Patent US3960618A successfully refreshed from Google Patents.
US3960618A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Epitaxial growth process for compound semiconductor crystals in liquid phase
Assignee: Hitachi Ltd
•
Filing: 1975-03-25
•
Granted: 1976-06-01
•
Expires: 1995-03-25
Abstract
Abstract In an epitaxial growth process for compound semiconductor crystals in a liquid phase, a substrate crystal is brought into contact with an etching solution containing as solute a predetermined amount of at least one constituent of the substrate crystal, which is smaller than that of a saturated solution, after heating them at a temperature for crystal growth. The substrate crystal is kept in contact with the solution during a period of time sufficient to remove a surface portion of the substrate crystal. Then the substrate crystal is brought into contact with a solution for crystal growth containing a substance to be grown as solute and a crystal of the substance is grown epitaxially on an exposed clean surface of the substrate crystal.
Inventors
- 👤 Masao Kawamura
- 👤 Kazuhiro Ito
- 👤 Makoto Morioka
- 👤 Yuichi Ono
- 👤 Sachio Ishioka
- 👤 Kazuhiro Kurata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:20
CPC Classifications
B; B60; B60C; B60C9/00; B60C9/18; B60C9/20; B60C9/2003; B60C9/2009; C; C30; C30B; C30B19/00; C30B19/12; H; H10; H10P; H10P14/00; H10P14/20; H10P14/26; H10P14/263; H10P14/265; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2909; H10P14/2911; H10P14/2926; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3421; H10P14/3438; H10P14/3441; H10P14/3442; H10P14/3444; H10P14/3446; Y; Y10; Y10S; Y10S438/00; Y10S438/955
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
135 words
An epitaxial growth process for compound semiconductor crystals of III-V and II-VI compounds in liquid phase comprising: preparing a substrate crystal of a compound semiconductor, preparing an etching solution containing the constituent elements of said compound semiconductor, which is unsaturated with respect to the solute at a temperature at the beginning of crystal growth, preparing a solution for crystal growth containing a III-V or II-VI compound to be grown, heating said substrate crystal, said etching solution and said solution for crystal growth to the temperature at the beginning of crystal growth, bringing said substrate in contact with said etching solution, bringing said substrate in contact with said solution for crystal growth just after having removed said substrate crystal from said etching solution, and growing epitaxially a crystal of said compound semiconductor on said substrate crystal.
Claim 2
Dependent Claim
135 words
An epitaxial growth process for compound semiconductor crystals of III-V and II-VI compounds in liquid phase comprising: preparing a substrate crystal of a compound semiconductor, preparing an etching solution containing the constituent elements of said compound semiconductor, which is unsaturated with respect to the solute at a temperature at the beginning of crystal growth, preparing a solution for crystal growth containing a III-V or II-VI compound to be grown, heating said substrate crystal, said etching solution and said solution for crystal growth to the temperature at the beginning of crystal growth, bringing said substrate in contact with said etching solution, bringing said substrate in contact with said solution for crystal growth just after having removed said substrate crystal from said etching solution, and growing epitaxially a crystal of said compound semiconductor on said substrate crystal.
Claim 3
Dependent Claim
43 words
An epitaxial growth process for compound semiconductor crystals in liquid phase according to claim 1, wherein a speed of dissolution of said substrate crystal by said etching solution is controlled by controlling a degree of saturation of the solute within said etching solution.
Claim 4
Dependent Claim
76 words
An epitaxial growth process for compound semiconductor crystals in liquid phase according to claim 2, wherein said substrate crystal is made of one selected from the group consisting of gallium phosphide and gallium arsenide, the solvent of said etching solution being gallium, said degree of saturation represented by the ratio of an amount of solute in said etching solution with respect to an amount of solute in a saturated solution being comprised between 60 and 98%.
Claim 5
Dependent Claim
82 words
An epitaxial growth process for compound semiconductor crystals in liquid phase according to claim 2, wherein said substrate crystal is made of one selected from the group consisting of gallium aluminum arsenide and gallium aluminum phosphide, the solvent of said etching solution being gallium, the amount of aluminum with respect to that of gallium by weight being comprised between 0.25 and 1.25%, said degree of saturation with respect to the other two elements forming the solute being comprised between 30 and 60%.
Claim 6
Dependent Claim
32 words
An epitaxial growth process for compound semiconductor crystals in liquid phase according to claim 1, wherein both said substrate crystal and said compound semiconductor to be grown are a III-V compound semiconductor.
References Cited (Backward Citations)
US2944321A
Cited
US3192082A
Cited
US3530011A
Cited
US3697336A
Cited
US3677836A
Cited
US3692593A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |