Method for making nanoporous silicone resins from alkylhydridosiloxane resins
Assignee: Dow Silicones Corp
•
Filing: 2000-06-16
•
Granted: 2001-02-06
•
Expires: 2020-06-16
Abstract
Abstract A method for preparing a nanoporous silicone resin which can be used to form low dielectric constant films useful for electrical insulating coatings on electronic devices comprising (A) contacting a hydridosilicon containing resin with a 1-alkene comprising about 8 to 28 carbon atoms in the presence of a platinum group metal-containing hydrosilation catalyst effecting formation of an alkylhydridosiloxane resin where at least 5 percent of silicon atoms are substituted with at least one group comprising about 8 to 28 carbon atoms and at least 45 percent of silicon atoms are substituted with at least one hydrogen atom and (B) heating the alkylhydridosiloxane resin of step (A) at a temperature sufficient to effect curing and thermolysis of alkyl groups comprising about 8 to 28 carbon atoms from the silicon atoms thereby forming a nanoporous silicone resin.
Inventors
- 👤 Bianxiao Zhong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:31
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/02; H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; C09; C09D; C09D183/00; C09D183/04; H10P14/63; H10P14/6326; H10P14/6342; H10P14/66; H10P14/668; H10P14/6681; H10P14/6684; H10P14/6686; H10P14/665
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
119 words
A method for preparing a nanoporous silicone resin comprising the steps of (A) contacting a hydridosilicon containing resin with a 1-alkene comprising about 8 to 28 carbon atoms in the presence of a platinum group metal-containing hydrosilation catalyst effecting formation of an alkylhydridosiloxane resin where at least 5 percent of silicon atoms are substituted with at least one alkyl group comprising about 8 to 28 carbon atoms and at least 45 percent of silicon atoms are substituted with at least one hydrogen atom and (B) heating the alkylhydridosiloxane resin of step (A) at a temperature sufficient to effect thermolysis of alkyl substituents comprising about 8 to 28 carbon atoms of the alkylhydridosiloxane resin thereby forming a nanoporous silicone resin.
Claim 2
Independent Claim
119 words
A method for preparing a nanoporous silicone resin comprising the steps of (A) contacting a hydridosilicon containing resin with a 1-alkene comprising about 8 to 28 carbon atoms in the presence of a platinum group metal-containing hydrosilation catalyst effecting formation of an alkylhydridosiloxane resin where at least 5 percent of silicon atoms are substituted with at least one alkyl group comprising about 8 to 28 carbon atoms and at least 45 percent of silicon atoms are substituted with at least one hydrogen atom and (B) heating the alkylhydridosiloxane resin of step (A) at a temperature sufficient to effect thermolysis of alkyl substituents comprising about 8 to 28 carbon atoms of the alkylhydridosiloxane resin thereby forming a nanoporous silicone resin.
Claim 3
Dependent Claim
85 words
A method according to claim 1 where the hydridosilicon containing resin is selected from the group of hydridosiloxane resins described by formulas (HSiO 3/2 ) n , (H 2 SiO) m , and (HSiO 3/2 ) x (H 2 SiO) y , where n is within a range of about 100 to 1000, m is within a range of about 100 to 1000, x and y are each an integer of one or greater and x+y is within a range of about 100 to 1000.
Claim 4
Dependent Claim
31 words
A method according to claim 1 where the hydridosilicon containing resin is described by formula (HSiO 3/2 ) n , where n is within a range of about 100 to 1000.
Claim 5
Dependent Claim
21 words
A method according to claim 1 , where the 1-alkene is a branched 1-alkene comprising about 8 to 28 carbon atoms.
Claim 6
Dependent Claim
21 words
A method according to claim 1 , where the 1-alkene is selected from the group consisting of 1-dodecene, 1-ecicosene and 3,7,11,15-tetramethyl-1-hexadecen-3-ol.
Claim 7
Dependent Claim
32 words
A method according to claim 1 , where the mole ratio of the 1-alkene to silicon-bonded hydrogen atoms in the hydridosilicon containing resin is within a range of about 0.05:1 to 0.7:1.
Claim 8
Dependent Claim
32 words
A method according to claim 1 , where the mole ratio of the 1-alkene to silicon-bonded hydrogen atoms in the hydridosilicon containing resin is within a range of about 0.1 to 0.5:1.
Claim 9
Dependent Claim
53 words
A method according to claim 1 , where about 10 to 25 percent of the silicon atoms of the alkylhydridosiloxane resin are substituted with at least one alkyl group comprising about 8 to 28 carbon atoms and at least 70 percent of the silicon atoms are substituted with at least one hydrogen atom.
Claim 10
Dependent Claim
19 words
A method according to claim 1 , where the heating of step (B) is conducted in an inert atmosphere.
Claim 11
Dependent Claim
37 words
A method according to claim 1 , where the thermolysis of alkyl substituents comprising about 8 to 28 carbon atoms is conducted at a temperature within a range of greater than 350° C. to about 600° C.
Claim 12
Dependent Claim
34 words
A method according to claim 1 , where the thermolysis of alkyl substituents comprising about 8 to 28 carbon atoms is conducted at a temperature within a range of 400° C. to 550° C.
Claim 13
Dependent Claim
12 words
A nanoporous silicon resin prepared by the method of claim 1 .
References Cited (Backward Citations)
US3159601A
Cited
US3220972A
Cited
US3296291A
Cited
US3419593A
Cited
US3516946A
Cited
US3615272A
Cited
US3814730A
Cited
US3928629A
Cited
US3989668A
Cited
US4756977A
Cited
US5010159A
Cited
US5036117A
Cited
US5063267A
Cited
US5776990A
Cited
US5494859A
Cited
JPH10287746A
Cited
WO1998047941A1
Cited
WO1998047944A1
Cited
WO1998047945A1
Cited
WO1998049721A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-02-06 | 2004-08-07 | 2005-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-02-06 | 2008-08-07 | 2009-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-02-06 | 2012-08-07 | 2013-02-06 | $7700.00 | Window Closed / Lapsed |