Catalysts for electroless deposition of metals on comparatively low-temperature polyolefin and polyester substrates
Assignee: TE Connectivity Corp
•
Filing: 1974-11-08
•
Granted: 1977-02-01
•
Expires: 1994-11-08
Abstract
Abstract A method for the metallization of a nonconductive surface with gold, nickel or copper whereby on a nonconductive, relatively low temperature surface (such as a polyester or a polyolefin) a thermosensitive coordination complex of palladium (or platinum) is deposited from a solvent; the complex has the general formula LmPdXn wherein L is a ligand or unsaturated organic radical, X is a halide, alkyl group or a bidentate ligand and m is an integer from 1 to 4 and n is from 0 to 3; bis-benzonitrile palladium dichloride complex is an appropriate illustration; the palladium complex is applied in a thin film from a suitable nonaqueous solution solvent such as xylene, toluene or a chlorobenzene onto the surface of the nonconductive material and that thin film is thermally decomposed, such as by an infrared irradiation; the method in the preferred embodiment can be practiced without the necessity of surface etching or similar chemical conditioning of the polyester, polyamide, polyvinyl chloride, or polyolefin substrate prior to the catalytic coating; circuit element intermediates of said substrates are also disclosed.
Inventors
- 👤 Charles Roscoe Brummett
- 👤 Ray Ned Shaak
- 👤 Daniel Marshall Andrews
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:38
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/28; C23C18/30
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
215 words
A method for the deposition of a copper, nickel cobalt, or gold as metal onto an inert substrate for said metal said substrate being selected from the group consisting of polyester, polyamides, polyvinylchloride, polyethylene, polypropylene, copolymers of either polyolefin, and poly (1a) olefins in the homologous series of the polyethylene and polypropylene, from an electroless bath containing said metal, said method comprising the steps of: degreasing said substrate; applying to said substrate a thin film of a thermally decomposable complex of palladium or platinum having the formulae LmPdXn, or LmPtXn wherein L is a ligand or an unsaturated organic group; Pd or Pt is palladium or platinum metal; X is a halide, an alkyl group or a bidentate ligand; and m is from 1 to 4 and n is from 0 to 3 exposing said substrate to which said complex has been applied to heat at a temperature of less than a temperature at which the substrate loses its dimensional stability, to effect decomposition of said complex and to create a residue on said substrate catalytic to a copper, nickel, cobalt or gold metal in an electroless bath solution; and depositing a copper, nickel, cobalt or gold metal from said electroless bath on said substrate in an area rendered catalytic by decomposition of said complex.
Claim 2
Independent Claim
215 words
A method for the deposition of a copper, nickel cobalt, or gold as metal onto an inert substrate for said metal said substrate being selected from the group consisting of polyester, polyamides, polyvinylchloride, polyethylene, polypropylene, copolymers of either polyolefin, and poly (1a) olefins in the homologous series of the polyethylene and polypropylene, from an electroless bath containing said metal, said method comprising the steps of: degreasing said substrate; applying to said substrate a thin film of a thermally decomposable complex of palladium or platinum having the formulae LmPdXn, or LmPtXn wherein L is a ligand or an unsaturated organic group; Pd or Pt is palladium or platinum metal; X is a halide, an alkyl group or a bidentate ligand; and m is from 1 to 4 and n is from 0 to 3 exposing said substrate to which said complex has been applied to heat at a temperature of less than a temperature at which the substrate loses its dimensional stability, to effect decomposition of said complex and to create a residue on said substrate catalytic to a copper, nickel, cobalt or gold metal in an electroless bath solution; and depositing a copper, nickel, cobalt or gold metal from said electroless bath on said substrate in an area rendered catalytic by decomposition of said complex.
Claim 3
Dependent Claim
44 words
The process as defined in claim 1 wherein said substrate is selected from the group consisting of polyesters useful as dielectrics in electrical circuit applications, polyethylene, polypropylene, copolymers of either polyolefin, and poly (α) olefins in the homologous series of the polyethylene and polypropylene.
Claim 4
Dependent Claim
13 words
The process as defined in claim 1 wherein said substrate is polyethylene terephthalate.
Claim 5
Dependent Claim
49 words
The process as defined in claim 1 wherein said substrate is selected from the group consisting of polyethylene terephthalate and polypropylene and is exposed with said complex to heat at a temperature of between about 50° C and about 150° C, said complex decomposing at or below said temperature.
Claim 6
Dependent Claim
36 words
The process as defined in claim 1 wherein said substrate is polyethylene and is exposed with said complex to heat at a temperature up to about 98° C, said complex decomposing at or below said temperature.
Claim 7
Dependent Claim
28 words
The process as defined in claim 1, wherein the palladium complex is selected from the group consisting of bis-benzonitrile palladium dichloride, 1,3-butadiene palladium dichloride, and bis-acetonitrile palladium dichloride.
Claim 8
Dependent Claim
53 words
The process as defined in claim 1, wherein the said substrate, after application of said complex decomposition of same and immersion in an electroless bath, is masked and additionally an electroless metal deposit is made and, thereafter the additional deposit protected, said mask removed and said substrate back-etched to obtain a circuit element.
Claim 9
Dependent Claim
14 words
The process as defined in claim 1 and wherein the substrate is a polyamide.
Claim 10
Dependent Claim
13 words
The process as defined in claim 1 and wherein the substrate is polyvinylchloride.
Claim 11
Dependent Claim
38 words
The process as defined in claim 2, wherein the said substrate, after application of said complex and electroless metal in a nickel, cobalt, copper or gold electroless bath solution, is masked and exposed to further additive electroless deposition.
Claim 12
Dependent Claim
32 words
The process as defined in claim 2 and wherein the substrate is degreased before applying said complex to same by a solvent which wets and slightly swells the surface of said substrate.
Claim 13
Dependent Claim
31 words
The process as defined in claim 7 wherein said substrate after said further additive deposition is stripped of said mask and back-etched in areas wherein said electroless metal has been deposited.
Claim 14
Dependent Claim
28 words
The process as defined in claim 3, wherein the palladium complex is selected from the group consisting of bis-benzonitrile palladium dichloride, 1,3-butadiene palladium dichloride, and bis-acetonitrile palladium dichloride.
Claim 15
Dependent Claim
28 words
The process as defined in claim 4, wherein the palladium complex is selected from the group consisting of bis-benzonitrile palladium dichloride, 1,3-butadiene palladium dichloride, and bis-acetonitrile palladium dichloride.
Claim 16
Dependent Claim
28 words
The process as defined in claim 5 wherein the palladium complex is chosen from the group consisting of bis-benzonitrile palladium dichloride, 1,3-butadiene palladium dichloride, and bis-acetonitrile palladium dichloride.
References Cited (Backward Citations)
US3212918A
Cited
US3414427A
Cited
US3370973A
Cited
US3457638A
Cited
US3741800A
Cited
US3562118A
Cited
US3558443A
Cited
US3544432A
Cited
US3666549A
Cited
US3698940A
Cited
US3674550A
Cited
US3684534A
Cited
US3704156A
Cited
US3745095A
Cited
US3808028A
Cited
US3799816A
Cited
US3937857A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-01 | 1980-08-02 | 1981-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-01 | 1984-08-02 | 1985-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-01 | 1988-08-02 | 1989-02-01 | $7700.00 | Window Closed / Lapsed |