Ultra-low sheet resistance metal/poly-si gate for deep sub-micron CMOS application
Assignee: National University of Singapore
•
Filing: 1998-10-01
•
Granted: 2000-07-25
•
Expires: 2018-10-01
Abstract
Abstract A method for fabricating a deep sub-micron gate electrode, comprising polysilicon and metal, having ultra-low sheet resistance. The process begins by forming shallow trench isolation regions 14 in a silicon substrate 10. A gate oxide layer is formed on device areas. A doped blanket polysilicon layer 16 is formed on the gate oxide layer. A cap layer 20 composed of silicon nitride is formed on the polysilicon layer 16. The cap layer 20 and the polysilicon layer 16 are patterned by photoresist masking and anisotropic etching to form a bottom gate electrode 16A and a gate cap 20A. Lightly doped source/drain areas 22 are formed adjacent to the gate bottom electrodes 16A by ion implantation. Sidewall spacers 21 are formed on the gate electrode 16A and gate cap 20A. Source/drain regions 24 are formed by ion implantation adjacent to said sidewall spacers 21. A metal silicide 23 is formed on the source/drain regions 24. An interlevel dielectric layer (ILD) 28 is deposited and planarized by CMP using the gate cap 20A as a CMP stop. The gate cap 20 is selectively removed. A barrier layer 32 composed of a TaN, CoWP, TiN or W x N y is formed over the planarized IDL 28A. A top gate layer 36 composed of copper or tungsten is formed on the barrier layer 32. The top gate layer 36 and the barrier layer 32 are removed down to the level of the top of the ILD 28 using CMP; thereby forming a top gate electrode. A passivation layer 40, composed of Pd or NiP is selectively deposited over the gate top electrode 36A.
Inventors
- 👤 Chong Wee Lim
- 👤 Kin Leong Pey
- 👤 Soh Yun Siah
- 👤 Eng Hwa Lim
- 👤 Lap Chan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:04
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/01312; H10D64/60; H10D64/66; H10D64/661; H10D64/662; H10D64/664; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0172; H10D84/0177; H10D84/02; H10D84/03; H10D84/038; H10D64/017
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
227 words
A method for fabricating an ultra-low sheet resistance gate electrode for CMOS applications; comprising the steps of: a) providing a semiconductor substrate having a gate oxide layer thereon, a bottom gate electrode over said gate oxide layer, a gate cap over said bottom gate electrode, a lightly doped source/drain region adjacent to said bottom gate electrode, sidewall spacers on said bottom gate electrode and said gate cap, source/drain regions adjacent to said sidewall spacers, suicide contacts on said source/drain regions, and an interlevel dielectric layer over said substrate, said gate oxide layer, said bottom gate electrode, said lightly doped source/drain region, said sidewall spacers, said source/drain regions, and said silicide contacts; b) chemical/mechanically polishing said interlevel dielectric layer down to the level of the top of said gate cap; c) selectively removing said gate cap; d) forming a barrier layer over said interlevel dielectric layer, said bottom gate electrode and said sidewall spacers; e) forming a top gate electrode layer on said barrier layer; said top gate electrode layer being composed of metal; f) removing said top gate electrode layer and said barrier layer down to the level of the top of said interlevel dielectric layer using chemical/mechanical polishing; thereby forming a gate electrode comprising a top gate electrode, a barrier layer and a bottom gate electrode; g) forming a passivation layer over said top gate electrode.
Claim 2
Independent Claim
227 words
A method for fabricating an ultra-low sheet resistance gate electrode for CMOS applications; comprising the steps of: a) providing a semiconductor substrate having a gate oxide layer thereon, a bottom gate electrode over said gate oxide layer, a gate cap over said bottom gate electrode, a lightly doped source/drain region adjacent to said bottom gate electrode, sidewall spacers on said bottom gate electrode and said gate cap, source/drain regions adjacent to said sidewall spacers, suicide contacts on said source/drain regions, and an interlevel dielectric layer over said substrate, said gate oxide layer, said bottom gate electrode, said lightly doped source/drain region, said sidewall spacers, said source/drain regions, and said silicide contacts; b) chemical/mechanically polishing said interlevel dielectric layer down to the level of the top of said gate cap; c) selectively removing said gate cap; d) forming a barrier layer over said interlevel dielectric layer, said bottom gate electrode and said sidewall spacers; e) forming a top gate electrode layer on said barrier layer; said top gate electrode layer being composed of metal; f) removing said top gate electrode layer and said barrier layer down to the level of the top of said interlevel dielectric layer using chemical/mechanical polishing; thereby forming a gate electrode comprising a top gate electrode, a barrier layer and a bottom gate electrode; g) forming a passivation layer over said top gate electrode.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein said gate bottom electrode has a maximum width of 0.25 μm and a thickness in the range between about 1000 Å and 3000 Å.
Claim 4
Dependent Claim
28 words
The method of claim 1 wherein said top gate electrode layer is composed of copper or tungsten having a thickness of between about 200 Å and 2000 Å.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein said barrier layer is composed of TaN, CoWP or W x N y having a thickness in the range between about 50 Å and 500 Å.
Claim 6
Dependent Claim
52 words
The method of claim 1 wherein said bottom gate electrode layer is composed of N+ polysilicon having a thickness in the range between about 1000 Å and 3000 Å; said polysilicon layer being doped with arsenic at a concentration of between about 1.2 E 20 and 2.8 E 20 atoms/cm 3 .
Claim 7
Dependent Claim
68 words
The method of claim 1 wherein said silicide contacts are formed by depositing a metal layer comprising Ti, Co, Ni, Pd, or a combination thereof having a thickness between about 10 and 350 Angstroms; said metal layer being annealed by rapid thermal annealing at a temperature in the range of between about 350° C. and 850° C. for a time of between about 20 seconds and 60 seconds.
Claim 8
Dependent Claim
36 words
The method of claim 1 wherein said passivation layer is composed of a Pd or NiP selectively deposited on said top gate electrode having a thickness in the range between about 50 Å and 500 Å.
Claim 9
Dependent Claim
33 words
The method of claim 1 wherein said passivation layer is composed of Si 3 N 4 or SiO x N y blanket deposited over said top gate electrode and said interlevel dielectric layer.
Claim 10
Dependent Claim
44 words
The method of claim 1 wherein the gate cap acts a polish stop during chemical/mechanical polishing of said interlevel dielectric layer and said interlevel dielectric layer acts as a polishing stop during chemical/mechanical polishing of said top gate electrode layer and said barrier layer.
Claim 11
Independent Claim
241 words
A method for fabricating an ultra-low sheet resistance gate electrode for CMOS applications; comprising the steps of: a) providing a semiconductor substrate; b) forming a gate oxide layer on said semiconductor substrate; c) depositing a non-monocrystalline silicon layer on said substrate; d) depositing a cap layer on said non-monocrystalline silicon layer; e) patterning said cap layer and said non-monocrystalline silicon layer to form a bottom gate electrode and a gate cap thereover; f) forming lightly doped source/drain regions adjacent to said gate bottom gate electrode; g) forming sidewall spacers on said gate bottom electrode and said gate cap; h) forming source/drain regions adjacent to said sidewall spacers; i) forming suicide contacts on said source/drain regions; j) depositing an interlevel dielectric layer over said substrate; k) chemical/mechanically polishing said interlevel dielectric layer down to the level of the top of said gate cap; l) selectively removing said gate cap; m) forming a barrier layer over said interlevel dielectric layer, said bottom gate electrode and said sidewall spacers; n) forming a top gate electrode layer on said barrier layer; said top gate electrode layer composed of copper or tungsten; o) removing said top gate electrode layer and said barrier layer down to the level of the top of said interlevel dielectric layer using chemical/mechanical polishing; thereby forming a gate electrode comprising a top gate electrode, a barrier layer and a bottom gate electrode; p) forming a passivation layer over said top gate electrode.
Claim 12
Independent Claim
241 words
A method for fabricating an ultra-low sheet resistance gate electrode for CMOS applications; comprising the steps of: a) providing a semiconductor substrate; b) forming a gate oxide layer on said semiconductor substrate; c) depositing a non-monocrystalline silicon layer on said substrate; d) depositing a cap layer on said non-monocrystalline silicon layer; e) patterning said cap layer and said non-monocrystalline silicon layer to form a bottom gate electrode and a gate cap thereover; f) forming lightly doped source/drain regions adjacent to said gate bottom gate electrode; g) forming sidewall spacers on said gate bottom electrode and said gate cap; h) forming source/drain regions adjacent to said sidewall spacers; i) forming suicide contacts on said source/drain regions; j) depositing an interlevel dielectric layer over said substrate; k) chemical/mechanically polishing said interlevel dielectric layer down to the level of the top of said gate cap; l) selectively removing said gate cap; m) forming a barrier layer over said interlevel dielectric layer, said bottom gate electrode and said sidewall spacers; n) forming a top gate electrode layer on said barrier layer; said top gate electrode layer composed of copper or tungsten; o) removing said top gate electrode layer and said barrier layer down to the level of the top of said interlevel dielectric layer using chemical/mechanical polishing; thereby forming a gate electrode comprising a top gate electrode, a barrier layer and a bottom gate electrode; p) forming a passivation layer over said top gate electrode.
Claim 13
Dependent Claim
30 words
The method of claim 10 wherein said gate bottom electrode has a maximum width of 0.25 μm and a thickness in the range between about 1000 Å and 3000 Å.
Claim 14
Dependent Claim
33 words
The method of claim 10 wherein said barrier layer is composed of TaN, CoWP or W x N y having a thickness in the range of between about 50 Å and 500 Å.
Claim 15
Dependent Claim
52 words
The method of claim 10 wherein said bottom gate electrode layer is composed of N+ polysilicon having a thickness in the range between about 1000 Å and 3000 Å; said polysilicon layer being doped with arsenic at a concentration of between about 1.2 E 20 and 2.8 E 20 atoms/cm 3 .
Claim 16
Dependent Claim
67 words
The method of claim 10 wherein said silicide contacts are formed by depositing a metal layer comprising Ti, Co, Ni, Pd, or combination thereof having a thickness between about 10 and 350 Angstroms; said metal layer being annealed by rapid thermal annealing at a temperature in the range of between about 350° C. and 850° C. for a time of between about 20 seconds and 60 seconds.
Claim 17
Dependent Claim
36 words
The method of claim 10 wherein said passivation layer is composed of a Pd or NiP selectively deposited on said top gate electrode having a thickness in the range between about 50 Å and 500 Å.
Claim 18
Dependent Claim
33 words
The method of claim 10 wherein said passivation layer is composed of Si 3 N 4 or SiO x N y blanket deposited over said top gate electrode and said interlevel dielectric layer.
Claim 19
Dependent Claim
43 words
The method of claim 10 wherein the gate cap acts a CMP stop during polishing of said interlevel dielectric layer and said interlevel dielectric layer acts as a polish stop during chemical/mechanical polishing of said top gate electrode layer and said barrier layer.
Claim 20
Dependent Claim
22 words
The method of claim 10 wherein said gate cap has a thickness in the range between about 1000 Å and 2000 Å.
Claim 21
Dependent Claim
20 words
The method of claim 10 wherein said gate cap is selectively removed using a wet etch comprising hot phosphoric acid.
References Cited (Backward Citations)
US4931411A
Cited
US5641983A
Cited
US5447874A
Cited
US5861340A
Cited
US5731239A
Cited
US5899740A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-07-25 | 2004-01-24 | 2004-07-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-07-25 | 2008-01-24 | 2008-07-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-07-25 | 2012-01-24 | 2012-07-25 | $7700.00 | Window Closed / Lapsed |