Composition for pre-treating fabric for transfer printing and a transfer printing process
Assignee: Individual
•
Filing: 1977-08-31
•
Granted: 1978-10-10
•
Expires: 1997-08-31
Abstract
Abstract A composition for the treatment of a fabric containing fibres which do not readily retain dyes imparted thereto by transfer printing, such as wool and cellulosic fibres e.g. cotton, the treatment being prior to transfer printing on the fabric and the composition comprising in combination (a) a coating material comprising a self-curing acrylic resin composition, (b) at least one of (i) an agent for softening the fibres of the fabric and (ii) a self-curing elastomeric polysiloxane composition, and optionally one or more of the following ingredients: (c) a curable amine-formaldehyde prepolymer containing free hydroxyl groups, (d) a polymer emulsion, (e) at least one humectant, (f) a wetting agent, and (g) a dispersion stabiliser for the composition. The resin content of the coating deposited from the composition on the fabric is preferably substantially completely cured prior to transfer printing.
Inventors
- 👤 Terry Brook Purser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:41
CPC Classifications
D; D06; D06P; D06P5/00; D06P5/003; D06P5/004; D06P5/005
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
180 words
A method of transfer printing a fabric containing fibres that do not readily retain dyes applied thereto by transfer printing, said method comprising (I) applying to the fabric an aqueous composition formed by the addition to water of (a) a coating material comprising a self-curing acrylic resin composition in an amount to provide 40 to 120 grams of said acrylic resin per liter of said water and excluding any water included in said acrylic resin composition, and (b) at least one of (i) a softening agent for the fibres of the fabric in an amount to provide 8 to 40 grams of said agent per liter of said water and excluding any water added with said softening agent and (ii) a self-curing elastomeric polysiloxane composition in an amount to provide 1 to 35 grams of said polysiloxane composition per liter of said water and excluding any water in said polysiloxane composition. (II) drying the thus treated fabric. (III) transfer printing the fabric thus obtained, (IV) curing the resin content of the coating before, during and/or after the transfer printing step.
Claim 2
Independent Claim
180 words
A method of transfer printing a fabric containing fibres that do not readily retain dyes applied thereto by transfer printing, said method comprising (I) applying to the fabric an aqueous composition formed by the addition to water of (a) a coating material comprising a self-curing acrylic resin composition in an amount to provide 40 to 120 grams of said acrylic resin per liter of said water and excluding any water included in said acrylic resin composition, and (b) at least one of (i) a softening agent for the fibres of the fabric in an amount to provide 8 to 40 grams of said agent per liter of said water and excluding any water added with said softening agent and (ii) a self-curing elastomeric polysiloxane composition in an amount to provide 1 to 35 grams of said polysiloxane composition per liter of said water and excluding any water in said polysiloxane composition. (II) drying the thus treated fabric. (III) transfer printing the fabric thus obtained, (IV) curing the resin content of the coating before, during and/or after the transfer printing step.
Claim 3
Dependent Claim
25 words
A method as claimed in claim 1 in which the softening agent is selected from the group consisting of ethylene polymers and epoxidised vegetable oils.
Claim 4
Dependent Claim
16 words
A method as claimed in claim 1 in which the softening agent is epoxidised soybean oil.
Claim 5
Dependent Claim
46 words
A method as claimed in claim 1 in which said aqueous composition further includes an aqueous emulsion of a vinyl polymer in an amount to give from 2 to 30 grams of the polymer per liter of said water and excluding the water of the emulsion.
Claim 6
Dependent Claim
41 words
A method as claimed in claim 1 in which said aqueous composition further includes a wetting agent provided in an amount of from 2 to 30 grams per liter of said water and excluding any water supplied with the wetting agent.
Claim 7
Dependent Claim
32 words
A method as claimed in claim 1 in which said aqueous composition further includes a dispersion stabiliser provided in an amount of from 1 to 3% by weight of said aqueous composition.
Claim 8
Dependent Claim
13 words
A method as claimed in claim 1 in which the fabric contains cotton.
Claim 9
Dependent Claim
24 words
A method as claimed in claim 1 in which the resin content of the coating is at least partially cured prior to transfer printing.
Claim 10
Dependent Claim
23 words
A method as claimed in claim 1 in which the resin content of the coating is substantially completely cured prior to transfer printing.
Claim 11
Dependent Claim
36 words
A method as claimed in claim 1 in which curing is effected by heating the coated fabric at a temperature of from 165° C. to 170° C. for a period of 30 seconds to 1 minute.
Claim 12
Dependent Claim
33 words
A method as claimed in claim 1 in which the aqueous composition further includes a curable amine-formaldehyde prepolymer containing free hydroxyl groups, in a minor amount compared with that of the acrylic resin.
Claim 13
Dependent Claim
28 words
A method as claimed in claim 11 in which the aqueous composition includes both a softening agent for the fibers of the fabric and a self-curing polysiloxane composition.
Claim 14
Dependent Claim
34 words
A method as claimed in claim 11 in which the prepolymer is provided in an amount of from 20 to 40 grams per liter of said water and excluding any water with said prepolymer.
Claim 15
Dependent Claim
34 words
A method as claimed in claim 13 in which the prepolymer comprises a condensate of formaldehyde with an amine selected from the group consisting of urea, melamine and substituted derivatives of urea and melamine.
Claim 16
Dependent Claim
35 words
A method as claimed in claim 11 in which the aqueous composition further comprises at least one humectant in an amount to provide from 5 to 100 grams of humectant per liter of said water.
Claim 17
Dependent Claim
30 words
A method as claimed in claim 15 in which a glycol selected from the group consisting of alkalene glycols, poly(alkylene oxide) glycols and poly(hydroxyalkyl) cycloalkanes is provided as a humectant.
Claim 18
Dependent Claim
40 words
A method as claimed in claim 15 in which a hydroxylated aliphatic amide is provided as a humectant in an amount of from 5 to 50 grams per liter of said water and excluding any water added with said humectant.
Claim 19
Dependent Claim
113 words
A method as claimed in claim 15 in which said softening agent is selected from ethylene polymers and epoxidised vegetable oils, the composition further contains a prepolymer comprising a condensate of formaldehyde with an amine selected from urea, the group consisting of melamine and substitued derivatives of urea and melamine, and at least one humectant selected from alkylene glycols, poly (alkylene oxide) glycols, poly (hydroxyalkyl) cycloalkanes and hydroxylated aliphatic amides, and the components of the composition are provided in the following amounts per liter of water (excluding any water added with any of the components): acrylic resin 40-120g softener 8-40g self-curing elastomeric polysiloxane composition 1-35g amine-formaldehyde prepolymer 20-40g at least one humectant 5-100g
References Cited (Backward Citations)
CA693453A
Cited
US3592686A
Cited
US3706595A
Cited
US4009000A
Cited
US3997701A
Cited
US3896070A
Cited
US3995992A
Cited
DE2453362A1
Cited
US3935147A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-09 | 1982-04-10 | 1982-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-09 | 1986-04-10 | 1986-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-09 | 1990-04-10 | 1990-10-10 | $7700.00 | Window Closed / Lapsed |