Method of forming thin film resistor
Assignee: Sprague Electric Co
•
Filing: 1972-12-07
•
Granted: 1977-05-03
•
Expires: 1992-12-07
Abstract
Abstract A process is disclosed for vacuum depositing by co-sputtering a thin film nickel-chromium resistor of metastable composition. Also disclosed is a resistor made by this process, which resistor possesses a near zero temperature coefficient of resistance.
Inventors
- 👤 George A. Shirn
- 👤 William J. Pfister
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:39
CPC Classifications
C; C23; C23C; C23C14/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49099
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
86 words
A method of forming a thin resistor film comprising, depositing by co-sputtering a metastable alloy film on a substrate, said sputtering being accomplished by the simultaneous sputtering of chromium and nickel, the ratio of the sputtering rates of chromium and nickel being adjusted such that the sputtered resistor film composition is substantially 2/3 chromium and 1/3 nickel by weight, annealing said resistor film, determining the geometry of said film by a normal photo-etch process, and providing electrical contacts at distal surface regions of said resistor film.
Claim 2
Independent Claim
86 words
A method of forming a thin resistor film comprising, depositing by co-sputtering a metastable alloy film on a substrate, said sputtering being accomplished by the simultaneous sputtering of chromium and nickel, the ratio of the sputtering rates of chromium and nickel being adjusted such that the sputtered resistor film composition is substantially 2/3 chromium and 1/3 nickel by weight, annealing said resistor film, determining the geometry of said film by a normal photo-etch process, and providing electrical contacts at distal surface regions of said resistor film.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein said co-sputtering is accomplished by sputtering from two targets having different compositions.
Claim 4
Dependent Claim
38 words
The method of claim 1 wherein said substrate is comprised of a silicon body and a layer of silicon oxide covering at least a portion of said body, and said resistor film is deposited on said oxide layer.
Claim 5
Dependent Claim
40 words
The method of claim 1 wherein said contacts are formed by vacuum depositing spaced first and second metal electrodes, such that at least a portion of each of said electrodes lies in contact with a portion of said resistor film.
Claim 6
Dependent Claim
47 words
The method of claim 1 wherein the geometry of said resistor film is determined by forming by a normal process a photo resist mask having an aperture, and sputtering said resistor film onto said mask and onto said substrate through said aperture, and chemically removing said mask.
Claim 7
Dependent Claim
45 words
The method of claim 1 wherein the geometry of said resistor film is determined by forming by a normal process a photo resist mask over a portion of said resistor film, chemically etching away exposed portions of said resistor film and chemically removing said mask.
Claim 8
Dependent Claim
42 words
The method of claim 2 wherein said compositions of said two targets are chromium and an alloy composed essentially of 80% nickel and 20% chromium, respectively, said simultaneous sputtering being accomplished by alternately moving said substrate under each of said two targets.
Claim 9
Dependent Claim
30 words
The method of claim 7 wherein during each pass of said moving substrate under each of said targets, said substrate receives substantially less than one atomic layer of sputtered material.
References Cited (Backward Citations)
US3325258A
Cited
US3402073A
Cited
US3400066A
Cited
US3528906A
Cited
US3669730A
Cited
US3756847A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-02 | 1980-11-01 | 1981-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-02 | 1984-11-01 | 1985-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-02 | 1988-11-01 | 1989-05-03 | $7700.00 | Window Closed / Lapsed |