US4239560A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Open tube aluminum oxide disc diffusion
Assignee: General Electric Co
•
Filing: 1979-05-21
•
Granted: 1980-12-16
•
Expires: 1999-05-21
Abstract
Abstract A p-type region is formed in a semiconductor body by diffusion of aluminum from an aluminum oxide source in an open tube process. Both ceramic aluminum oxide and sapphire sources are described and an inert atmosphere of argon and hydrogen provides stable results. An alternative embodiment provides both the deep diffusion characteristics of aluminum with the high surface concentration of boron by using a boron nitride wafer carrier.
Inventors
- 👤 Mike F. Chang
- 👤 David K. Hartman
- 👤 Richard W. Kennedy
- 👤 Alfred Roesch
- 👤 Henri B. Assalit
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:31
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/19; H10P32/12; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S252/00; Y10S252/95; Y10S252/951; Y10S438/00; Y10S438/909
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
42 words
A method for diffusing aluminum into a semiconductor comprising: (a) disposing a semiconductor wafer in a diffusion tube; (b) disposing a single crystal sapphire source wafer in said tube; and (c) heating said tube to a temperature in excess of 1000° C.
Claim 2
Independent Claim
42 words
A method for diffusing aluminum into a semiconductor comprising: (a) disposing a semiconductor wafer in a diffusion tube; (b) disposing a single crystal sapphire source wafer in said tube; and (c) heating said tube to a temperature in excess of 1000° C.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said method further comprises providing a flow of argon gas in said tube.
Claim 4
Dependent Claim
29 words
The method of claim 2 wherein providing said flow comprises providing a flow in excess of about 10 milliliter/cm 3 of tube cross-sectional area per minute through said tube.
Claim 5
Dependent Claim
21 words
The method of claim 2 wherein providing said flow further comprises providing at least some hydrogen along with said argon gas.
Claim 6
Dependent Claim
22 words
The method of claim 4 wherein providing said flow comprises providing a flow of between about 10 and 30 ml/cm 2 /min.
Claim 7
Dependent Claim
15 words
The method of claim 1 wherein said sapphire source wafer has an "as cut" surface.
Claim 8
Dependent Claim
20 words
The method of claim 6 further comprising providing a flow of argon gas through said tube during said heating step.
Claim 9
Dependent Claim
14 words
The method of claim 7 further comprising providing about 10% hydrogen in said flow.
Claim 10
Dependent Claim
20 words
The method of claim 7 wherein said flow comprises a flow of between about 10 and 30 ml/cm 2 /min.
Claim 11
Independent Claim
101 words
A method for forming a uniform p-conductivity type region in an n-conductivity type silicon wafer from an aluminum oxide source comprising: providing an aluminum oxide wafer carrier; disposing a plurality of aluminum oxide source wafers in said carrier in spaced-apart relationship; disposing a plurality of silicon target wafers between said source wafers in said carrier; and heating said carrier, source wafers and target wafers in an open diffusion tube in an atmosphere of argon to a temperature sufficient to cause diffusion of aluminum atoms into said target wafers whereby such diffusion is substantially uniform over the surface of said target wafers.
Claim 12
Independent Claim
101 words
A method for forming a uniform p-conductivity type region in an n-conductivity type silicon wafer from an aluminum oxide source comprising: providing an aluminum oxide wafer carrier; disposing a plurality of aluminum oxide source wafers in said carrier in spaced-apart relationship; disposing a plurality of silicon target wafers between said source wafers in said carrier; and heating said carrier, source wafers and target wafers in an open diffusion tube in an atmosphere of argon to a temperature sufficient to cause diffusion of aluminum atoms into said target wafers whereby such diffusion is substantially uniform over the surface of said target wafers.
Claim 13
Dependent Claim
68 words
The method of claim 10 wherein said wafer carrier comprises a bottom portion having grooves therein for supporting said source wafers and said target wafers in upstanding, spaced-apart relationship, and a top portion cooperating with said bottom portion to form a tube surrounding said wafers, said tube acting as an auxiliary diffusion source for increasing the uniformity of diffusion in the target wafers, especially at the edges thereof.
Claim 14
Independent Claim
101 words
A method for forming a p-conductivity type region in a silicon semiconductor body, said region being a deep region for high voltage and having a high surface concentration comprising: providing a wafer carrier, said wafer carrier being fabricated of boron nitride; disposing a plurality of aluminum oxide source wafers into said carrier; disposing a plurality of silicon target wafers adjacent said aluminum oxide source wafers; heating said wafers and said carrier to a temperature in excess of 1000° C. to cause both aluminum from said aluminum oxide and boron from said boron nitride to simultaneously diffuse into said silicon target wafers.
Claim 15
Independent Claim
101 words
A method for forming a p-conductivity type region in a silicon semiconductor body, said region being a deep region for high voltage and having a high surface concentration comprising: providing a wafer carrier, said wafer carrier being fabricated of boron nitride; disposing a plurality of aluminum oxide source wafers into said carrier; disposing a plurality of silicon target wafers adjacent said aluminum oxide source wafers; heating said wafers and said carrier to a temperature in excess of 1000° C. to cause both aluminum from said aluminum oxide and boron from said boron nitride to simultaneously diffuse into said silicon target wafers.
Claim 16
Dependent Claim
22 words
The method of claim 12 wherein said heating comprises heating in an open diffusion tube having a flow of inert gas therein.
Claim 17
Dependent Claim
16 words
The method of claim 13 wherein said flow of gas is a flow of argon gas.
Claim 18
Dependent Claim
16 words
The method of claim 14 wherein said flow of gas further comprises about 10% hydrogen gas.
Claim 19
Dependent Claim
28 words
The method of claim 14 wherein said carrier comprises a tubular carrier having a top and a bottom portion cooperating to substantially surround said source and target wafers.
References Cited (Backward Citations)
US3314833A
Cited
US3374125A
Cited
US3577287A
Cited
US3644154A
Cited
US3834349A
Cited
US3939017A
Cited
US3842794A
Cited
US4040878A
Cited
US4141738A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-16 | 1984-06-16 | 1984-12-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-16 | 1988-06-16 | 1988-12-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-16 | 1992-06-16 | 1992-12-16 | $7700.00 | Window Closed / Lapsed |