Abstract
Abstract A semicrystalline silicon solar energy cell formed from individual grains of silicon having portions thereof at the light-receiving surface of the cell. An electrical junction is formed at said light-receiving surface and extends across and below that surface and into and between the boundaries of adjoining grains to an extent such that the total junction area substantially exceeds the product of the linear dimensions of the wafer surface but does not extend completely around the boundaries of the silicon grains or to the opposed surface of the wafer.
Inventors
- 👤 Joseph Lindmayer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:25
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/10; H10F77/16; H10F77/162; H10F77/164; H10F77/1642; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/546; Y10; Y10S; Y10S148/00; Y10S148/025; Y10S148/12; Y10S148/122; Y10S438/00; Y10S438/914; Y10S438/922
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
215 words
A method of making a photovoltaic cell from a wafer of semicrystalline silicon having a surface adapted for the impingement of light thereon, said surface being formed from individual grains of silicon having a mean diameter of at least about 100 microns and grain boundaries that at said surface are in contact with or separated only slightly from the boundaries of adjoining grains, and a surface opposed to said impingement surface, comprising in a primary diffusion step, diffusing an impurity into said impingement surface of said wafer and then, in a secondary diffusion step, maintaining said wafer in an atmosphere substantially free from said impurity at a temperature and for a period of time sufficient to cause said impurity to penetrate between said grain boundaries and into said individual grains to form a photovoltaic junction at said impingement surface and extending across and below said surface and also into the interior of said wafer along and inwardly of said grain boundaries, said junction penetrating said wafer to a substantial depth whereby the total junction area exceeds the product of the linear dimensions of said wafer surface but not to an extent whereby said junction extends completely around the boundaries of said silicon grains or from said impingement surface to said opposed surface of said wafer.
Claim 2
Independent Claim
215 words
A method of making a photovoltaic cell from a wafer of semicrystalline silicon having a surface adapted for the impingement of light thereon, said surface being formed from individual grains of silicon having a mean diameter of at least about 100 microns and grain boundaries that at said surface are in contact with or separated only slightly from the boundaries of adjoining grains, and a surface opposed to said impingement surface, comprising in a primary diffusion step, diffusing an impurity into said impingement surface of said wafer and then, in a secondary diffusion step, maintaining said wafer in an atmosphere substantially free from said impurity at a temperature and for a period of time sufficient to cause said impurity to penetrate between said grain boundaries and into said individual grains to form a photovoltaic junction at said impingement surface and extending across and below said surface and also into the interior of said wafer along and inwardly of said grain boundaries, said junction penetrating said wafer to a substantial depth whereby the total junction area exceeds the product of the linear dimensions of said wafer surface but not to an extent whereby said junction extends completely around the boundaries of said silicon grains or from said impingement surface to said opposed surface of said wafer.
Claim 3
Dependent Claim
44 words
A method of making a photovoltaic cell as claimed in claim 1, in which said impurity in said primary diffusion step is phosphorus and is diffused into said wafer at a temperature of about 850° to 900° C. for about 5 to 20 minutes.
Claim 4
Dependent Claim
50 words
A method of making a photovoltaic cell as claimed in claim 1 or claim 2, in which said wafer in said secondary diffusion step is maintained in an atmosphere substantially free from said impurity at a temperature of about 800° to 850° C. for about 5 minutes to one hour.
References Cited (Backward Citations)
US3900943A
Cited
US3990097A
Cited
US4028151A
Cited
US4082889A
Cited
US4155785A
Cited
US4113531A
Cited
US4162177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-28 | 1984-04-28 | 1984-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-28 | 1988-04-28 | 1988-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-28 | 1992-04-28 | 1992-10-28 | $7700.00 | Window Closed / Lapsed |