Method of producing silicon-iron sheet material with boron addition, and product
Assignee: General Electric Co
•
Filing: 1977-03-25
•
Granted: 1980-01-29
•
Expires: 1997-03-25
Abstract
Abstract By adding a relatively small amount of boron to the electrolytically-deposited Mg(OH) 2 coating on silicon-iron magnetic sheet containing a small but critical amount of boron, a substantial improvement in permeability of the finally-annealed product sheet material can be obtained.
Inventors
- 👤 Carl M. Maucione
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:35
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/16; C; C21; C21D; C21D8/00; C21D8/12; C21D8/1277; C21D8/1283; C22; C22C; C22C38/00; C22C38/02; C22C38/04; C22C38/16; C22C38/60; C21D8/1244; C21D8/1272
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
123 words
The method of producing grain-oriented silicon-iron sheet of enhanced magnetic properties which comprises the steps of providing a fine-grained, primary-recrystallized, silicon-iron sheet containing 2.2 to 4.5 percent silicon, between about three and 50 parts per million boron, amounts of manganese and sulfur within a ratio of manganese to sulfur less than 2.3, and between about 30 and 90 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, covering the sheet with an adherent electrically-insulating coating containing boron in amount effective to cause secondary recrystallization of the silicon-iron sheet during final heat treatment, and subjecting the coated sheet to a final sheet heat treatment to develop (110) [001] secondary recrystallization texture in the silicon-iron sheet.
Claim 2
Independent Claim
123 words
The method of producing grain-oriented silicon-iron sheet of enhanced magnetic properties which comprises the steps of providing a fine-grained, primary-recrystallized, silicon-iron sheet containing 2.2 to 4.5 percent silicon, between about three and 50 parts per million boron, amounts of manganese and sulfur within a ratio of manganese to sulfur less than 2.3, and between about 30 and 90 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, covering the sheet with an adherent electrically-insulating coating containing boron in amount effective to cause secondary recrystallization of the silicon-iron sheet during final heat treatment, and subjecting the coated sheet to a final sheet heat treatment to develop (110) [001] secondary recrystallization texture in the silicon-iron sheet.
Claim 3
Dependent Claim
19 words
The method of claim 1 in which the boron in the coating is in the form of boric acid.
Claim 4
Dependent Claim
19 words
The method of claim 1 in which the boron in the coating is in the form of sodium borate.
Claim 5
Dependent Claim
30 words
The method of claim 1 including the steps of forming an electrically-insulating coating on the sheet and then contacting the then-coated sheet with an aqueous solution of a boron compound.
Claim 6
Dependent Claim
22 words
The method of claim 4 in which the aqueous solution contains about five grams-per-liter of Na 2 B 4 O 7 .
Claim 7
Dependent Claim
22 words
The method of claim 4 in which the aqueous solution contains about ten grams-per-liter of Na 2 B 4 O 7 .
Claim 8
Dependent Claim
25 words
The method of claim 4 in which the boron compound is boric acid and the solution contains between one and 15 grams-per-liter of said acid.
Claim 9
Dependent Claim
31 words
The method of claim 1 in which the boron content of the coating is equivalent to between about 50 and 80 parts per million on the basis of the silicon-iron sheet.
Claim 10
Dependent Claim
92 words
An electrically-insulated magnetic sheet material of enhanced magnetic properties comprising a fine-grained, primary-recrystallized, magnetic, silicon-iron sheet containing between three and 50 parts per million boron, amounts of manganese and sulfur within a ratio of manganese to sulfur less than 2.3, and between about 30 and 90 parts per million nitrogen and having thereon a thin and tightly-adherent coating of a water-insoluble hydroxide of a metal selected from the group consisting of calcium, magnesium, manganese and aluminum containing boron in amount effective to cause secondary recrystallization of the silicon-iron sheet during final anneal.
Claim 11
Dependent Claim
92 words
An electrically-insulated magnetic sheet material of enhanced magnetic properties comprising a fine-grained, primary-recrystallized, magnetic, silicon-iron sheet containing between three and 50 parts per million boron, amounts of manganese and sulfur within a ratio of manganese to sulfur less than 2.3, and between about 30 and 90 parts per million nitrogen and having thereon a thin and tightly-adherent coating of a water-insoluble hydroxide of a metal selected from the group consisting of calcium, magnesium, manganese and aluminum containing boron in amount effective to cause secondary recrystallization of the silicon-iron sheet during final anneal.
Claim 12
Dependent Claim
53 words
The sheet material of claim 9 in which the coating is an electrolytic Mg(OH) 2 coating, the silicon-iron sheet contains about ten parts per million boron and about 30 parts per million nitrogen, and the coating contains between about 50 and 80 parts per million boron on the basis of the silicon-iron sheet.
References Cited (Backward Citations)
US3054732A
Cited
US3222228A
Cited
US3676227A
Cited
US3583887A
Cited
US3945862A
Cited
US3905843A
Cited
US3905842A
Cited
US3957546A
Cited
US4097343A
Cited
US4116730A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-01-28 | 1983-07-30 | 1984-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-01-28 | 1987-07-30 | 1988-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-01-28 | 1991-07-30 | 1992-01-29 | $7700.00 | Window Closed / Lapsed |