Growing smooth epitaxial layers on misoriented substrates
Assignee: AT&T Inc
•
Filing: 1976-02-23
•
Granted: 1977-09-27
•
Expires: 1996-02-23
Abstract
Abstract A process for improving the smoothness of semiconductor layers grown by epitaxy is described. Smooth epitaxial layers, free of crystal terraces, are attained by misorienting the growth surface of the substrate from a major crystallographic plane by a small critical angle approximately equal to the tread-to-riser angle of terraces which would be formed if the epitaxial layer were deposited on a growth surface nominally parallel to the major plane. The critical angle is a function of both the growth temperature and the crystal composition. Specific examples for the growth of LPE AlxGa1-xAs at various growth temperatures and values of x on GaAs substrates misoriented from the (100) and (111)B major planes are given. Also described are examples of silicon layers grown by CVD on (111) substrates to measure the critical angle in the (112) direction.
Inventors
- 👤 Daniel Leon Rode
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 12:42
CPC Classifications
C; C30; C30B; C30B19/00; C30B19/12; Y; Y10; Y10S; Y10S117/00; Y10S117/901; Y10S117/902
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
63 words
A process of epitaxially depositing semiconductor material on a semiconductor substrate comprising the step of misorienting the growth surface from a crystallographic plane of the substrate by an angle approximately equal to the angle between the treads and risers of terraces which would be formed at the growth temperature if the epitaxial layer were deposited on a surface nominally parallel to said plane
Claim 2
Dependent Claim
63 words
A process of epitaxially depositing semiconductor material on a semiconductor substrate comprising the step of misorienting the growth surface from a crystallographic plane of the substrate by an angle approximately equal to the angle between the treads and risers of terraces which would be formed at the growth temperature if the epitaxial layer were deposited on a surface nominally parallel to said plane
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein said material is a Group III(a)-V(a) compound.
Claim 4
Dependent Claim
98 words
The process of claim 2 wherein said material is deposited from the liquid phase using apparatus comprising: a solution holder having a plurality of wells for carrying source solutions of Group III(a) and Group V(a) materials and a seed holder for carrying a saturation seed and said substrate both of which comprise said Group III(a)-V(a) compound, said slider being slidably positioned beneath said wells so that said saturation seen precedes said substrate under each well; and wherein said saturation seed is misoriented by an angle at least as great as the angle by which said substrate is misoriented.
Claim 5
Dependent Claim
68 words
The process of claim 2 wherein said material comprises Al x Ga 1-x As which is epitaxially deposited from the liquid phase on a GaAs substrate at growth temperatures in the range of about 730° C to 880° C and said substrate is misoriented from the (100) plane by angles in the range of about 1.1° to about 0.2° for x in the range of 0 to 0.36.
Claim 6
Dependent Claim
67 words
The process of claim 2 wherein said material comprises Al x Ga 1-x As which is epitaxially deposited from the liquid phase on a GaAs substrate at growth temperatures in the range of about 730° C to 880° C and said substrate is misoriented from the (111)B plane by angles in the range of about 1.0° to 0.5° for x in the range of 0 to 0.36.
Claim 7
Dependent Claim
58 words
The process of claim 1 wherein said material comprises silicon which is epitaxially deposited from the vapor phase on a silicon substrate at growth temperatures in the range of about 950° C to 1200° C and said substrate is misoriented from the (111) plane in the (112) direction by angles in the range of about 1.10° to 0.20°.
Claim 8
Dependent Claim
78 words
A process of epitaxially depositing a layer of semiconductor material on a growth surface of a semiconductor substrate comprising the steps of: a. deriving a critical angle defined by the tread-to-riser angle of terraces which would be formed on said layer if said material were deposited on a plane nominally parallel to a major crystallographic plane of said substrate, and b. misorienting the growth surface from said plane by approximately said critical angle before depositing said layer thereon.
Claim 9
Dependent Claim
78 words
A process of epitaxially depositing a layer of semiconductor material on a growth surface of a semiconductor substrate comprising the steps of: a. deriving a critical angle defined by the tread-to-riser angle of terraces which would be formed on said layer if said material were deposited on a plane nominally parallel to a major crystallographic plane of said substrate, and b. misorienting the growth surface from said plane by approximately said critical angle before depositing said layer thereon.
Claim 10
Dependent Claim
43 words
The process of claim 7 wherein step (a) includes epitaxially depositing a layer of said material on a growth surface of another substrate oriented along said plane, measuring the height profile of terraces thereby formed, and calculating said critical angle from said profile.
References Cited (Backward Citations)
US3325314A
Cited
US3146137A
Cited
US3379584A
Cited
US3476592A
Cited
US3471324A
Cited
US3632431A
Cited
US3920492A
Cited
US3899371A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-26 | 1981-03-28 | 1981-09-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-26 | 1985-03-28 | 1985-09-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-26 | 1989-03-28 | 1989-09-27 | $7700.00 | Window Closed / Lapsed |