Single stage hot bonding method for producing composite honeycomb core structures
Assignee: Boeing Co
•
Filing: 1979-04-17
•
Granted: 1981-08-18
•
Expires: 1999-04-17
Abstract
Abstract A single stage hot bonding process for manufacturing composite honeycomb core structures, such as airplane control surface structures, capable of withstanding bending and shear stresses, is disclosed. The single stage hot bonding process includes the steps of bonding a low density honeycomb core to a high density honeycomb core, shaping the combined honeycomb core, adhesively attaching spar caps to opposing surfaces of the high density honeycomb core, adhesively attaching a skin to the spar caps and the low density honeycomb core and curing the composite structure in an autoclave. Additionally, if the low density honeycomb core is shaped so that its upper and/or lower surfaces slope toward the opposing surface and join in an edge opposite the high density honeycomb core, such as in the case of airplane control surface structures, the hot bonding process further includes the steps of securing a tab of cured adhesive to the edge of the low density core before the skin is attached, and securing the tab during curing so as to prevent the lateral component of the fluid pressure in the autoclave from causing the lateral movement of the core relative to the skin.
Inventors
- 👤 R. John Hilton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:15
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/10; B32B3/12; B31; B31D; B31D3/00; B31D3/02; B31D3/0207; B32B7/00; B32B7/04; B32B7/12; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1003; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/49336; Y10T29/49337; Y10T428/00; Y10T428/24; Y10T428/24149
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
288 words
A single stage hot bonding process for forming composite honeycomb core structures comprising the steps of: bonding a primary load carrying honeycomb core to an edge of a shape defining honeycomb core to form a combined honeycomb core; forming opposed undercut regions in said combined honeycomb core in the region of said primary load carrying honeycomb core by reducing the thickness of said primary load carrying honeycomb core to less than the thickness of said shape defining honeycomb core; placing a first skin on a working surface; applying adhesive to the exposed side of said first skin; attaching a first spar cap to said first skin; applying adhesive to the exposed side of said first spar cap; attaching said combined honeycomb core to said first spar cap and said first skin such that one of said opposed undercut regions of said combined honeycomb core overlies and is attached to said first spar cap and the surface of said shape defining honeycomb core portion of said combined honeycomb core adjacent to said undercut region overlies and is attached to said first skin; applying adhesive to the exposed side of said combined honeycomb core; attaching a second spar cap to the other one of said opposed undercut regions of said combined honeycomb core; applying adhesive to the exposed side of said second spar cap; attaching a second skin to said second spar cap and said exposed side of said combined honeycomb core; and, simultaneously heating said attached combined honeycomb core, said first and second spar caps and said first and second skins to cure said adhesives and simultaneously form bonds between said combined honeycomb core, said first and second spar caps and said first and second skins where they join.
Claim 2
Dependent Claim
288 words
A single stage hot bonding process for forming composite honeycomb core structures comprising the steps of: bonding a primary load carrying honeycomb core to an edge of a shape defining honeycomb core to form a combined honeycomb core; forming opposed undercut regions in said combined honeycomb core in the region of said primary load carrying honeycomb core by reducing the thickness of said primary load carrying honeycomb core to less than the thickness of said shape defining honeycomb core; placing a first skin on a working surface; applying adhesive to the exposed side of said first skin; attaching a first spar cap to said first skin; applying adhesive to the exposed side of said first spar cap; attaching said combined honeycomb core to said first spar cap and said first skin such that one of said opposed undercut regions of said combined honeycomb core overlies and is attached to said first spar cap and the surface of said shape defining honeycomb core portion of said combined honeycomb core adjacent to said undercut region overlies and is attached to said first skin; applying adhesive to the exposed side of said combined honeycomb core; attaching a second spar cap to the other one of said opposed undercut regions of said combined honeycomb core; applying adhesive to the exposed side of said second spar cap; attaching a second skin to said second spar cap and said exposed side of said combined honeycomb core; and, simultaneously heating said attached combined honeycomb core, said first and second spar caps and said first and second skins to cure said adhesives and simultaneously form bonds between said combined honeycomb core, said first and second spar caps and said first and second skins where they join.
Claim 3
Dependent Claim
50 words
The single stage hot bonding process set forth in claim 1 including the step of shaping said shape defining honeycomb core to a desired contour with the thickness of said shape defining honeycomb core tapering gradually away from said primary load carrying honeycomb core and terminating in a trailing edge.
Claim 4
Dependent Claim
39 words
The single stage hot bonding process set forth in claim 2 wherein the step of simultaneously heating said attached combined honeycomb core, said first and second spar caps and said first and second skins occurs in a pressurized autoclave.
Claim 5
Dependent Claim
177 words
The single stage hot bonding process set forth in claim 3 further comprising: before the step of shaping said shape defining honeycomb core to a desired contour, the steps of applying adhesive to the region of said shape defining honeycomb core that will ultimately form said trailing edge of said shape defining honeycomb core and curing said adhesive; shaping said cured adhesive applied to the region of said shape defining honeycomb core that will ultimately form said trailing edge of said shape defining honeycomb core into an adhesive tab extending outwardly from the trailing edge of said shape defining honeycomb core during said step of shaping said shape defining honeycomb core to a desired contour; and, securing said adhesive tab to said working surface and, thereby, said shape defining honeycomb core to said working surface to prevent the lateral movement of said shape defining honeycomb core relative to said first and second skins when said attached combined honeycomb core, said first and second spar caps and said first and second skins are heated in said pressurized autoclave.
Claim 6
Dependent Claim
38 words
The single stage hot bonding process set forth in claim 1 wherein the step of simultaneously heating said attached combined honeycomb core, said first and second spar caps and said first and second skins occurs in an autoclave.
Claim 7
Dependent Claim
20 words
The single stage hot bonding process claimed in claim 5 wherein said autoclave is pressurized during said simultaneous heating step.
Claim 8
Dependent Claim
127 words
The single stage hot bonding process set forth in claim 6 further comprising the steps of: applying adhesive to the region of said shape defining honeycomb core remote from said primary load carrying honeycomb core and curing said adhesive; shaping said cured adhesive applied to the region of said shape defining honeycomb core remote from said load carrying honeycomb core into an adhesive tab extending outwardly from said shape defining honeycomb core; and, securing said adhesive tab with respect to said shape defining honeycomb core to prevent the lateral movement of said shape defining honeycomb core relative to said first and second skins when said attached combined honeycomb core, said first and second spar caps and said first and second skins are heated in said pressurized autoclave.
Claim 9
Dependent Claim
136 words
A single stage hot bonding process for forming composite honeycomb core structures comprising the steps of: forming opposed elongate undercut regions in a combined honeycomb core that comprises a primary load carrying honeycomb core and a shape defining honeycomb core, said opposed elongate undercut regions being aligned with said primary load carrying honeycomb core; adhesively attaching first and second spar caps to the outer surfaces of said primary load carrying member so as to fill said opposed elongate undercut regions; adhesively attaching a skin to the outer surfaces of said spar caps and said shape defining honeycomb core; and, simultaneously heating said combined honeycomb core, said first and second spar caps and said skin to cure said adhesives and simultaneously form bonds between said combined honeycomb core, said first and second spar caps and said skin.
Claim 10
Dependent Claim
136 words
A single stage hot bonding process for forming composite honeycomb core structures comprising the steps of: forming opposed elongate undercut regions in a combined honeycomb core that comprises a primary load carrying honeycomb core and a shape defining honeycomb core, said opposed elongate undercut regions being aligned with said primary load carrying honeycomb core; adhesively attaching first and second spar caps to the outer surfaces of said primary load carrying member so as to fill said opposed elongate undercut regions; adhesively attaching a skin to the outer surfaces of said spar caps and said shape defining honeycomb core; and, simultaneously heating said combined honeycomb core, said first and second spar caps and said skin to cure said adhesives and simultaneously form bonds between said combined honeycomb core, said first and second spar caps and said skin.
Claim 11
Dependent Claim
51 words
The single stage hot bonding process set forth in claim 8 wherein said combined honeycomb core, said first and second spar caps and said skin are heated in an autoclave to simultaneously cure said adhesives and bond said combined honeycomb core, said first and second spar caps and said skin together.
Claim 12
Dependent Claim
50 words
The single stage hot bonding process set forth in claim 8 including the step of shaping said shape defining honeycomb core to a desired contour with the thickness of said shape defining honeycomb core tapering gradually away from said primary load carrying honeycomb core and terminating in a trailing edge.
Claim 13
Dependent Claim
52 words
The single stage hot bonding process set forth in claim 10 wherein said combined honeycomb core, said first and second spar caps and said skin are heated in a pressurized autoclave to simultaneously cure said adhesives and bond said combined honeycomb core, said first and second spar caps and said skin together.
Claim 14
Dependent Claim
132 words
The single stage hot bonding process set forth in claim 11 further comprising: before the step of shaping said shape defining honeycomb core, the steps of applying adhesive to the region of said shape defining honeycomb core that will ultimately form said trailing edge of said shape defining honeycomb core and curing said adhesive; shaping said shape defining honeycomb core such that an adhesive tab projects outwardly from said trailing edge of said shape defining honeycomb core; and, securing said adhesive tab with respect to said shape defining honeycomb core and, thereby, said shape defining honeycomb core to prevent the lateral movement of said shape defining honeycomb core relative to said skin when said combined honeycomb core, said first and second spar caps and said skin are heated in said pressurized autoclave.
Claim 15
Dependent Claim
19 words
The single stage hot bonding process claimed in claim 9 wherein said autoclave is pressurized during said heating step.
Claim 16
Dependent Claim
88 words
The single stage hot bonding process set forth in claim 13 further comprising the steps of: applying adhesive to the outer edge of said shape defining honeycomb core and curing said adhesive; shaping said cured adhesive applied to the outer edge of said shape defining honeycomb core such that an adhesive tab projects outwardly from said shape defining honeycomb core; and, securing said adhesive tab with respect to said shape defining honeycomb core to prevent the lateral movement of said shape defining honeycomb core relative to said skin.
References Cited (Backward Citations)
US3533894A
Cited
US3566493A
Cited
US3883093A
Cited
US3707583A
Cited
US3754840A
Cited
US3782856A
Cited
US3813186A
Cited
US3950115A
Cited
US4022546A
Cited
US4136846A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-17 | 1985-02-16 | 1985-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-17 | 1989-02-16 | 1989-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-17 | 1993-02-16 | 1993-08-18 | $7700.00 | Window Closed / Lapsed |