Gallium nitride-on-silicon interface using multiple aluminum compound buffer layers
Assignee: Sharp Corp
•
Filing: 2007-07-06
•
Granted: 2009-10-06
•
Expires: 2027-07-06
Abstract
Abstract A thermal expansion interface between silicon (Si) and gallium nitride (GaN) films using multiple buffer layers of aluminum compounds has been provided, along with an associated fabrication method. The method provides a ( 111 ) Si substrate and deposits a first layer of AlN overlying the substrate by heating the substrate to a relatively high temperature of 1000 to 1200° C. A second layer of AlN is deposited overlying the first layer of AlN at a lower temperature of 500 to 800° C. A third layer of AlN is deposited overlying the second layer of AlN by heating the substrate to the higher temperature range. Then, a grading Al 1-X Ga X N layer is formed overlying the third layer of AlN, where 0<X<1, followed by a fixed composition Al 1-X Ga X N layer overlying the first grading Al 1-X Ga X N layer. An epitaxial GaN layer can then be grown overlying the fixed composition Al 1-X Ga X N layer.
Inventors
- 👤 Tingkai Li
- 👤 Douglas J. Tweet
- 👤 Jer-shen Maa
- 👤 Sheng Teng Hsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:49
CPC Classifications
H; H10; H10D; H10D62/00; H10D62/80; H10D62/81; H10D62/815; H10D62/8161; H10D62/8162; H10D62/8164; H10D62/82; H10D62/824; H10D62/85; H10D62/8503; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3216; H10P14/3242; H10P14/3244; H10P14/3251; H10P14/3254; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3416; H10P14/27; H10P14/276
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
184 words
A method for forming a thermal expansion interface between silicon (Si) and gallium nitride (GaN) films using multiple buffer layers of aluminum compounds, the method comprising: providing a ( 111 ) Si substrate; depositing a first layer of AIN overlying the substrate, heating the substrate to a temperature within a first range; depositing a second layer of AlN directly overlying and in contact with the first layer of AlN, hearing the substrate to a temperature within a second range, lower than the first range; depositing a third layer of AlN directly overlying and in contact with the second layer of AlN, heating the substrate to a temperature within the first range; forming a first grading Al 1-X Ga X N layer directly overlying and in contact with the third layer of AlN, where 0<X<1; forming a first fixed composition Al 1-X Ga X N layer directly overlying and in contact with the first grading Al 1-X Ga X N layer, where 0<X<1; and, growing a first epitaxial GaN layer directly overlying and in contact with the fixed composition Al 1-X Ga X N layer.
Claim 2
Independent Claim
184 words
A method for forming a thermal expansion interface between silicon (Si) and gallium nitride (GaN) films using multiple buffer layers of aluminum compounds, the method comprising: providing a ( 111 ) Si substrate; depositing a first layer of AIN overlying the substrate, heating the substrate to a temperature within a first range; depositing a second layer of AlN directly overlying and in contact with the first layer of AlN, hearing the substrate to a temperature within a second range, lower than the first range; depositing a third layer of AlN directly overlying and in contact with the second layer of AlN, heating the substrate to a temperature within the first range; forming a first grading Al 1-X Ga X N layer directly overlying and in contact with the third layer of AlN, where 0<X<1; forming a first fixed composition Al 1-X Ga X N layer directly overlying and in contact with the first grading Al 1-X Ga X N layer, where 0<X<1; and, growing a first epitaxial GaN layer directly overlying and in contact with the fixed composition Al 1-X Ga X N layer.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein depositing the first and third AlN layers includes depositing AlN at a temperature within a first range of 1000 to 1200° C.
Claim 4
Dependent Claim
37 words
The method of claim 2 wherein forming the first grading and first fixed composition Al 1-X Ga X N layers includes depositing each Al 1-X Ga X N layer at a substrate temperature within the first range.
Claim 5
Dependent Claim
25 words
The method of claim 2 wherein growing the first epitaxial GaN layer includes depositing the GaN layer at a substrate temperature within the first range.
Claim 6
Dependent Claim
26 words
The method of claim 1 wherein depositing the second AlN layer includes depositing AlN at a temperature within a second range of 500 to 800° C.
Claim 7
Dependent Claim
43 words
The method of claim 1 wherein depositing the first, second, and third AlN layers includes introducing Al (III) and N (IV) precursors in a chemical vapor deposition (CVD) process having a III to IV mole ratio in a range of 500 to 4000.
Claim 8
Dependent Claim
30 words
The method of claim 1 wherein depositing the first and second AlN layers includes depositing each AlN layer to a thickness in a range of 10 to 50 nanometers (nm).
Claim 9
Dependent Claim
25 words
The method of claim 1 wherein depositing the third AlN layer includes depositing AlN to a thickness in a range of 100 to 500 nm.
Claim 10
Dependent Claim
40 words
The method of claim 1 wherein forming the first grading and first fixed composition Al 1-X Ga X N layers includes forming each Al 1-X Ga X N layer having a thickness in a range of 10 to 500 nm.
Claim 11
Dependent Claim
58 words
The method of claim 1 wherein forming the first grading and first fixed composition Al 1-X Ga X N layers includes forming each Al 1-X Ga X N layer by introducing Ga (III) and Al (III), and N (IV) precursors in a CVD process having a III to IV mole ratio in a range of 500 to 4000.
Claim 12
Dependent Claim
28 words
The method of claim 1 wherein growing the first epitaxial GaN layer includes forming a GaN layer having a thickness in a range of 500 to 3000 nm.
Claim 13
Dependent Claim
43 words
The method of claim 1 wherein growing the first epitaxial GaN layer includes forming a GaN layer by introducing Ga (III) and N (IV) precursors in a CVD process having a III to IV mole ratio in a range of 500 to 4000.
Claim 14
Dependent Claim
69 words
The method of claim 1 further comprising: subsequent to growing the first epitaxial GaN layer, forming a second grading Al 1-X Ga X N layer overlying the first epitaxial GaN layer, forming a second fixed composition Al 1-X Ga X N layer overlying the second grading Al 1-X Ga X N layer, and growing a second epitaxial GaN layer overlying the fixed composition Al 1-X Ga X N layer.
Claim 15
Dependent Claim
46 words
The method of claim 13 further comprising: forming a patterned layer overlying the second epitaxial GaN layer, selected from a group consisting of anodized aluminum oxide (AAO) and block polymer; and, using a lateral nanoheteroepitaxy overgrowth (LNEO) process, growing a GaN layer overlying the patterned layer.
Claim 16
Dependent Claim
39 words
The method of claim 14 wherein forming the patterned layer of AAO includes using a film material selected from a group consisting of AlN, an AlN/grading AlGaN (Al 1-x Ga x N (0<X<1)) stack, an AlN/AlGaN/GaN stack, and Al.
Claim 17
Dependent Claim
62 words
The method of claim 14 wherein forming the patterned layer includes forming a layer having a thickness in a range of 10 to 500 nm, and pattern openings having a diameter in a range between 5 and 100 nm, a depth extending through the patterned layer thickness, and a distance between openings in a range between 100 nm and 2 micrometers (μm).
References Cited (Backward Citations)
US4865830A
Cited
US5679965A
Cited
US6391748B1
Cited
US6649287B2
Cited
US6818061B2
Cited
US20050067935A1
Cited
US20050142876A1
Cited
US20060073621A1
Cited
US20060244011A1
Cited
US20060270087A1
Cited
US20060286782A1
Cited
US20070197004A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2012-10-05 | 2013-04-06 | 2013-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2016-10-05 | 2017-04-06 | 2017-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2020-10-05 | 2021-04-06 | 2021-10-06 | $7700.00 | Window Closed / Lapsed |