Method for rendering non-platable surfaces platable
Assignee: Surface Technology Inc
•
Filing: 1977-06-06
•
Granted: 1980-01-01
•
Expires: 1997-06-06
Abstract
Abstract A process is described for the reception of electroless plating onto a non-catalytic metal or alloy substrate, non-catalytic to conventional electroless plating. The process comprises contacting the non-catalytic substrate with a promoter composition comprising ions selected from the group consisting of nickel, cobalt, iron and mixtures thereof; and a suitable reducing agent capable of chemically interacting with the non-catalytic metal or alloy and the metal ions in the promoter composition and further wherein the relative concentration of the reducing agent to metal ions is so adjusted as to yield first a reaction of the reducing agent with the non-catalytic metal or alloy and thereafter a heterogeneous reduction of the metal ions; and thereafter contacting the treated substrate with a conventional electroless plating bath, e.g, a nickel or cobalt-hypophosphite type bath or a copper-formaldehyde type bath for the metallic build-up.
Inventors
- 👤 Nathan Feldstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:20
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/1803; C23C18/1824; C23C18/1837; C23C18/1841; C23C18/1601; C23C18/1633; C23C18/1646; C23C18/165; C23C18/1651; C23C18/20; C23C18/2006; C23C18/2046; C23C18/2073; C23C18/2086; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/22; H05K3/24; H05K3/244; H05K3/245
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
199 words
A process for metallizing a non-catalytic metal or alloy wherein said non-catalytic metal or alloy is selected from the group consisting of copper, gold, silver, chromium containing stainless steels, zinc, chromium, Kovar, moly, moly-manganese, aluminum and its alloys by conventional electroless plating comprising the steps of: (a) contacting said non-catalytic metal or alloy with a promoter composition wherein said promoter composition comprises a suitable reducing agent and metal ions wherein said reducing agent is capable of chemically reacting with said non-catalytic metal or alloy and the metal ions within the promoter composition and wherein said metal ions are selected from the group consisting of nickel, cobalt, and iron and mixtures thereof, and wherein the relative molar concentration of the reducing agent to the metal ions is so adjusted as to permit the initial chemical interaction of the reducing agent with the non-catalytic metal or alloy and then the heterogeneous reduction of the metal ions present in the promoter composition and wherein said relative molar concentration is adjusted to yield a molar excess of the reducing agent, and then (b) contacting the treated non-catalytic metal or alloy with a conventional electroless plating bath wherein said electroless plating bath comprises hypophosphite.
Claim 2
Dependent Claim
199 words
A process for metallizing a non-catalytic metal or alloy wherein said non-catalytic metal or alloy is selected from the group consisting of copper, gold, silver, chromium containing stainless steels, zinc, chromium, Kovar, moly, moly-manganese, aluminum and its alloys by conventional electroless plating comprising the steps of: (a) contacting said non-catalytic metal or alloy with a promoter composition wherein said promoter composition comprises a suitable reducing agent and metal ions wherein said reducing agent is capable of chemically reacting with said non-catalytic metal or alloy and the metal ions within the promoter composition and wherein said metal ions are selected from the group consisting of nickel, cobalt, and iron and mixtures thereof, and wherein the relative molar concentration of the reducing agent to the metal ions is so adjusted as to permit the initial chemical interaction of the reducing agent with the non-catalytic metal or alloy and then the heterogeneous reduction of the metal ions present in the promoter composition and wherein said relative molar concentration is adjusted to yield a molar excess of the reducing agent, and then (b) contacting the treated non-catalytic metal or alloy with a conventional electroless plating bath wherein said electroless plating bath comprises hypophosphite.
Claim 3
Dependent Claim
13 words
The process according to claim 1 wherein said reducing agent is dimethylamine borane.
Claim 4
Dependent Claim
16 words
The process according to claim 1 wherein said silver is derived from a silver ink composition.
Claim 5
Dependent Claim
15 words
The process according to claim 1 wherein said electroless plating bath additionally comprises nickel ions.
Claim 6
Dependent Claim
15 words
The process according to claim 1 wherein said promoter composition is used above room temperature.
Claim 7
Dependent Claim
16 words
The process according to claim 1 wherein said promoter composition is used at an alkaline pH.
Claim 8
Dependent Claim
19 words
The process according to claim 1 further containing the step of heat treating the metallized non-catalytic metal or alloy.
Claim 9
Dependent Claim
25 words
The process according to claim 1 wherein said relative molar concentration of reducing agent to metal ions is at least 2:1 and less than 15:1.
Claim 10
Dependent Claim
156 words
A process for metallizing a non-catalytic to conventional electroless plating metal or alloy by conventional electroless plating comprising the steps of: (a) contacting said non-catalytic metal or alloy with a promotor composition wherein said promoter composition comprises a suitable reducing agent and metal ions and wherein said reducing agent is capable of chemically reacting with said non-catalytic metal or alloy and the metal ions within the promoter composition and wherein said metal ions are selected from the group consisting of nickel, cobalt, and iron and mixtures thereof, and wherein the relative molar concentration of the reducing agent to the metal ions is sufficient to permit the initial chemical interaction of the reducing agent with the non-catalytic metal or alloy and then the heterogeneous reduction of the metal ions present in the promoter composition, then (b) contacting the treated non-catalytic metal or alloy with a conventional electroless plating bath and wherein said electroless plating bath comprises hypophosphite.
Claim 11
Dependent Claim
156 words
A process for metallizing a non-catalytic to conventional electroless plating metal or alloy by conventional electroless plating comprising the steps of: (a) contacting said non-catalytic metal or alloy with a promotor composition wherein said promoter composition comprises a suitable reducing agent and metal ions and wherein said reducing agent is capable of chemically reacting with said non-catalytic metal or alloy and the metal ions within the promoter composition and wherein said metal ions are selected from the group consisting of nickel, cobalt, and iron and mixtures thereof, and wherein the relative molar concentration of the reducing agent to the metal ions is sufficient to permit the initial chemical interaction of the reducing agent with the non-catalytic metal or alloy and then the heterogeneous reduction of the metal ions present in the promoter composition, then (b) contacting the treated non-catalytic metal or alloy with a conventional electroless plating bath and wherein said electroless plating bath comprises hypophosphite.
Claim 12
Dependent Claim
34 words
The process according to claim 9 wherein said non-catalytic metal or alloy is selected from the group consisting of gold, copper, silver, chromium, aluminum and its alloys, tool steel, Kovar, moly, moly-manganese and zinc.
Claim 13
Dependent Claim
21 words
The process according to claim 9 wherein said reducing agent is selected from the group consisting of amineboranes, borohydrides and hydrazine.
Claim 14
Dependent Claim
21 words
The process according to claim 9 wherein said relative molar concentration of reducing agent to metal ions is at least 1:1.
Claim 15
Dependent Claim
18 words
The process according to claim 9 containing the step of heat treating the metallized non-catalytic metal or alloy.
Claim 16
Dependent Claim
16 words
The process according to claim 9 wherein said promoter composition is used at an alkaline pH.
Claim 17
Dependent Claim
15 words
The process according to claim 9 wherein said promoter composition is used above room temperature.
Claim 18
Dependent Claim
15 words
The process according to claim 9 wherein said electroless plating bath further comprises nickel ions.
Claim 19
Dependent Claim
27 words
The process according to claim 9 wherein said relative molar concentration of the reducing agent to the metal ions is at least 2:1 and less than 15:1.
References Cited (Backward Citations)
US3666529A
Cited
US3853590A
Cited
US3772056A
Cited
US3962494A
Cited
US4002778A
Cited
US3870526A
Cited
US3958048A
Cited
US3993801A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-31 | 1983-07-02 | 1984-01-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-31 | 1987-07-02 | 1988-01-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-31 | 1991-07-02 | 1992-01-01 | $7700.00 | Window Closed / Lapsed |