Abstract
Abstract Improved processes and systems are described for the reception of electroless plating of non-metallic substrates, the processes comprising forming a coating of metal ions onto the non-metallic substrate, immersing the coated substrate in a developer solution containing ions selected from nickel, cobalt and copper ions and mixtures thereof and a reducing agent, and thereafter immersing the substrate in conventional electroless plating baths, e.g., nickel or cobalt-hypophosphite baths or a copper-formaldehyde bath.
Inventors
- 👤 Nathan Feldstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 15:34
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
85 words
An improved developer solution useful in developing substrates primed with non-precious metal ions, said developer solution comprising ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of first reducing the non-precious metal ions of said substrate to the metallic state and then heterogeneously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 2
Dependent Claim
85 words
An improved developer solution useful in developing substrates primed with non-precious metal ions, said developer solution comprising ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of first reducing the non-precious metal ions of said substrate to the metallic state and then heterogeneously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 3
Dependent Claim
21 words
The developer of claim 1, wherein said reducing agent is selected from the group consisting of amine-boranes, borohydrides and mixtures thereof.
Claim 4
Dependent Claim
25 words
The developer of claim 1, wherein said non-precious metal ions are selected from the group consisting of copper, nickel, cobalt, iron, tin and mixtures thereof.
Claim 5
Dependent Claim
25 words
The developer of claim 1, wherein the molar ratio of said reducing agent to said ions in solution is from about 2:1 to about 15:1.
Claim 6
Dependent Claim
87 words
An improved process for developing non-precious metal primed substrates comprising contacting said substrates with a developer solution comprised of ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of first reducing the non-precious metal ions on said substrate to the metallic state and then heterogenously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 7
Dependent Claim
87 words
An improved process for developing non-precious metal primed substrates comprising contacting said substrates with a developer solution comprised of ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of first reducing the non-precious metal ions on said substrate to the metallic state and then heterogenously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 8
Dependent Claim
21 words
The process of claim 5, wherein said reducing agent is selected from the group consisting of amine-boranes, borohydrides and mixtures thereof.
Claim 9
Dependent Claim
18 words
The process of claim 5 wherein said metal ions are selected from the group consisting of copper, nickel,
Claim 10
Dependent Claim
25 words
The process of claim 5, wherein the molar ration of said reducing agent to said ions in solution is from about 2:1 to about 15:1.
Claim 11
Dependent Claim
102 words
An improved process for preparing non-metallic substrates for electroless plating comprising: A. forming on the surface of a non-metallic substrate a primer composition containing non-precious metal ions; and B. immersing said substrate in a developer solution comprising ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of reducing the metal ions on said substrate to the metallic state, and heterogeneously reducing the metal ions in said developer solution to their metallic state, the molar ratio of said reducing agent to said ions in the developer solution being at least 1:1.
Claim 12
Dependent Claim
102 words
An improved process for preparing non-metallic substrates for electroless plating comprising: A. forming on the surface of a non-metallic substrate a primer composition containing non-precious metal ions; and B. immersing said substrate in a developer solution comprising ions of a metal selected from the group consisting of copper, nickel, cobalt and mixtures thereof, and a reducing agent capable of reducing the metal ions on said substrate to the metallic state, and heterogeneously reducing the metal ions in said developer solution to their metallic state, the molar ratio of said reducing agent to said ions in the developer solution being at least 1:1.
Claim 13
Dependent Claim
34 words
The process of claim 9 wherein said substrate contacted with primer by immersing said substrate in a primer solution containing metal ions selected from the group consisting of copper, nickel, cobalt and mixtures thereof.
Claim 14
Dependent Claim
21 words
The process of claim 9, wherein said reducing agent is selected from the group consisting of amine-boranes, borohydrides and mixtures thereof.
Claim 15
Dependent Claim
27 words
The process of claim 9, wherein the molar ratio of said reducing agent and said ions in said developer solution is from about 2:1 to about 15:1.
Claim 16
Dependent Claim
14 words
The process recited in claim 9 wherein said primer composition is a colloidal dispersion.
Claim 17
Dependent Claim
19 words
The process recited in claim 9 wherein said primer composition comprises a colloidal dispersion of metal or metallic alloy.
Claim 18
Dependent Claim
28 words
The process recited in claim 9 wherein said primer composition comprises copper and tin ions where said tin ions are in excess of said copper ions plus phenol.
Claim 19
Dependent Claim
105 words
An improved process for forming a metalic pattern on a non-metallic substrate comprising: A. selectively forming a pattern of non-precious metal ions on a non-metallic substrate; and B. contacting said substrate with a developer solution comprised of ions of a metal selected from the group consisting of copper, nickel, cobalt, iron, and mixtures thereof, and a reducing agent capable of first reducing the metal ions on said substrate to the metalic state and then heterogenously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 20
Dependent Claim
105 words
An improved process for forming a metalic pattern on a non-metallic substrate comprising: A. selectively forming a pattern of non-precious metal ions on a non-metallic substrate; and B. contacting said substrate with a developer solution comprised of ions of a metal selected from the group consisting of copper, nickel, cobalt, iron, and mixtures thereof, and a reducing agent capable of first reducing the metal ions on said substrate to the metalic state and then heterogenously reducing the metal ions in said developer solution to their metallic state, said reducing agent and said ions in solution being present in a molar ratio of at least 1:1.
Claim 21
Dependent Claim
21 words
The process of claim 16, wherein said reducing agent is selected from the group consisting of amine-boranes, borohydrides and mixtures thereof.
Claim 22
Dependent Claim
29 words
The process of claim 16, wherein said non-precious metal ions on said non-metallic substrate are selected from the group consisting of copper, nickel, cobalt, iron, tin and mixtures thereof.
Claim 23
Dependent Claim
29 words
The process of claim 16, wherein said reducing agent and said ions in said developer solution are present in a molar ration of from about 2:1 to about 15:1.
Claim 24
Dependent Claim
17 words
The process of claim 16, wherein said pattern is in the form of a printed circuit diagram.
Claim 25
Dependent Claim
97 words
An improved process for electroless nickel plating on a non-metallic substrate primed with copper ions comprising A. contacting said substrate with a developer solution comprising at least one member of the group consisting of nickel and cobalt ions and a reducing agent selected from the group consisting of amineboranes, borohydrides and mixture thereof, said reducing agent and said metal ions being present in a molar ratio of at least 1:1, and B. contacting said substrate with an electroless plating bath comprising nickel ions and a hypophosphite reducing agent whereby a nickel layer is deposited on said substrate.
Claim 26
Dependent Claim
97 words
An improved process for electroless nickel plating on a non-metallic substrate primed with copper ions comprising A. contacting said substrate with a developer solution comprising at least one member of the group consisting of nickel and cobalt ions and a reducing agent selected from the group consisting of amineboranes, borohydrides and mixture thereof, said reducing agent and said metal ions being present in a molar ratio of at least 1:1, and B. contacting said substrate with an electroless plating bath comprising nickel ions and a hypophosphite reducing agent whereby a nickel layer is deposited on said substrate.
References Cited (Backward Citations)
US3318711A
Cited
US3620804A
Cited
US3667991A
Cited
US3666527A
Cited
US3697319A
Cited
US3772078A
Cited
US3772056A
Cited
US3745039A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-23 | 1980-05-24 | 1980-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-23 | 1984-05-24 | 1984-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-23 | 1988-05-24 | 1988-11-23 | $7700.00 | Window Closed / Lapsed |