 gram atom of titanium.
Claim 39
Dependent Claim
24 words
The Ziegler-type catalyst composition of claim 27 wherein said Lewis base complexing agent is an organic electron-donor compound containing phosphorous, sulphur, nitrogen, and/or oxygen.
Claim 40
Dependent Claim
24 words
The Ziegler-type catalyst composition of claim 28 wherein said Lewis base complexing agent is an organic electron-donor compound containing phosphorous, sulphur, nitrogen and/or oxygen.
Claim 41
Dependent Claim
33 words
The Ziegler-type catalyst composition of claim 24 wherein said Lewis base complexing agent is selected from the group consisting of ethers, thioethers, thiols, organo phosphorous compounds, organonitrogen compounds, ketones, esters and mixtures thereof.
Claim 42
Dependent Claim
17 words
The Ziegler-type catalyst composition of claim 39 wherein said Lewis base complexing agent is a dialkyl ether.
Claim 43
Dependent Claim
31 words
The Ziegler-type catalyst composition of claim 27 wherein said chlorinated hydrocarbon has from 2 to 8 carbon atoms and is selected from chlorinated saturated hydrocarbons, chlorinated unsaturated hydrocarbons or mixtures thereof.
Claim 44
Dependent Claim
23 words
The Ziegler-type catalyst composition of claim 41 wherein said chlorinated hydrocarbon is selected from chlorinated aliphatic hydrocarbons, chlorinated aromatic hydrocarbons or mixtures thereof.
Claim 45
Dependent Claim
27 words
The Ziegler-type catalyst composition of claim 42 wherein said chlorinated hydrocarbon is selected from hexachloroethane, pentachloroethane, tetrachloroethane, trichloroethane, dichloroethane, tetrachloroethane, hexachloropropane, pentachloropropane, tetrachloropropane, dichlorobutane and mixtures thereof.
Claim 46
Dependent Claim
32 words
The Ziegler-type catalyst composition of claim 40 wherein said complexing agent is selected from the group consisting of di-n-butyl ether, di-n-amyl ether, diisoamyl ether, di-n-heptyl ether, di-2-ethyl hexyl ether, or mixtures thereof.
Claim 47
Dependent Claim
13 words
The Ziegler-type catalyst composition of claim 43 wherein the chlorinated hydrocarbon is hexachloroethane.
Claim 48
Dependent Claim
14 words
The Ziegler-type catalyst composition of claim 44 wherein said complexing agent is di-n-butyl ether.
Claim 49
Dependent Claim
120 words
The Ziegler-type catalyst composition of claim 24 wherein said TiCl 4 is mixed with said organo-aluminum compound in a ratio of from 1 to 5 gram atoms as aluminum of said organoaluminum compound per gram atom of TiCl 4 at a temperature of from about -50° to about +30° C. for a period of time from about 30 minutes to about 3 hours and said prepolymerized reduced solid TiCl 3 is contacted with the chlorinated hydrocarbon in a ratio of about 0.2 to about 3.0 mols chlorinated hydrocarbon per 1 gram atom of said TiCl 3 and with said complexing agent in a ratio of about 0.1 to about 2.5 mols complexing agent per 1 gram atom of titanium trichloride.
References Cited (Backward Citations)
US3094568A
Cited
US3549717A
Cited
US3922322A
Cited
US4127504A
Cited
US4085064A
Cited
US4123387A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-19 | 1985-04-20 | 1985-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-19 | 1989-04-20 | 1989-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-19 | 1993-04-20 | 1993-10-20 | $7700.00 | Window Closed / Lapsed |