Process for fabricating two different gate dielectric thicknesses using a polysilicon mask and chemical mechanical polishing (CMP) planarization
Assignee: International Business Machines Corp
•
Filing: 1999-07-22
•
Granted: 2001-03-13
•
Expires: 2019-07-22
Abstract
Abstract A method of forming a semiconductor device, including forming a substrate with a memory array region and a logic device region, growing a thick gate dielectric over the substrate, forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the memory array region, forming a thin gate dielectric on the substrate over the logic device region, wherein layers of the gate stack in the memory array region protect the thick gate oxide during the forming of the thin gate dielectric, forming a second polysilicon layer for the gate stack in the logic device region, to produce a resulting structure, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the memory array region, planarizing the structure using chemical mechanical polishing (CMP), and patterning the gate stacks in said memory array region and the logic device region.
Inventors
- 👤 Gary B. Bronner
- 👤 Jeffrey Peter Gambino
- 👤 Carl J. Radens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:02
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0135; H10D84/0137; H10D84/014; H10D84/0144; H10D84/02; H10D84/03; H10D84/038
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
185 words
A method of forming a semiconductor device, comprising: forming a substrate with a memory array region and a logic device region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the memory array region; removing the thick gate dielectric over said logic device region; forming a thin gate dielectric on said substrate over said logic device region, wherein layers of the gate stack in the memory array region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the logic device region, to produce a resulting structure, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the memory array region; planarizing the structure using chemical mechanical polishing (CMP); and patterning the gate stacks in said memory array region and said logic device region such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 2
Independent Claim
185 words
A method of forming a semiconductor device, comprising: forming a substrate with a memory array region and a logic device region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the memory array region; removing the thick gate dielectric over said logic device region; forming a thin gate dielectric on said substrate over said logic device region, wherein layers of the gate stack in the memory array region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the logic device region, to produce a resulting structure, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the memory array region; planarizing the structure using chemical mechanical polishing (CMP); and patterning the gate stacks in said memory array region and said logic device region such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 3
Dependent Claim
62 words
The method according to claim 1 , wherein said forming said gate stack comprises: forming said first polysilicon layer over said thick gate dielectric, said first polysilicon being a doped polysilicon; forming a silicide over said first polysilicon layer; forming a pad nitride over said silicide; and removing materials of the gate stack over the logic device region by lithography and etching.
Claim 4
Dependent Claim
35 words
The method according to claim 1 , wherein said gate stack has a cap nitride layer, and wherein said planarizing comprises using a cap nitride layer in the memory array region as a polish stop.
Claim 5
Dependent Claim
30 words
The method according to claim 1 , wherein the thin gate dielectric is formed on top of the first polysilicon layer, and is used as a polish stop during CMP.
Claim 6
Dependent Claim
52 words
The method according to claim 1 , wherein said patterning is performed using lithography and reactive ion etching (RIE), said method further comprising: doping of diffusions and gates in the logic device region by ion implantation and annealing; and forming silicides on the diffusions and the gates in the logic device region.
Claim 7
Dependent Claim
26 words
The method according to claim 1 , wherein said thick gate dielectric has a thickness within a range of about 5 nm to about 50 nm.
Claim 8
Dependent Claim
19 words
The method according to claim 1 , wherein said thick gate dielectric has a thickness of about 7 nm.
Claim 9
Dependent Claim
25 words
The method according to claim 1 , wherein said thick gate dielectric is at least one of SiO 2 and SiO x N y .
Claim 10
Dependent Claim
36 words
The method according to claim 1 , wherein said first polysilicon layer is at least one of As- and P-doped polysilicon, and has a thickness within a range of about 20 nm to about 200 nm.
Claim 11
Dependent Claim
19 words
The method according to claim 9 , wherein said first polysilicon layer has a thickness of about 50 nm.
Claim 12
Dependent Claim
27 words
The method according to claim 2 , wherein said silicide comprises WSi 2 having a thickness within a range of about 20 nm to about 100 nm.
Claim 13
Dependent Claim
17 words
The method according to claim 11 , wherein said silicide has a thickness of about 50 nm.
Claim 14
Dependent Claim
25 words
The method according to claim 2 , wherein said cap nitride has a thickness within a range of about 20 nm to about 300 nm.
Claim 15
Dependent Claim
18 words
The method according to claim 13 , wherein said cap nitride has a thickness of about 150 nm.
Claim 16
Dependent Claim
26 words
The method according to claim 1 , wherein the thin gate dielectric has a thickness within a range of about 2 nm to about 20 nm.
Claim 17
Dependent Claim
44 words
The method according to claim 15 , wherein said thin gate dielectric has a thickness of 5 nm, and comprises at least one of SiO 2 and SiO x N y , SiN, Ta 2 O 5 , and Al 2 O 3 .
Claim 18
Dependent Claim
33 words
The method according to claim 1 , wherein said second polysilicon layer comprises an undoped polysilicon layer deposited by chemical vapor deposition (CVD), and is for the gates in the logic device region.
Claim 19
Dependent Claim
30 words
The method according to claim 1 , wherein a thickness of the second polysilicon layer is at least as thick as the total gate stack in the memory array region.
Claim 20
Dependent Claim
22 words
The method according to claim 2 , wherein said pad nitride comprises Si 3 N 4 and functions as a polish stop.
Claim 21
Dependent Claim
26 words
The method according to claim 1 , wherein said thin gate dielectric formed on top of the first polysilicon layer is used as a polish stop.
Claim 22
Dependent Claim
47 words
The method of claim 1 , wherein said gate stacks respectively have two different gate dielectric thicknesses, while maintaining a planar surface for all lithography processes and wherein said gate stack over the thick gate dielectric is planar with said gate stack over said thin gate dielectric.
Claim 23
Independent Claim
169 words
A method of forming a semiconductor device having two different gate dielectric thicknesses, comprising: forming a substrate with a first region and a second region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the first region; removing the thick gate dielectric over said second region; forming a thin gate dielectric on said substrate over said second region, wherein layers of the gate stack in the first region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the second region, to produce a resulting structure, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the first region; and planarizing the structure using chemical mechanical polishing (CMP) such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 24
Independent Claim
169 words
A method of forming a semiconductor device having two different gate dielectric thicknesses, comprising: forming a substrate with a first region and a second region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the first region; removing the thick gate dielectric over said second region; forming a thin gate dielectric on said substrate over said second region, wherein layers of the gate stack in the first region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the second region, to produce a resulting structure, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the first region; and planarizing the structure using chemical mechanical polishing (CMP) such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 25
Dependent Claim
21 words
The method according to claim 22 , further comprising: patterning the gate stacks in said first region and said second region.
Claim 26
Dependent Claim
25 words
The method according to claim 22 , wherein said first region comprises a memory array region and said second region comprises a logic device region.
Claim 27
Dependent Claim
60 words
The method according to claim 22 , wherein forming said gate stack comprises: forming said first polysilicon layer over said thick gate dielectric, said first polysilicon being a doped polysilicon; forming a silicide over said first polysilicon layer; forming a pad nitride over said silicide; and removing materials of the gate stack over the second region by lithography and etching.
Claim 28
Independent Claim
143 words
A method of forming an embedded flash memory, comprising: forming a substrate with a first region and a second region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the first region; removing the thick gate dielectric over said second region; forming a thin gate dielectric on said substrate over said second region, wherein layers of the gate stack in the first region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the second region, to produce a resulting structure; and planarizing the structure using chemical mechanical polishing (CMP) such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 29
Independent Claim
143 words
A method of forming an embedded flash memory, comprising: forming a substrate with a first region and a second region; growing a thick gate dielectric over said substrate; forming a gate stack, including a first polysilicon layer, over the thick gate dielectric for the first region; removing the thick gate dielectric over said second region; forming a thin gate dielectric on said substrate over said second region, wherein layers of the gate stack in the first region protect the thick gate oxide during the forming of the thin gate dielectric; forming a second polysilicon layer for a gate stack in the second region, to produce a resulting structure; and planarizing the structure using chemical mechanical polishing (CMP) such that a planar surface is provided during all of said patterning of the gate stacks and said gate stacks each have a planar gate stack.
Claim 30
Dependent Claim
42 words
The method according to claim 26 , further comprising: patterning the gate stacks in said first region and said second region, wherein a thickness of the second polysilicon layer is at least as thick as the gate stack in the first region.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-03-12 | 2004-09-11 | 2005-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-03-12 | 2008-09-11 | 2009-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-03-12 | 2012-09-11 | 2013-03-13 | $7700.00 | Window Closed / Lapsed |