Process for forming heteroepitaxial structure
Assignee: Harris Corp
•
Filing: 1975-12-15
•
Granted: 1976-10-12
•
Expires: 1995-12-15
Abstract
Abstract A process for producing light emitting diodes is disclosed. In the process a major planar surface of a single crystal silicon wafer is modified to acceptably match the crystallographic lattice constant of a preselected electroluminescent single crystal semiconductor, such as gallium phosphide. The preselected electroluminescent semiconductor material is then epitaxially deposited in single crystal form on the modified surface of the silicon wafer, a step which is not feasible without the modification of the silicon wafer surface. Preferably, the modification is achieved by epitaxially depositing a thin layer of semiconductor material whose lattice structure offers a substantially smaller disparity with the structure of the electroluminescent material than the existing disparity between the silicon wafer and the electroluminescent material.
Inventors
- 👤 Donald R. Mason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:23
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/81; H10H20/822; H10H20/826; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/32; H10P14/3202; H10P14/3204; H10P14/3211; H10P14/3242; H10P14/3244; H10P14/3254; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; H10P14/3438; H10P14/3441; H10P14/3446
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
117 words
A process for preparing a single crystal silicon substrate for the production of light emitting diodes comprising: epitaxially depositing a thin layer of single crystal silicon-germanium semiconductor material on a major surface of said substrate to form a graded layer having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a second surface; and epitaxially depositing said preselected electroluminescent semiconductor material in single crystal form on said second surface of said graded layer.
Claim 2
Dependent Claim
117 words
A process for preparing a single crystal silicon substrate for the production of light emitting diodes comprising: epitaxially depositing a thin layer of single crystal silicon-germanium semiconductor material on a major surface of said substrate to form a graded layer having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a second surface; and epitaxially depositing said preselected electroluminescent semiconductor material in single crystal form on said second surface of said graded layer.
Claim 3
Dependent Claim
43 words
The process according to claim 1 wherein said thin layer is an alloy of silicon and germanium wherein the germanium concentration of said silicon-germanium alloy is zero at said major surface of said substrate and under 10 mole percent at said second surface.
Claim 4
Dependent Claim
22 words
The process according to claim 1, wherein said electroluminescent semiconductor material is selected from the group consisting of GaP, GaAs, and GaAsP.
Claim 5
Independent Claim
124 words
A method of preparing a single crystal silicon substrate for fabrication of a monolithic semiconductor display comprising: epitaxially depositing on a plurality of selected regions of a surface of said silicon substrate a thin layer of a silicon-germanium alloy to form a graded layer on each selected region having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said silicon substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a asecond surface; and thereafter epitaxially depositing a layer of said preselected electroluminescent semiconductor material on each of said thin layers.
Claim 6
Independent Claim
124 words
A method of preparing a single crystal silicon substrate for fabrication of a monolithic semiconductor display comprising: epitaxially depositing on a plurality of selected regions of a surface of said silicon substrate a thin layer of a silicon-germanium alloy to form a graded layer on each selected region having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said silicon substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a asecond surface; and thereafter epitaxially depositing a layer of said preselected electroluminescent semiconductor material on each of said thin layers.
Claim 7
Dependent Claim
23 words
The method according to claim 4, wherein said layer of electroluminescent material is selected from the group consisting of GaP, GaAs, and GaAsP.
Claim 8
Dependent Claim
19 words
The method of claim 4 wherein said silicon germanium alloy has a maximum germanium concentration under 10 mole percent.
Claim 9
Dependent Claim
31 words
The method according to claim 6, wherein said silicon-germanium alloy has a concentration of germanium that increases from zero to 8 percent from said silicon substrate surface to said second surface.
Claim 10
Dependent Claim
16 words
The method according to claim 7, wherein said electroluminescent semiconductor material is a Group III-V compound.
Claim 11
Dependent Claim
133 words
A process for producing light emitting diodes on a single crystal silicon substrate comprising: epitaxially depositing a thin layer of single crystal silicon-germanium semiconductor material on a major surface of said silicon substrate to form a graded layer having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said silicon substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a second surface; epitaxially depositing said preselected electrolominescent semiconductor material in single crystal form on said second surface of said graded layer; and forming a p-n junction in said deposited electrolominescent semiconductor material for operation as a light emitting diode.
Claim 12
Dependent Claim
133 words
A process for producing light emitting diodes on a single crystal silicon substrate comprising: epitaxially depositing a thin layer of single crystal silicon-germanium semiconductor material on a major surface of said silicon substrate to form a graded layer having a crystal lattice constant determined by a substantially zero germanium concentration for substantially matching the crystal lattice constant of said silicon substrate at the boundary therebetween and having a crystal lattice constant determined by the maximum germanium concentration for substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at a second surface; epitaxially depositing said preselected electrolominescent semiconductor material in single crystal form on said second surface of said graded layer; and forming a p-n junction in said deposited electrolominescent semiconductor material for operation as a light emitting diode.
Claim 13
Dependent Claim
15 words
The process of claim 9 wherein said electroluminescent semiconductor material is a Group III-V compound.
Claim 14
Dependent Claim
19 words
The process of claim 9 wherein said thin layer has a maximum germanium concentration of under 10 mole percent.
Claim 15
Independent Claim
136 words
A method of fabricating a monolithic semiconductor display in a single crystal silicon substrate comprising: epitaxially depositing on a plurality of selected regions of a surface of said silicon substrate a thin layer of a silicon-germanium alloy to form a graded layer on each selected region having a substantially zero germanium concentration at the boundary with the silicon substrate and having the maximum germanium concentration at a second surface to provide a crystal lattice constant substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at said second surface; thereafter epitaxially depositing a layer of said preselected electroluminescent semiconductor material on each of said thin layers; and forming a planar p-n junction in each of said layers of electroluminescent semiconductor material to form a plurality of light emitting diodes for said display.
Claim 16
Independent Claim
136 words
A method of fabricating a monolithic semiconductor display in a single crystal silicon substrate comprising: epitaxially depositing on a plurality of selected regions of a surface of said silicon substrate a thin layer of a silicon-germanium alloy to form a graded layer on each selected region having a substantially zero germanium concentration at the boundary with the silicon substrate and having the maximum germanium concentration at a second surface to provide a crystal lattice constant substantially matching the crystal lattice constant of a preselected electroluminescent single crystal semiconductor material at said second surface; thereafter epitaxially depositing a layer of said preselected electroluminescent semiconductor material on each of said thin layers; and forming a planar p-n junction in each of said layers of electroluminescent semiconductor material to form a plurality of light emitting diodes for said display.
Claim 17
Dependent Claim
21 words
The method of claim 12 wherein said electroluminescent semiconductor material is selected from the group consisting of GaP, GaAs, and GaAsP.
Claim 18
Dependent Claim
19 words
The method of claim 12 wherein said thin layer has a maximum germanium concentration of under 10 mole percent.
References Cited (Backward Citations)
US3341376A
Cited
US3275906A
Cited
US3309553A
Cited
US3433686A
Cited
US3433684A
Cited
US3473978A
Cited
GB1242310A
Cited
US3615855A
Cited
US3699401A
Cited
US3725749A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-12 | 1980-04-12 | 1980-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-12 | 1984-04-12 | 1984-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-12 | 1988-04-12 | 1988-10-12 | $7700.00 | Window Closed / Lapsed |