Stable aqueous dispersions of mixed resins and process for use as coating compositions

Claim 2

A process for preparing a stable aqueous dispersion of mixed resins comprising the steps of (1) preparing a solution of an aminoplast in a substantially water-miscible organic solvent; (2) heating the solution and adding thereto a mixture of vinyl polymerization catalyst and α,β-olefinically unsaturated carboxylic acid monomer and at least one other vinyl polymerizable monomer to form a polymerization product solution wherein the unsaturated monocarboxylic acid monomer is present in the amount of about 20 to about 90 weight percent based on total monomer weight; (3) admixing and heating together the polymerization product solution and an epoxy resin; (4) at least partially neutralizing the admixture with ammonia or an organic amine; and (5) dispersing the admixture into an aqueous medium to provide a stable aqueous dispersion of mixed resin solids having a solids content in the range of between about 15 to about 40 weight percent wherein the aminoplast component is present in the amount of about 1 to about 12 weight percent, the monomers are present in the amount of about 20 to about 40 weight percent and the epoxy resin component is present in the amount of about 48 to about 79 weight percent, said weight percents being based on the total weight of aminoplast, monomers and epoxy resin components.

Claim 3

A process for the preparation of a stable aqueous dispersion of mixed resins adapted for application as a thermosetting protective coating for metal surfaces, which process comprises the steps of (1) preparing a solution of an aminoplast component dissolved in a substantially water-miscible organic solvent; (2) heating and maintaining the temperature of the solution in the range between about 120° and about 300° F., and adding to the solution at a uniform rate over a period between about 0.5 to about 6 hours a blend of a vinyl polymerization catalyst and monomers comprising (a) between about 20 to about 90 weight percent based on total monomer weight of α,β-olefinically unsaturated carboxylic acid, and (b) 10 to about 80 weight percent based on total monomer weight of at least one olefinically unsaturated monomer which is copolymerizable with the carboxylic acid monomer, thereby forming a polymerization product solution; (3) admixing and interacting at a temperature between about 100° to about 300° F. the polymerization product solution and an epoxy resin component, wherein said epoxy resin is a glycidyl polyether of a polyhydric phenol or hydrogenated phenol and contains an average of more than one epoxide group per molecule and has an epoxy equivalent weight in the range between about 150 to about 8000; (4) treating and at least partially neutralizing the admixture reaction product medium with ammonia or an organic amine, thereby forming a substantially homogeneous single phase solution; and dispersing the said solution into a sufficient quantity of water to provide a stable aqueous dispersion of mixed resins having a solids content in the range of between about 15 to about 40 weight percent wherein the aminoplast component is present in the amount of about 1 to about 12 weight percent, the monomers are present in the amount of about 20 to about 40 weight percent and the epoxy resin component is present in the amount of about 48 to about 79 weight percent, said weight percents being based on the total weight of aminoplast, monomers and epoxy resin components.

Claim 4

A process for the preparation of a stable aqueous dispersion of mixed resins adapted for application as a thermosetting protective coating for metal surfaces, which process comprises the steps of (1) preparing a solution of an aminoplast component dissolved in a substantially water-miscible organic solvent; (2) heating and maintaining the temperature of the solution in the range between about 120° and about 300° F., and adding to the solution at a uniform rate over a period between about 0.5 to about 6 hours a blend of a vinyl polymerization catalyst and monomers comprising (a) between about 20 to about 90 weight percent based on total monomer weight of α,β-olefinically unsaturated carboxylic acid, and (b) 10 to about 80 weight percent based on total monomer weight of at least one olefinically unsaturated monomer which is copolymerizable with the carboxylic acid monomer, thereby forming a polymerization product solution; (3) admixing and interacting at a temperature between about 100° to about 300° F. the polymerization product solution and an epoxy resin component, wherein said epoxy resin is a glycidyl polyether of a polyhydric phenol or hydrogenated phenol and contains an average of more than one epoxide group per molecule and has an epoxy equivalent weight in the range between about 150 to about 8000; (4) treating and at least partially neutralizing the admixture reaction product medium with ammonia or an organic amine, thereby forming a substantially homogeneous single phase solution; and dispersing the said solution into a sufficient quantity of water to provide a stable aqueous dispersion of mixed resins having a solids content in the range of between about 15 to about 40 weight percent wherein the aminoplast component is present in the amount of about 1 to about 12 weight percent, the monomers are present in the amount of about 20 to about 40 weight percent and the epoxy resin component is present in the amount of about 48 to about 79 weight percent, said weight percents being based on the total weight of aminoplast, monomers and epoxy resin components.

Claim 5

A process in accordance with claim 2 wherein the aminoplast component is a melamine-aldehyde condensate derivative.

Claim 6

A process is accordance with claim 3 wherein the aminoplast component is a melamine-formaldehyde condensate etherified with methanol.

Claim 7

A process in accordance with claim 2 wherein the water-miscible organic solvent is selected from at least one of monohydric and polyhydric alcohols and ether derivatives thereof.

Claim 8

The process of claim 2 wherein the water-miscible organic solvent is present in the amount of about 30 to about 85 weight percent based on the total weight of aminoplast, monomers epoxy resin and organic solvent.

Claim 9

A process in accordance with claim 2 wherein the α,β-olefinically unsaturated carboxylic acid monomer is acrylic acid or methacrylic acid.

Claim 10

A process in accordance with claim 2 wherein at least one of the monomers in the monomer mixture is an acrylic or methacrylic alkyl ester.

Claim 11

A process in accordance with claim 2 wherein at least one of the monomers in the monomer mixture is a vinyl aromatic compound.

Claim 12

A process in accordance with claim 2 wherein the epoxy resin component is a polyglycidyl ether of p,p'-dihydroxydiphenyl propane.

Claim 13

A process in accordance with claim 2 wherein the admixture reaction product medium is neutralized to a pH in the range between about 4 to about 8.

Claim 14

A process in accordance with claim 2 wherein the average particle size of the dispersed mixed resin solids phase is less than about one micron.

Claim 15

The process of claim 2 wherein the aminoplast is present in the amount of about 4 to about 8 weight percent, the monomers are present in the amount of about 25 to about 35 weight percent and the epoxy resin is present in the amount of about 57 to about 71 weight percent.

Claim 16

The process of claim 2 wherein the water-miscible solvent is present in the amount of about 40 to about 75 weight percent based on total weight of aminoplast, polymerized monomers, epoxy resin and solvent.

Claim 17

A stable aqueous dispersion of mixed resins prepared in accordance with the process of claim 2.

Claim 20

A method in accordance with claim 16 wherein the said stable aqueous dispersion coating composition is applied to the interior surface of metal containers.