Method of manufacturing an aluminum oxide film in a semiconductor device
Assignee: SK Hynix Inc
•
Filing: 2001-06-15
•
Granted: 2002-07-30
•
Expires: 2021-06-15
Abstract
Abstract In a method of manufacturing an aluminum oxide film using atomic layer deposition, alcohol is delivered as an oxygen source instead of water vapor into a reactor via a different delivery line from an aluminum source. Thus, the disclosed method can prevent degradation of an aluminum oxide thin film in uniform fashion by a chemical vapor deposition method that is parasitically generated. Also, an activation gas is delivered into the reactor at about the same time an aluminum source and an alcoholic gas is delivered. Therefore, the disclosed method can prevent reduction in the deposition rate and also prohibit degradation in an electrical property by impurity.
Inventors
- 👤 Chan Lim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:08
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/455; C23C16/45523; C23C16/45525; C23C16/45553; C23C16/22; C23C16/30; C23C16/40; C23C16/403; C23C16/45527; C23C16/45534; H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6339; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69391
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
86 words
A method of manufacturing an aluminum oxide film in a semiconductor device, comprising the sequential steps of: (a) simultaneously delivering an aluminum source and an activation gas into a reactor in which a wafer is mounted, via different delivery lines; (b) removing unreacted aluminum source from the reactor; (c) substantially simultaneously delivering a reactive alcohol gas and an activation gas into the reactor, via a same delivery line; (d) removing unreacted alcohol gas from the reactor; and (e) repeating steps (a) through (d) at least once.
Claim 2
Independent Claim
86 words
A method of manufacturing an aluminum oxide film in a semiconductor device, comprising the sequential steps of: (a) simultaneously delivering an aluminum source and an activation gas into a reactor in which a wafer is mounted, via different delivery lines; (b) removing unreacted aluminum source from the reactor; (c) substantially simultaneously delivering a reactive alcohol gas and an activation gas into the reactor, via a same delivery line; (d) removing unreacted alcohol gas from the reactor; and (e) repeating steps (a) through (d) at least once.
Claim 3
Dependent Claim
43 words
The method according to claim 1 , wherein the pressure of the reactor is within the range of about 50 mTorr to about 300 mTorr and the temperature of the wafer is within the range of about 200° C. to about 450° C.
Claim 4
Dependent Claim
34 words
The method according to claim 1 , wherein the aluminum source is delivered into the reactor within about 0.1 second to about 3 seconds using either trimethyl aluminum (TMA) or modified trimethyl aluminum (MTMA).
Claim 5
Dependent Claim
52 words
The method according to claim 1 , wherein the aluminum source comprises MTMA, the temperature of an aluminum source container is in the range of about 50° C. to about 100° C., and the temperature of an aluminum delivery line is in the range between about 70° C. and about 180° C.
Claim 6
Dependent Claim
39 words
The method of claim 1 , wherein the activation gas includes ammonia gas and is delivered into the reactor for about 0.1 second to about 3 seconds at a flow rate of about 20 sccm to about 1000 sccm.
Claim 7
Dependent Claim
47 words
The method of claim 1 , wherein the alcohol is selected from the group consisting of methanol (CH 3 OH), ethanol (C 2 H 5 OH), and isopropanol (CH 3 CH(OH)CH 3 ) and is delivered into the reactor for about 0.1 second to about 3 seconds.
References Cited (Backward Citations)
US5923056A
Cited
US6287965B1
Cited
US6270572B1
Cited
US6305314B1
Cited
US6124158A
Cited
US6203613B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2005-07-29 | 2006-01-28 | 2006-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2009-07-29 | 2010-01-28 | 2010-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2013-07-29 | 2014-01-28 | 2014-07-30 | $7700.00 | Window Closed / Lapsed |