Method of and structure for forming a reaction product such as calcium silicate and the resulting structure
Assignee: Redco NV SA
•
Filing: 1979-02-16
•
Granted: 1980-12-09
•
Expires: 1999-02-16
Abstract
Abstract Calcium silicate insulation is formed by a process which involves the transfer of the calcium silicate crystals from an autoclave to a holding vessel at a flow rate selected to minimize or prevent damage to the reaction product and through a flow passage such that heat can be removed from the reaction product to stabilize the reaction product prior to its arrival at the holding tank. The calcium silicate material produced by this process is particularly suitable for use as high temperature insulation and has a porosity of in excess of 84% and a permeability to gas of about 0.01% or less. The thermal conductivity of the reaction product is substantially lower than prior art calcium silicate insulations at high temperature.
Inventors
- 👤 Pieter Krijgsman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:19
CPC Classifications
B; B01; B01J; B01J3/00; B01J3/02; C; C01; C01B; C01B33/00; C01B33/20; C01B33/24; C04; C04B; C04B28/00; C04B28/18; Y; Y02; Y02P; Y02P40/00; Y02P40/60; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
86 words
The method of forming a reaction product comprising the steps of: mixing the reaction constituents in an autoclave; reacting the reaction constituents for a selected time to form reaction products; and transferring, at the end of said selected time, the reaction products from said autoclave to another vessel connected by a flow passage to said autoclave, while maintaining the pressure in said vessel in a controlled manner beneath the pressure in said autoclave during the transfer of the reaction products from said autoclave to said vessel.
Claim 2
Independent Claim
86 words
The method of forming a reaction product comprising the steps of: mixing the reaction constituents in an autoclave; reacting the reaction constituents for a selected time to form reaction products; and transferring, at the end of said selected time, the reaction products from said autoclave to another vessel connected by a flow passage to said autoclave, while maintaining the pressure in said vessel in a controlled manner beneath the pressure in said autoclave during the transfer of the reaction products from said autoclave to said vessel.
Claim 3
Dependent Claim
80 words
The method of claim 1 wherein the step of transferring, at the end of said selected time, the reaction products from said autoclave to said vessel comprises: maintaining the pressure in said vessel in a controlled manner below the pressure in said autoclave during the transfer of said reaction products from said autoclave to said vessel; and removing a portion of the energy in said reaction products during the transfer of said reaction products from said autoclave to said vessel.
Claim 4
Dependent Claim
83 words
The method of claim 2 wherein said step of transferring the reaction products from said autoclave to said vessel comprises: maintaining the pressure in said vessel in a controlled manner beneath the pressure in said autoclave, allowing the reaction products in said autoclave to flow from said autoclave to said vessel through said flow passage, and transferring a portion of the heat in said reaction products from said reaction products to another material thereby to make available the tranferred heat for further use.
Claim 5
Dependent Claim
58 words
The method of claim 3 wherein said step of allowing the reaction products in said autoclave to flow from said autoclave to said vessel through said flow passage comprises allowing said reaction products to flow through said flow passage at a rate such that the reaction products are not substantially altered as a result of the flow process.
Claim 6
Dependent Claim
56 words
The method of claim 3 or 4 wherein said step of transferring a portion of the heat in said reaction products from said reaction products to another material comprises transferring heat from said reaction products at a rate so as to stabilize the reaction products in a desired form before the reaction products reach said vessel.
Claim 7
Independent Claim
42 words
The method of claims 1, 2, 3 or 4 wherein the step of transferring the reaction products from said autoclave to said vessel through said flow passage comprises passing said reaction products through said flow passage at a Reynolds number beneath 4,000.
Claim 8
Dependent Claim
26 words
The method of claim 6 wherein the reaction products are transferred from said autoclave to said vessel through said flow passage by a laminar flow process.
Claim 9
Dependent Claim
17 words
The method of claim 7 wherein the laminar flow process has a Reynolds number of about 200.
Claim 10
Independent Claim
27 words
The method of claims 1, 2, 3 or 4 wherein said reaction product is calcium silicate and said reaction constituents comprise calcium hydroxide, silicon dioxide and water.
Claim 11
Independent Claim
27 words
The method of claims 1, 2, 3 or 4 wherein said reaction product comprises calcium silicate and said reaction constituents comprise calcium oxide, silicon dioxide and water.
Claim 12
Dependent Claim
31 words
The method of claim 9 wherein the weight ratio of calcium hydroxide to silicon dioxide is selected to give a mole ratio of calcium oxide to silicon dioxide of approximately one-to-one.
Claim 13
Dependent Claim
18 words
The method of claim 10 wherein the mole ratio of calcium oxide to silicon dioxide is approximately one-to-one.
Claim 14
Dependent Claim
22 words
The method of claim 11 wherein said selected time is such as to insure the formation of xonotlite crystals in said autoclave.
Claim 15
Dependent Claim
22 words
The method of claim 12 wherein said selected time is such as to insure the formation of xonotlite crystals in said autoclave.
Claim 16
Dependent Claim
44 words
The method of claim 3 wherein said material containing the heat transferred from said reaction products is water which is suitable for use as a reaction constituent in said autoclave thereby to reduce the energy required to form a subsequent batch of reaction products.
Claim 17
Dependent Claim
45 words
The method of claim 1 wherein said reaction product is calcium silicate and the step of reacting the reaction constituents comprises heating the constituents to a temperature of about 197.4° C. at a pressure of about 15 bars for about one hour and fifteen minutes.
Claim 18
Dependent Claim
56 words
The method of claim 1 wherein the pressure in said vessel is maintained beneath the pressure in said autoclave during the transfer of the contents of said autoclave to said vessel by an amount sufficient to prevent the rupture of the reaction products during the transfer of these reaction products from the autoclave to the vessel.
Claim 19
Independent Claim
185 words
The method of forming calcium silicate comprising the steps of mixing reaction constituents consisting of calcium hydroxide and silicon dioxide so as to provide a mole ratio of calcium oxide to silicon dioxide of approximately one-to-one and water in an autoclave; heating the reaction constituents to a selected temperature and pressure for a selected time sufficient to allow the formation of a reaction product made up substantially of xonotlite crystals; transferring the reaction products in said autoclave from said autoclave through a flow passage to another vessel at the end of said selected time while maintaining the pressure in said vessel no more than a selected amount beneath the pressure in said autoclave during the transfer of said reaction products from said autoclave to said vessel and simultaneously removing a portion of the heat from said reaction products while they pass through said flow passage; adding selected fibrous material to said reaction product; mixing said fibrous material substantially uniformly throughout said reaction product thereby to form a slurry; removing a selected amount of water from said slurry; and forming said slurry into selectively shaped insulation.
Claim 20
Independent Claim
185 words
The method of forming calcium silicate comprising the steps of mixing reaction constituents consisting of calcium hydroxide and silicon dioxide so as to provide a mole ratio of calcium oxide to silicon dioxide of approximately one-to-one and water in an autoclave; heating the reaction constituents to a selected temperature and pressure for a selected time sufficient to allow the formation of a reaction product made up substantially of xonotlite crystals; transferring the reaction products in said autoclave from said autoclave through a flow passage to another vessel at the end of said selected time while maintaining the pressure in said vessel no more than a selected amount beneath the pressure in said autoclave during the transfer of said reaction products from said autoclave to said vessel and simultaneously removing a portion of the heat from said reaction products while they pass through said flow passage; adding selected fibrous material to said reaction product; mixing said fibrous material substantially uniformly throughout said reaction product thereby to form a slurry; removing a selected amount of water from said slurry; and forming said slurry into selectively shaped insulation.
Claim 21
Dependent Claim
74 words
The method of claim 18 wherein the steps of removing a selected amount of water from said slurry and forming said slurry into insulation comprise: placing said slurry in a mold; removing water from said slurry; subjecting said slurry in said mold to pressure for a selected time to form a molded product; and drying said molded product to remove substantially all the remaining water from said product thereby to form calcium silicate insulation.
Claim 22
Dependent Claim
29 words
The method of claim 19 wherein said calcium silicate insulation has a density in the range of between 200 kilograms per cubic meter to 400 kilograms per cubic meter.
Claim 23
Dependent Claim
34 words
The method of claim 18 wherein said step of adding selected fibrous material comprises first adding non-nodulated mineral wool fibers dispersed uniformly in water and then adding cellulose fibers also dispersed uniformly in water.
Claim 24
Dependent Claim
27 words
Calcium silicate insulation comprising crystals of beta wollastonite with a porosity of greater than about 84 percent and a gas permeability of less than about 0.01 percent.
Claim 25
Dependent Claim
27 words
Calcium silicate insulation comprising crystals of beta wollastonite with a porosity of greater than about 84 percent and a gas permeability of less than about 0.01 percent.
Claim 26
Dependent Claim
22 words
Calcium silicate insulation with a porosity of greater than about 84 percent and a gas permeability of less than about 0.01 percent.
Claim 27
Dependent Claim
22 words
Calcium silicate insulation with a porosity of greater than about 84 percent and a gas permeability of less than about 0.01 percent.
Claim 28
Dependent Claim
37 words
Insulation as in claim 23 with a thermal conductivity given as a function of temperature by the following table: ______________________________________
Temperature mean Thermal conductivity
(degrees centigrade)
(Kcal/m/h/°C.)
______________________________________
200 0.0555
400 0.0758
600 0.1055
800 0.1344
______________________________________
Claim 29
Dependent Claim
47 words
Insulation as in claim 23 with a thermal conductivity given approximately as a function of temperature by the following table: ______________________________________
Thermal conductivity
Temperature (K cal per hour, per meter per
(degrees centigrade)
degree centigrade)
______________________________________
20 0.07
300 0.11
600 0.17
900 0.22
1000 0.24
______________________________________
Claim 30
Dependent Claim
22 words
Insulation as in claim 23 wherein said insulation comprises predominantly xonotlite crystals which transform to beta wollastonite crystals at about 865° C.
Claim 31
Dependent Claim
17 words
Insulation comprising crystals of calcium silicate with cellulose and non-nodulated mineral wool fibers mixed substantially uniformly therethrough.
Claim 32
Dependent Claim
17 words
Insulation comprising crystals of calcium silicate with cellulose and non-nodulated mineral wool fibers mixed substantially uniformly therethrough.
Claim 33
Dependent Claim
38 words
Insulation as in claim 27 wherein said cellulose fibers and said non-nodulated mineral wool fibers each comprise by weight about 2.5 percent of the weight of the calcium hydroxide and silicon dioxide used to form said calcium silicate.
Claim 34
Dependent Claim
24 words
Insulation as in claim 28 wherein the density of said insulation is between 200 kilograms per cubic meter and 400 kilograms per cubic meter.
Claim 35
Dependent Claim
9 words
The product made by the process of claim 18.
Claim 36
Dependent Claim
20 words
The method of claim 19 wherein said step of drying said molded product comprises subjecting said product to infrared radiation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-12-09 | 1984-06-09 | 1984-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-12-09 | 1988-06-09 | 1988-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-12-09 | 1992-06-09 | 1992-12-09 | $7700.00 | Window Closed / Lapsed |