Copolymer for contact lens, its preparation and contact lens made thereof
Assignee: Menicon Co Ltd
•
Filing: 1978-03-20
•
Granted: 1979-02-13
•
Expires: 1998-03-20
Abstract
Abstract A copolymer suitable for use as contact lenses, comprising a polymerization product of (a) at least one monomer selected from methyldi(trimethylsiloxy)sylylpropylglycerol methacrylate and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate, (b) a hydrophilic monomer, (c) a methacrylic acid alkyl ester and (d) a cross-linking agent having at least two copolymerizable functional groups. Contact lenses made of the above copolymer has excellent oxygen permeability and can be comfortably worn continuously for a long term without a foreign body sensation and pain.
Inventors
- 👤 Kyoichi Tanaka
- 👤 Kouzou Takahashi
- 👤 Mitsuhiro Kanada
- 👤 Yasuyuki Kato
- 👤 Masuji Ichihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:48
CPC Classifications
C; C08; C08F; C08F230/00; C08F230/04; C08F230/08; C07; C07F; C07F7/00; C07F7/02; C07F7/08; C07F7/0834; C07F7/0838; C07F7/0872; C07F7/0889; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C08F220/14; C08F220/26; C08F220/28; C08F220/282; C08F222/00; C08F222/10; C08F222/1006; C08F222/102
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
155 words
A polymerization product of (a) 30 to 80% of at least one monomer selected from the group consisting of methyldi(trimethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR2## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR3## (b) 5 to 30% of at least one hydrophilic monomer selected from the group consisting of ethylene glycol monomethacrylate, diethylene glycol monomethacrylate, triethylene glycol monomethacrylate, N-vinyl pyrrolidone and dimethyl acrylamide, (c) 5 to 60% of at least one methacrylic acid alkyl ester monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and cyclohexyl methacrylate, and (d) 0.5 to 15% of at least one cross-linking agent having at least two copolymerizable functional groups selected from the group consisting of ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, allyl methacrylate, divinyl benzene, diallyl phthalate and trimethylolpropane trimethacrylate, said % of (a), (b), (c) and (d) being % by weight based on the total weight of (a), (b), (c) and (d).
Claim 2
Dependent Claim
155 words
A polymerization product of (a) 30 to 80% of at least one monomer selected from the group consisting of methyldi(trimethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR2## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR3## (b) 5 to 30% of at least one hydrophilic monomer selected from the group consisting of ethylene glycol monomethacrylate, diethylene glycol monomethacrylate, triethylene glycol monomethacrylate, N-vinyl pyrrolidone and dimethyl acrylamide, (c) 5 to 60% of at least one methacrylic acid alkyl ester monomer selected from the group consisting of methyl methacrylate, ethyl methacrylate and cyclohexyl methacrylate, and (d) 0.5 to 15% of at least one cross-linking agent having at least two copolymerizable functional groups selected from the group consisting of ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, allyl methacrylate, divinyl benzene, diallyl phthalate and trimethylolpropane trimethacrylate, said % of (a), (b), (c) and (d) being % by weight based on the total weight of (a), (b), (c) and (d).
Claim 3
Dependent Claim
60 words
The polymerization product of claim 1, having an oxygen permeability of 3.0 × 10 -10 to 32.1 × 10 -10 ml.cm./cm. 2 sec.cmHg, a refractive index of n D 20 = 1.40 to 1.49, a specific gravity of 1.08 to 1.21, a visible ray percent transmission of not less than 90% and a Vickers hardness number of 4.0 to 19.0.
Claim 4
Dependent Claim
127 words
A process for preparing a copolymer which comprises bulk-polymerizing (a) 30 to 80% of at least one monomer selected from the group consisting of methyldi(trimethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR4## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR5## (b) 5 to 30% of a hydrophilic monomer, (c) 5 to 60% of a methacrylic acid alkyl ester monomer, and (d) 0.5 to 15% of a cross-linking agent having at least two copolymerizable functional groups, in the presence of 0.05 to 1.0 part by weight, per 100 parts by weight of the mixture of (a), (b), (c) and (d), of a free radical polymerization initiator, said % of (a), (b), (c) and (d) being % by weight based on the total weight of (a), (b), (c) and (d).
Claim 5
Dependent Claim
127 words
A process for preparing a copolymer which comprises bulk-polymerizing (a) 30 to 80% of at least one monomer selected from the group consisting of methyldi(trimethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR4## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR5## (b) 5 to 30% of a hydrophilic monomer, (c) 5 to 60% of a methacrylic acid alkyl ester monomer, and (d) 0.5 to 15% of a cross-linking agent having at least two copolymerizable functional groups, in the presence of 0.05 to 1.0 part by weight, per 100 parts by weight of the mixture of (a), (b), (c) and (d), of a free radical polymerization initiator, said % of (a), (b), (c) and (d) being % by weight based on the total weight of (a), (b), (c) and (d).
Claim 6
Dependent Claim
30 words
The process of claim 3, wherein the bulk polymerization is thermally carried out for about 60 to about 110 hours by stepwise raising the temperature from 40° to 120° C.
Claim 7
Dependent Claim
59 words
The process of claim 3, wherein the bulk polymerization is carried out first under the ultraviolet irradiation for about 30 to about 40 hours by stepwise raising the temperature from 15° to 50° C., and then thermally carried out without the ultraviolet irradiation for about 30 to 40 hours by stepwise raising the temperature from 50° to 120° C.
Claim 8
Dependent Claim
27 words
The process of claim 3, wherein said free radical polymerization initiator is at least one member selected from the group consisting of benzoyl peroxide, azobisisobutyronitrile and azobisdimethylvaleronitrile.
Claim 9
Dependent Claim
87 words
A contact lens made of a copolymer consisting essentially of (a) 30 to 80% by weight of units of at least one monomer selected from the group consisting of methyldi(triethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR6## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR7## (b) 5 to 30% by weight of hydrophilic monomer units, (c) 5 to 60% by weight of methacrylic acid alkyl ester monomer units, and (d) 0.5 to 15% by weight of units of a cross-linking agent having at least two copolymerizable functional groups.
Claim 10
Dependent Claim
87 words
A contact lens made of a copolymer consisting essentially of (a) 30 to 80% by weight of units of at least one monomer selected from the group consisting of methyldi(triethylsiloxy)sylylpropylglycerol methacrylate having the following formula ##STR6## and methyldi(trimethylsiloxy)sylylpropylglycerolethyl methacrylate having the following formula ##STR7## (b) 5 to 30% by weight of hydrophilic monomer units, (c) 5 to 60% by weight of methacrylic acid alkyl ester monomer units, and (d) 0.5 to 15% by weight of units of a cross-linking agent having at least two copolymerizable functional groups.
Claim 11
Dependent Claim
35 words
The contact lens of claim 7, wherein said hydrophilic monomer is at least one member selected from the group consisting of ethylene glycol monomethacrylate, diethylene glycol monomethacrylate, triethylene glycol monomethacrylate, N-vinyl pyrrolidone and dimethyl acrylamide.
Claim 12
Dependent Claim
31 words
The contact lens of claim 7, wherein said methacrylic acid alkyl ester monomer is at least one member selected from the group consisting of methyl methacrylate, ethyl methacrylate and cyclohexyl methacrylate.
Claim 13
Dependent Claim
39 words
The contact lens of claim 7, wherein said cross-linking agent is at least one member selected from the group consisting of ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, allyl methacrylate, divinyl benzene, diallyl phthalate and trimethylolpropane trimethacrylate.
Claim 14
Dependent Claim
60 words
The contact lens of claim 7, having an oxygen permeability of 3.0 × 10 -10 to 32.1 × 10 -10 ml.cm./cm. 2 sec.cmHg, a refractive index of n D 20 = 1.40 to 1.49, a specific gravity of 1.08 to 1.21, a visible ray percent transmission of not less than 90% and a Vickers hardness number of 4.0 to 19.0.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |