Sheet for a thermal conductive substrate, a method for manufacturing the same, a thermal conductive substrate using the sheet and a method for manufacturing the same
Assignee: Panasonic Holdings Corp
•
Filing: 1997-10-06
•
Granted: 2000-05-09
•
Expires: 2017-10-06
Abstract
Abstract A thermally conductive substrate having a structure in which inorganic filler for improving the thermal conductivity and thermosetting resin composition are included. The thermosetting resin composition has a flexibility in the not-hardened state, and becomes rigid after hardening. The thermally conductive substrate has excellent thermal radiation characteristics. The method of manufacturing the thermally conductive substrate includes: piling up (a) the thermally conductive sheets comprising 70 to 95 weight parts of an inorganic filler, and 4.9 to 28 weight parts of a thermosetting resin composition, the thermosetting resin composition comprising at least one thermosetting resin, a hardener and a hardening accelerator, and (b) lead frame on which a wiring is formed; thermal pressing the pile; filling the thermally conductive sheet to the surface of the lead frame; hardening the thermosetting resin; cutting excess sections of the thermally conductive substrate; and processing the bending perpendicularly for making a removable electrode.
Inventors
- 👤 Seiichi Nakatani
- 👤 Hiroyuki Handa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:49
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B32B27/00; B32B27/18; B32B27/20; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0373; H10; H10W; H10W70/00; H10W70/40; H10W70/479; H10W70/60; H10W70/67; H10W70/69; H10W70/695; H10W90/00; H10W90/401; B32B2305/00; B32B2305/74; B32B2307/00; B32B2307/30; B32B2307/302; B32B2311/00; B32B2311/12; B32B2457/00; B32B2457/08; H05K1/05; H05K1/056; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0209; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K3/00; H05K3/0058; H05K3/10; H05K3/20; H05K3/202; H05K3/40; H05K3/4038; H05K3/4053; H05K3/4069; H05K3/4092; H05K3/46; H05K3/4611; H05K3/4614; H05K3/4644; H05K3/4652; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1034; Y10T156/1052; Y10T156/1056; Y10T156/1057; Y10T156/1089; Y10T156/109; Y10T156/1092; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/25; Y10T428/252; Y10T428/256; Y10T428/257; Y10T428/258; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31692
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
122 words
A sheet mixture for a thermally conductive substrate comprising 70 to 95 weight parts of an inorganic filler and 5 to 30 weight parts of a thermosetting resin composition comprising at least one thermosetting resin, a hardener and a hardening accelerator; said sheet mixture having flexibility in a half hardened state or partially hardened state, wherein said thermosetting resin composition comprises: 1) 4 to 45 weight parts of a first resin that is solid at room temperature, 2) 5 to 50 weight parts of a second resin that is liquid at room temperature, 3) 4.9 to 45 weight parts of said hardener, and 4) 0.1 to 5 weight parts of said hardening accelerator in 100 weight parts of said thermosetting resin composition.
Claim 2
Dependent Claim
122 words
A sheet mixture for a thermally conductive substrate comprising 70 to 95 weight parts of an inorganic filler and 5 to 30 weight parts of a thermosetting resin composition comprising at least one thermosetting resin, a hardener and a hardening accelerator; said sheet mixture having flexibility in a half hardened state or partially hardened state, wherein said thermosetting resin composition comprises: 1) 4 to 45 weight parts of a first resin that is solid at room temperature, 2) 5 to 50 weight parts of a second resin that is liquid at room temperature, 3) 4.9 to 45 weight parts of said hardener, and 4) 0.1 to 5 weight parts of said hardening accelerator in 100 weight parts of said thermosetting resin composition.
Claim 3
Dependent Claim
33 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein the half hardened state or partially hardened state has viscosity in the range of 10 2 to 10 5 (Pa·s).
Claim 4
Dependent Claim
33 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein the half hardened state or partially hardened state has viscosity in the range of 10 3 to 10 4 (Pa·s).
Claim 5
Dependent Claim
51 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein 0.1 to 2 weight parts of a solvent having a boiling point of not less than 150° C. is further added to 100 weight parts of a mixture of said inorganic filler and said thermosetting resin it composition.
Claim 6
Dependent Claim
44 words
A sheet mixture for a thermally conductive substrate according to claim 4, wherein said solvent having a boiling point of not less than 150° C. is at least one solvent selected from the group consisting of ethyl carbitol, butyl carbitol and butyl carbitol acetate.
Claim 7
Dependent Claim
44 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein said resin that is liquid at room temperature contains one or more components selected from the group consisting of bisphenol A epoxy resin, bisphenol F epoxy resin and liquid phenol resin.
Claim 8
Dependent Claim
35 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein said thermosetting resin composition comprises at least one resin selected from the group consisting of epoxy resin, phenol resin and cyanate resin.
Claim 9
Dependent Claim
37 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein said thermosetting resin comprises a brominated multifunctional epoxy resin, said hardener is a bisphenol A novolak resin, and said hardening accelerator is an imidazole.
Claim 10
Dependent Claim
65 words
A sheet mixture for a thermally conductive substrates according to claim 8, wherein said brominated multifunctional epoxy resin comprises in the range of 60 to 80 weight parts; said bisphenol A novolak resin is in the range of 18 to 39.9 weight parts, and said imidazole is in the range of 0.1 to 2 weight parts, in 100 weight parts of said thermosetting resin composition.
Claim 11
Dependent Claim
38 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein said inorganic filler is at least one kind of filler selected from the group consisting of Al 2 O 3 , MgO, BN and AlN.
Claim 12
Dependent Claim
34 words
A sheet mixture for a thermally conductive substrate according to claim 1, further comprising at least one additives selected from the group consisting of coupling agent, dispersing agent, coloring agent and tack free agent.
Claim 13
Dependent Claim
53 words
A thermally conductive and electrical insulating substrate, comprising one sheet mixture according to claim 1 in a hardened state, wherein the coefficient of thermal expansion of hardened said sheet mixture is in the range of 8 to 20 ppm/° C. and the thermal conductivity is in the range of 1 to 10 W/mK.
Claim 14
Dependent Claim
28 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein the flexural strength of said thermally conductive substrate is not less than 10 Kgf/mm 2 .
Claim 15
Dependent Claim
31 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein the flexural strength of said thermally conductive substrate is in the range of 10 to 20 Kgf/mm 2 .
Claim 16
Dependent Claim
47 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein a lead frame comprising an opening space is integrated with the substrate, said opening space is filled with the substrate and a surface of the lead frame is level with a surface of the substrate.
Claim 17
Dependent Claim
40 words
A thermally conductive and electrical insulating substrate according to claim 15, wherein a metal substrate for thermal radiation is further formed on the face opposite to the face to which the lead frame is adhered of the thermally conductive substrate.
Claim 18
Dependent Claim
44 words
A thermally conductive and electrical insulating substrate according to claim 15, wherein a printed circuit board comprising two or more wiring layers is integrated to the substrate on a face of the substrate to which the lead frame comprising an opening space is adhered.
Claim 19
Dependent Claim
49 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein the substrate has a through hole, said through hole is filled with conductive resin composition or is plated with copper, and a metallic foil wiring pattern is further formed and integrated on both sides of the substrate.
Claim 20
Dependent Claim
66 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein a plurality of substrates are layered and each of the substrates has a through hole, said through hole is filled with a conductive resin composition and an internal wiring pattern is composed of said conductive resin composition, and a metallic foil wiring pattern is further formed and integrated on both sides of the substrate.
Claim 21
Dependent Claim
40 words
A thermally conductive and electrical insulating substrate according to claim 19, wherein said metallic foil is a copper foil having a thickness of 12 to 200 μm and having faces at least one surface of which is a rough surface.
Claim 22
Dependent Claim
58 words
A thermally conductive and electrical insulating substrate according to claim 19, wherein said conductive resin composition comprises: (1) 70 to 95 weight parts of at least one metallic powder selected from the group consisting of silver, copper and nickel; and (2) 5 to 30 weight parts of a thermosetting resin composition comprising a thermosetting resin and a hardener.
Claim 23
Dependent Claim
27 words
A thermally conductive and electrical insulating substrate according to claim 12, wherein said inorganic filler has a particle diameter of 0.1 to 100 μm on the average.
Claim 24
Dependent Claim
51 words
A sheet mixture for a thermally conductive substrate according to claim 1, wherein said sheet mixture further comprises 0.1-2 wt % of at least one solvent having a boiling point of not less than 150° C. and selected from the group consisting of ethyl carbitol, butyl carbitol and butyl carbitol acetate.
References Cited (Backward Citations)
US4311753A
Cited
US4617584A
Cited
US4477512A
Cited
US4501787A
Cited
US4599268A
Cited
US4656207A
Cited
US4710429A
Cited
US4975319A
Cited
US5434199A
Cited
US5266385A
Cited
US5576362A
Cited
US5419946A
Cited
JPH0873621A
Cited
US5670250A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-05-09 | 2003-11-08 | 2004-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-05-09 | 2007-11-08 | 2008-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-05-09 | 2011-11-08 | 2012-05-09 | $7700.00 | Window Closed / Lapsed |