Method of fabricating a semiconductor device
Assignee: RCA Corp
•
Filing: 1977-01-21
•
Granted: 1978-01-03
•
Expires: 1997-01-21
Abstract
Abstract A method of fabricating a semiconductor device comprises steps for forming recesses which can be used in the subsequent visual alignment of photomasks. The novel recess forming steps are so linked with a conventional processing step that the total number of steps required for the formation of the recesses is reduced. The present method is particularly adaptable to the fabrication of unisurface silicon controlled rectifiers wherein a doped isolation-type grid is formed to define each device.
Inventors
- 👤 Wojciech Rosnowski
- 👤 Richard Denning
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:39
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/17; H10P32/171; H10P50/60; H10P50/64; H10P50/642; H10P50/644; H10W; H10W46/00; H10W46/301; H10W46/501; Y; Y10; Y10S; Y10S438/00; Y10S438/914; Y10S438/92; Y10S438/975
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
154 words
A method of fabricating a semiconductor device comprising the steps of: heating, in an ambient containing oxygen, a body of silicon having a layer of aluminum on a portion of a surface thereof to a temperature whereat said aluminum diffuses into said body and maintaining said body at said temperature for a preselected period of time, whereby said aluminum diffuses into said body and simultaneously forms an aluminum/silicon alloy on said portion of said surface, said aluminum/silicon alloy having a cap of aluminum oxide thereover, the remainder of said surface having a layer of silicon dioxide simultaneously formed thereon; and treating said body with an etchant which attacks said cap, said alloy and said body at a comparatively faster rate than it attacks said layer of silicon dioxide, said treating step being carried out until recesses are formed in said body beneath said alloy, whereby a photomask can be visually aligned with said recesses.
Claim 2
Independent Claim
154 words
A method of fabricating a semiconductor device comprising the steps of: heating, in an ambient containing oxygen, a body of silicon having a layer of aluminum on a portion of a surface thereof to a temperature whereat said aluminum diffuses into said body and maintaining said body at said temperature for a preselected period of time, whereby said aluminum diffuses into said body and simultaneously forms an aluminum/silicon alloy on said portion of said surface, said aluminum/silicon alloy having a cap of aluminum oxide thereover, the remainder of said surface having a layer of silicon dioxide simultaneously formed thereon; and treating said body with an etchant which attacks said cap, said alloy and said body at a comparatively faster rate than it attacks said layer of silicon dioxide, said treating step being carried out until recesses are formed in said body beneath said alloy, whereby a photomask can be visually aligned with said recesses.
Claim 3
Dependent Claim
24 words
A method as claimed in claim 1 further comprising the step of: providing an ambient atmosphere during said heating step comprising nitrogen and oxygen.
Claim 4
Dependent Claim
32 words
A method as claimed in claim 2 wherein: said ambient providing step comprises providing an ambient comprising nitrogen and oxygen in a volumetric nitrogen to oxygen ratio of about 6 to 1.
Claim 5
Dependent Claim
22 words
A method as claimed in claim 2 wherein: said heating step is carried out at about 1300° C for about 20 hours.
Claim 6
Dependent Claim
20 words
A method as claimed in claim 4 further comprising the step of: changing said ambient to steam after 18 hours.
Claim 7
Dependent Claim
19 words
A method as claimed in claim 1 further comprising the step of: megasonically agitating said etchant during said treatment.
References Cited (Backward Citations)
US3560280A
Cited
US3579057A
Cited
US3685141A
Cited
US3843428A
Cited
US3886005A
Cited
US3972754A
Cited
US4021269A
Cited
US4029528A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |