Method of reducing carbon contamination of a thin dielectric film by using gaseous organic precursors, inert gas, and ozone to react with carbon contaminants
Assignee: Nokia of America Corp
•
Filing: 1999-06-08
•
Granted: 2000-09-26
•
Expires: 2019-06-08
Abstract
Abstract A process is provided for the formation of a thin film of gate dielectric or similar material on a silicon semiconductor substrate from an organic precursor by atomic layer epitaxy, wherein the organic precursor is introduced to react with the treated surface to form a bonded monolayer of reactive species. A second reactant is introduced to react with the surface to form the desired dielectric. After each step in the cycle, the reaction chamber is purged with an inert gas to prevent reactions except on the surface. The cycle is repeated tens to hundreds of times to achieve a desired final film thickness. No less frequently than every third cycle, the film undergoes a discrete treatment step wherein ozone is introduced into the chamber to oxidize carbon contaminants therein to form volatile products which are removed from the reaction chamber by purging with the inert gas. In a preferred embodiment where the substrate is silicon or polysilicon, a sub-monolayer of a protection material is formed by boding to silicon sites on the surface before the deposition of dielectric is begun. A preferred dielectric is gate aluminum oxide that is deposited using trimethyl aluminum as a precursor.
Inventors
- 👤 Mindaugas F. Dautartas
- 👤 Lalita Manchanda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:42
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/0134; H10D64/01342; H10D64/01344; H10D64/031; H10D64/035; H10D64/60; H10D64/66; H10D64/68; H10D64/691; H10D64/693; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6502; H10P14/6506; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6339; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69391
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
183 words
A process for forming a thin film of dielectric on a semiconductor substrate, said film having reduced carbon contamination, comprising heating the substrate under an inert atmosphere in a suitable reaction chamber to a temperature such that a selected gaseous organic precursor for said dielectric will react to form a bonded reactant on the surface, and carrying out multiple deposition cycles at said temperature to form said thin dielectric film, each deposition cycle comprising: a) introducing the gaseous organic precursor into the reaction chamber so that it reacts to form said bonded reactant on the surface; b) purging the reaction chamber with an inert gas; c) introducing a second gaseous reactant into the chamber which reacts with said bonded reactant to form said dielectric film; and d) purging the reaction chamber with the inert gas, wherein no less frequently than every third cycle, introducing ozone into the reaction chamber following step d) to react with carbon contaminants in the film thereby forming gaseous products and purging the reaction chamber with said inert gas to remove such products prior to initiating the next cycle.
Claim 2
Dependent Claim
183 words
A process for forming a thin film of dielectric on a semiconductor substrate, said film having reduced carbon contamination, comprising heating the substrate under an inert atmosphere in a suitable reaction chamber to a temperature such that a selected gaseous organic precursor for said dielectric will react to form a bonded reactant on the surface, and carrying out multiple deposition cycles at said temperature to form said thin dielectric film, each deposition cycle comprising: a) introducing the gaseous organic precursor into the reaction chamber so that it reacts to form said bonded reactant on the surface; b) purging the reaction chamber with an inert gas; c) introducing a second gaseous reactant into the chamber which reacts with said bonded reactant to form said dielectric film; and d) purging the reaction chamber with the inert gas, wherein no less frequently than every third cycle, introducing ozone into the reaction chamber following step d) to react with carbon contaminants in the film thereby forming gaseous products and purging the reaction chamber with said inert gas to remove such products prior to initiating the next cycle.
Claim 3
Dependent Claim
22 words
A process in accordance with claim 1, wherein the substrate is silicon and the film is a gate dielectric of aluminum oxide.
Claim 4
Dependent Claim
23 words
A process in accordance with claim 2, wherein the gaseous organic precursor is trimethyl aluminum and the second gaseous reactant is water vapor.
Claim 5
Dependent Claim
22 words
A process in accordance with claim 3, wherein the substrate is initially heated to a temperature from about 190° to 300° C.
Claim 6
Dependent Claim
20 words
A process in accordance with claim 4, wherein the substrate is initially heated to a temperature of about 190° C.
Claim 7
Dependent Claim
21 words
A process in accordance with claim 1, wherein ozone is introduced into the reaction chamber after every one to three cycles.
Claim 8
Dependent Claim
18 words
A process in accordance with claim 6, wherein ozone is introduced into the reaction chamber after every cycle.
Claim 9
Dependent Claim
13 words
A process in accordance with claim 1, wherein the inert gas is nitrogen.
Claim 10
Dependent Claim
49 words
A process in accordance with claim 1, wherein prior to step a) of said first cycle, the surface of the substrate is pretreated by introducing ozone into the reaction chamber to form gaseous products from contaminants on the substrate surface and the chamber is purged with said inert gas.
Claim 11
Dependent Claim
34 words
A process in accordance with claim 1, wherein the substrate surface does not contain hydroxyl groups and, prior to step a) of said first cycle, the surface is treated to form hydroxyl groups thereon.
Claim 12
Dependent Claim
19 words
A process in accordance with claim 10, wherein the surface is treated with water vapor at the reaction temperature.
Claim 13
Dependent Claim
23 words
A process in accordance with claim 10, wherein the surface of the substrate is treated prior to being admitted to the reaction chamber.
Claim 14
Dependent Claim
25 words
A process in accordance with claim 12, wherein the substrate is silicon and the surface is treated with hydrogen peroxide to form hydroxyl groups thereon.
Claim 15
Dependent Claim
54 words
A process in accordance with claim 1, wherein after each of said ozone treatment and purge with inert gas, the surface of the substrate is treated with water vapor at the reaction temperature to form hydroxyl groups thereon and the reaction chamber thereafter purged with said inert gas prior to initiating the next cycle.
Claim 16
Dependent Claim
42 words
A process in accordance with claim 1, wherein the substrate is silicon or polysilicon and, prior to step a), the reactive silicon sites on the surface are bonded to a protection material such that a sub-monolayer of protective material is formed thereon.
Claim 17
Dependent Claim
25 words
A process in accordance with claim 15 where said protection material is selected from the group consisting of silicon dioxide, silicon oxynitride and silicon nitride.
Claim 18
Dependent Claim
20 words
A process in accordance with claim 15, wherein said sub-monolayer is formed by atomic layer epitaxy from an inorganic precursor.
Claim 19
Dependent Claim
23 words
A process in accordance with claim 15, said protection material is silicon dioxide and said sub-monolayer is formed by thermo-oxidation of the substrate.
Claim 20
Dependent Claim
196 words
A process for forming a thin film of aluminum oxide gate dielectric on a semiconductor substrate, said film having reduced carbon contamination, comprising heating the substrate under an inert atmosphere in a suitable reaction chamber to a temperature such that a trimethyl aluminum will react to form a bonded reactant on the surface thereof, treating the surface of the substrate with water vapor to form hydroxyl groups thereon and carrying out multiple deposition cycles at said temperature to form said thin gate dielectric film, each deposition cycle comprising: a) introducing trimethyl aluminum into the reaction chamber so that it reacts to form said bonded reactant on the surface; b) purging the reaction chamber with an inert gas; c) introducing water vapor into the chamber which reacts with said bonded reactant to form said aluminum oxide gate dielectric film; and d) purging the reaction chamber with the inert gas, wherein no less frequently than every third cycle, introducing ozone into the reaction chamber following step d) to react with carbon contaminants in the film thereby forming gaseous products and purging the reaction chamber with said inert gas to remove such products prior to initiating the next cycle.
Claim 21
Dependent Claim
196 words
A process for forming a thin film of aluminum oxide gate dielectric on a semiconductor substrate, said film having reduced carbon contamination, comprising heating the substrate under an inert atmosphere in a suitable reaction chamber to a temperature such that a trimethyl aluminum will react to form a bonded reactant on the surface thereof, treating the surface of the substrate with water vapor to form hydroxyl groups thereon and carrying out multiple deposition cycles at said temperature to form said thin gate dielectric film, each deposition cycle comprising: a) introducing trimethyl aluminum into the reaction chamber so that it reacts to form said bonded reactant on the surface; b) purging the reaction chamber with an inert gas; c) introducing water vapor into the chamber which reacts with said bonded reactant to form said aluminum oxide gate dielectric film; and d) purging the reaction chamber with the inert gas, wherein no less frequently than every third cycle, introducing ozone into the reaction chamber following step d) to react with carbon contaminants in the film thereby forming gaseous products and purging the reaction chamber with said inert gas to remove such products prior to initiating the next cycle.
Claim 22
Dependent Claim
51 words
A process in accordance with claim 19 further wherein, prior treating the surface of the substrate to form hydroxyl groups thereon, the surface is pretreated by introducing ozone into the reaction chamber to form gaseous products from contaminants on the substrate surface and the chamber is purged with said inert gas.
Claim 23
Dependent Claim
48 words
A process in accordance with claim 20, wherein the substrate is silicon or polysilicon and, prior to treating the surface to form hydroxyl groups thereon, the reactive silicon sites on the surface are bonded to a protection material such that a sub-monolayer of protective material is formed thereon.
Claim 24
Dependent Claim
54 words
A process in accordance with claim 19, wherein after each of said ozone treatment and purge with inert gas, the surface of the substrate is treated with water vapor at the reaction temperature to form hydroxyl groups thereon and the reaction chamber thereafter purged with said inert gas prior to initiating the next cycle.
Claim 25
Dependent Claim
16 words
A semiconductor substrate having formed thereon a film of dielectric by the process of claim 1.
Claim 26
Dependent Claim
20 words
A silicon semiconductor substrate having formed thereon a film of aluminum oxide gate dielectric by the process of claim 19.
Claim 27
Dependent Claim
20 words
A silicon semiconductor substrate having formed thereon a film of aluminum oxide gate dielectric by the process of claim 21.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-09-26 | 2004-03-27 | 2004-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-09-26 | 2008-03-27 | 2008-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-09-26 | 2012-03-27 | 2012-09-26 | $7700.00 | Window Closed / Lapsed |