Method and composition for continuous electroless copper deposition using a hypophosphite reducing agent in the presence of cobalt or nickel ions
Assignee: MacDermid Inc
•
Filing: 1978-11-27
•
Granted: 1981-05-05
•
Expires: 1998-11-27
Abstract
Abstract Electroless copper deposition solutions, and method of continuously electrolessly depositing copper onto a workpiece using these solutions, are disclosed. The solutions contain, in addition to water as the usual solvent, a soluble source of copper ions, a complexing agent or mixture of agents to maintain the copper in solution, a non-formaldehyde copper reducing agent, such as hypophosphite, effective to reduce the copper ions to metallic copper as a deposit or plating on a prepared surface of a workpiece brought into contact with the solution, and a soluble source of non-copper metallic ions, such as nickel or cobalt ions, which act as an autocatalysis promoter to enable continuous plating using the solutions. The solutions are maintained in an alkaline condition and preferably in a pH range of 11-14 through the addition of pH adjusters. The properties of plating baths using the solutions, such as bath stability as well as plating process parameters such as plating rate, and the quality of deposit may be advantageously controlled through the appropriate selection of the non-copper metallic ion added and the complexing agent used. Optional additives, such as polymers, wetting agents, and various soluble unsaturated organic compounds, may also be utilized to influence these variables.
Inventors
- 👤 Rachel Goldstein
- 👤 Peter E. Kukanskis
- 👤 John J. Grunwald
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:23
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/38; C23C18/40
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
152 words
In a composition for the electroless deposition of copper including, in an essentially alkaline aqueous solution, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution and a reducing agent capable of providing a soluble source of hypophosphite ions effective to reduce the cupric ions to metallic copper to obtain satisfactory copper deposition on the prepared surface of a workpiece when in contact with the solution, the improvement therein providing continuous deposition of the copper on the workpiece such that the deposition thickness increases with time at a substantially constant rate similar to an initial deposition rate comprising including in the solution a soluble source of metal ions other than cupric ions which ions are capable of functioning as an autocatalysis promoter for metallic copper deposition, the metal ions in solution being predominantly cupric ions and the solution pH being maintained in the range of 11-14.
Claim 2
Dependent Claim
152 words
In a composition for the electroless deposition of copper including, in an essentially alkaline aqueous solution, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution and a reducing agent capable of providing a soluble source of hypophosphite ions effective to reduce the cupric ions to metallic copper to obtain satisfactory copper deposition on the prepared surface of a workpiece when in contact with the solution, the improvement therein providing continuous deposition of the copper on the workpiece such that the deposition thickness increases with time at a substantially constant rate similar to an initial deposition rate comprising including in the solution a soluble source of metal ions other than cupric ions which ions are capable of functioning as an autocatalysis promoter for metallic copper deposition, the metal ions in solution being predominantly cupric ions and the solution pH being maintained in the range of 11-14.
Claim 3
Dependent Claim
38 words
The improved composition as claimed in claim 1, wherein the source of metal ions other than cupric ions is one which provides ions selected from the group consisting of nickel and cobalt ions and combinations of the same.
Claim 4
Dependent Claim
40 words
The improved composition as claimed in claim 1, wherein the complexing agent is one which, in the solution, enables the metal ions other than cupric ions to codeposit with the cupric ions in small quantities forming an essentially copper deposit.
Claim 5
Dependent Claim
54 words
The improved composition as claimed in claim 3, wherein the complexing agent is one which, in the solution, provides the metal ions other than cupric ions with a stability constant substantially equal to the stability constant of the cupric ions, to obtain substantially the same kinetic drive for all the metal ions in solution.
Claim 6
Dependent Claim
138 words
An electroless copper deposition solution for the continuous plating of copper at a substantially linear plating rate comprising, in addition to water, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution and a soluble source of hypophosphite ions effective to reduce the cupric ions to essentially metallic copper as a deposit on a catalyzed non-conductive surface of a workpiece when in contact with the solution, and a soluble source of non-cupric metal ions selected from the group consisting of nickel and cobalt and combinations of the same, pH adjusters as required in an amount effective to maintain the solution pH in a range of 11-14; the complexing agent being one which enables the non-cupric metal ions to co-deposit with the copper in small quantities and to act as an autocatalysis promoter.
Claim 7
Dependent Claim
138 words
An electroless copper deposition solution for the continuous plating of copper at a substantially linear plating rate comprising, in addition to water, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution and a soluble source of hypophosphite ions effective to reduce the cupric ions to essentially metallic copper as a deposit on a catalyzed non-conductive surface of a workpiece when in contact with the solution, and a soluble source of non-cupric metal ions selected from the group consisting of nickel and cobalt and combinations of the same, pH adjusters as required in an amount effective to maintain the solution pH in a range of 11-14; the complexing agent being one which enables the non-cupric metal ions to co-deposit with the copper in small quantities and to act as an autocatalysis promoter.
Claim 8
Dependent Claim
30 words
An electroless copper deposition solution as claimed in claim 5, wherein the complexing agent is one selected from the group consisting of soluble hydroxy acids and hydroxy acid metal salts.
Claim 9
Dependent Claim
31 words
An electroless copper deposition solution as claimed in claim 5, wherein the complexing agent is one selected from the group consisting of soluble tartrates, gluconates, glycerates, glycolates, lactates and mixtures thereof.
Claim 10
Dependent Claim
47 words
An electroless copper deposition solution as claimed in claim 7, wherein the complexing agent further comprises an amino acid complexing agent selected from the group consisting of N-hydroxyethyl ethylenediamine triacetic acid (HEEDTA), ethylenediamine tetraacetic acid (EDTA) and nitrilotriacetic acid (NTA) and alkali metal salts of the same.
Claim 11
Dependent Claim
68 words
An electroless copper deposition solution as claimed in claim 5, wherein the complexing agent is one selected from the group consisting of N-hydroxyethyl ethylenediamine triacetic acid (HEEDTA), ethylenediamine tetraacetic acid (EDTA) and nitrilotriacetic acid (NTA), and is present in an amount insufficient to react all of the non-cupric ions to form a complex therewith so that at least some non-cupric ions remain available for co-deposition with the copper.
Claim 12
Dependent Claim
26 words
An electroless copper deposition solution as claimed in claim 5, further comprising an additive compound selected from the group consisting of unsaturated organic compounds and polymers.
Claim 13
Dependent Claim
36 words
An electroless copper deposition solution as claimed in claim 5, further comprising an additive compound selected from the group consisting of butyne diol, butene diol, polyoxyethylene, polyethylene glycol and a block copolymer of polyoxyethylene and polyoxypropylene.
Claim 14
Dependent Claim
27 words
The improved composition as claimed in claims 1 or 5 wherein the ratio of cupric ions to the other metal ions in solution is at least 5.5:1.
Claim 15
Independent Claim
170 words
A method of continuously electrolessly depositing a copper plating on the surface of a workpiece comprising the steps of preparing the surface of the workpiece to render it more receptive to the plating, immersing the workpiece in a solution comprising, in addition to water, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution, and a a soluble source of hypophosphite ions effective to reduce the cupric ions to metallic copper as a deposit on the surface of the workpiece when in contact with the solution, and a soluble source of non-cupric metal ions which are capable of functioning as an autocatalysis promoter for the copper plating, and maintaining the pH of the solution at an operable level which enables the satisfactory continuous deposition of a copper plating on the workpiece, and depositing the copper plating on the workpiece at a thickness which increases with time of immersion with a substantially constant rate of deposition essentially the same as the initial rate of deposition.
Claim 16
Independent Claim
170 words
A method of continuously electrolessly depositing a copper plating on the surface of a workpiece comprising the steps of preparing the surface of the workpiece to render it more receptive to the plating, immersing the workpiece in a solution comprising, in addition to water, a soluble source of cupric ions, a complexing agent to maintain the cupric ions in solution, and a a soluble source of hypophosphite ions effective to reduce the cupric ions to metallic copper as a deposit on the surface of the workpiece when in contact with the solution, and a soluble source of non-cupric metal ions which are capable of functioning as an autocatalysis promoter for the copper plating, and maintaining the pH of the solution at an operable level which enables the satisfactory continuous deposition of a copper plating on the workpiece, and depositing the copper plating on the workpiece at a thickness which increases with time of immersion with a substantially constant rate of deposition essentially the same as the initial rate of deposition.
Claim 17
Dependent Claim
29 words
A method of continuously electrolessly depositing a copper plating as claimed in claim 13, wherein the soluble source of non-cupric ions comprises a source of nickel and/or cobalt ions.
Claim 18
Dependent Claim
32 words
A method of continuously electrolessly depositing a copper plating as claimed in claim 13, and further comprising the step of increasing the temperature of the plating solution to increase the deposition rate.
Claim 19
Dependent Claim
49 words
A method of continuously electrolessly depositing a copper plating as claimed in claim 13, wherein the complexing agent is one which, in the solution, enables the metal ions other than cupric ions to co-deposit with the cupric ions in small quantities and form a co-deposit with the metallic copper.
Claim 20
Dependent Claim
35 words
A method of continuously electrolessly depositing a copper plating as claimed in claim 13, wherein the complexing agent is one selected from the group consisting of soluble tartartes, gluconates, glycerates, glycolates, lactates and mixtures thereof.
Claim 21
Dependent Claim
44 words
A method of continuously electrolessly depositing a copper plating as claimed in claim 13, wherein the complexing agent further comprises an additive compound selected from the group consisting of butyne diol, butene diol, polyoxyethylene, polyethylene glycol and a block copolymer of polyoxyethylene and polyoxypropylene.
References Cited (Backward Citations)
SU285439A1
Cited
US3046159A
Cited
US3093509A
Cited
US3615735A
Cited
US3615733A
Cited
US3615732A
Cited
US3716462A
Cited
JPS5030744A
Cited
US3935013A
Cited
US4019910A
Cited
JPS5125432A
Cited
US4131699A
Cited
US4138267A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-04 | 1984-11-03 | 1985-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-04 | 1988-11-03 | 1989-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-04 | 1992-11-03 | 1993-05-05 | $7700.00 | Window Closed / Lapsed |