Dental adhesive and use thereof in preparing dental impression

Claim 2

An organopolysiloxane adhesive composition, comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive, wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D, and wherein following evaporation of solvent, a non-tacky film is formed.

Claim 3

The adhesive composition of claim 1 , wherein said organopolysiloxane rubber is a vinyl-functional organopolysiloxane rubber, and said M′Q resin (C) is a vinyl-functional MQ resin.

Claim 4

The adhesive composition of claim 1 , containing the components (A)-(D) in amounts of: (A) 6%-10% (B) 16%-22% (C) 40%-70% (D) 2%-10%.

Claim 5

The adhesive of claim 3 wherein said organic solvent is present in an amount of from 45-55 weight percent based on the sum of components (A) through (E).

Claim 6

The adhesive of claim 1 wherein said organic solvent comprises an aliphatic hydrocarbon solvent.

Claim 7

The adhesive of claim 1 wherein said adhesive is free of fillers having a mean particle size in excess of 10 μm.

Claim 8

An organopolysiloxane adhesive composition, comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive; wherein said adhesive exhibits substantial adhesion to both a curable organopolysiloxane dental impression material and a dental impression tray, and wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D.

Claim 9

An organopolysiloxane adhesive composition, comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive; wherein said adhesive exhibits substantial adhesion to both a curable organopolysiloxane dental impression material and a dental impression tray, and wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D.

Claim 10

The adhesive of claim 7 which exhibits substantial adhesion to subsequently added dental impression material for a period of four hours between coating said adhesive onto a dental impress ion tray and adding said dental impression material.

Claim 11

In a process for preparing a dental impression by contacting teeth with a tray containing a curable dental impression material, the improvement comprising coating the tray with a dental adhesive prior to introducing impression material into the tray, said dental adhesive comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive, and wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D.

Claim 12

In a process for preparing a dental impression by contacting teeth with a tray containing a curable dental impression material, the improvement comprising coating the tray with a dental adhesive prior to introducing impression material into the tray, said dental adhesive comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive, and wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D.

Claim 13

The process of claim 9 , wherein said organopolysiloxane rubber is a vinyl-functional organopolysiloxane rubber, and said M 1 Q resin (C) is a vinyl-functional MQ resin.

Claim 14

The process of claim 9 , wherein said adhesive contains the components (A)-(D) in amounts of: (A) 6%-10% (B) 16%-22% (C) 40%-70% (D) 2%-10%.

Claim 15

The process of claim 9 , wherein said adhesive exhibits substantial adhesion to both a curable organopolysiloxane dental impression material and a dental impression tray.

Claim 16

The process of claim 9 , wherein said adhesive exhibits substantial adhesion to subsequently added dental impression material for a period of four hours between coating said adhesive onto a dental impression tray and adding said dental impression material.

Claim 17

The process of claim 9 , wherein said organic solvent comprises an aliphatic hydrocarbon solvent.

Claim 18

The process of claim 9 , wherein said adhesive is free of fillers having a mean particle size in excess of 10 μm.

Claim 19

The dental adhesive of claim 9 , wherein said organic solvent is present in an amount of from 45-55 weight percent based on the sum of components (A) through (E).

Claim 20

An organopolysiloxane adhesive composition, comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive; wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D, and wherein said adhesive composition contains no hydrosilylation catalyst.

Claim 21

An organopolysiloxane adhesive composition, comprising, in weight percent based on the total weight of component (A) through (D) of the composition: (A) from about 2% to about 20% of at least one organopolysiloxane rubber base; (B) from about 10% to about 25% of at least one organopolysiloxane pressure sensitive adhesive; (C) from about 30% to about 80% of at least one aliphatic unsaturation-functional organopolysiloxane M′Q resin; (D) from about 1% to about 20% of at least one Si—H functional organopolysiloxane crosslinking agent containing minimally 3 Si—H bound hydrogens per molecule on average; components (A) through (D) dissolved in (E) sufficient organic solvent to obtain a solids content of ingredients (A) to (D) of from 30 percent to about 70% based on the total weight of the adhesive; wherein the sum of the weight percentages of components A to D is 100% based on the weight of components A to D, and wherein said adhesive composition contains no hydrosilylation catalyst.

Claim 22

The adhesive composition of claim 17 , wherein said organopolysiloxane rubber is a vinyl-functional organopolysiloxane rubber, and said M′Q resin (C) is a vinyl-functional M′Q resin.

Claim 23

The adhesive composition of claim 17 , containing the components (A)-(D) in amounts of: (A) 6%-10% (B) 16%-22% (C) 40%-70% (D) 2%-10%.

Claim 24

The adhesive of claim 17 which exhibits substantial adhesion to subsequently added dental impression material for a period of four hours between coating said adhesive onto a dental impression tray and adding said dental impression material.