Propylene resin composition and automobile trim member
Assignee: Idemitsu Kosan Co Ltd
•
Filing: 1997-06-19
•
Granted: 2000-03-07
•
Expires: 2017-06-19
Abstract
Abstract A propylene-based resin composition comprising (A) from 42 to 95% by weight of a propylene-based resin having an isotactic pentad fraction of at least 95%, (B) from 1 to 10% by weight of an ethylene-C 3 -C 18 α-olefin copolymer having a density of from 0.850 to 0.875 g/cm 3 and a melt index of from 0.01 to 25 g/10 min, and prepared in the presence of a metallocene catalyst, (C) from 2 to 18% by weight of a high-density polyethylene having a density of from 0.93 to 0.97 g/cm 3 and a melt index of from 0.5 to 10 g/10 min, and (D) from 2 to 35% by weight of talc, the total of the components (B) and (C) being from 3 to 23% by weight.
Inventors
- 👤 Ryuzou Tomomatsu
- 👤 Toshiyuki Ishii
- 👤 Satoru Ohnishi
- 👤 Toshihide Nara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:08
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08K; C08K3/00; C08K3/34; C08L23/04; C08L23/06; C08L23/16
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
125 words
A propylene-based resin composition comprising (A) from 42 to 95% by weight of a propylene-based resin having an isotactic pentad fraction of at least 95%, (B) from 1 to 10% by weight of an ethylene-C 3-18 α-olefin copolymer having a density of from 0.850 to 0.875 g/cm 3 and a melt index of from 0.01 to 25 g/10 min, and prepared in the presence of a metallocene catalyst, (C) from 2 to 18% by weight of a high-density polyethylene having a density of from 0.93 to 0.97 g/cm 3 and a melt index of from 0.5 to 10 g/10 min, and (D) from 2 to 35% by weight of talc, the total of the components (B) and (C) being from 3 to 23% by weight.
Claim 2
Dependent Claim
125 words
A propylene-based resin composition comprising (A) from 42 to 95% by weight of a propylene-based resin having an isotactic pentad fraction of at least 95%, (B) from 1 to 10% by weight of an ethylene-C 3-18 α-olefin copolymer having a density of from 0.850 to 0.875 g/cm 3 and a melt index of from 0.01 to 25 g/10 min, and prepared in the presence of a metallocene catalyst, (C) from 2 to 18% by weight of a high-density polyethylene having a density of from 0.93 to 0.97 g/cm 3 and a melt index of from 0.5 to 10 g/10 min, and (D) from 2 to 35% by weight of talc, the total of the components (B) and (C) being from 3 to 23% by weight.
Claim 3
Dependent Claim
181 words
The propylene-based resin composition as claimed in claim 1, wherein the component (A) satisfies the following requirements (1) to (4): (1) The propylene-based resin of (A) comprises (a) from 70 to 98% by weight of a fragment insoluble in para-xylene at 23° C. and (b) from 2 to 30% by weight of a fragment soluble in para-xylene at 23° C.; (2) The fragment (a) has a relaxation time, τ, of from 0.01 to 0.35 seconds at an angular frequency, ω, of 10°/sec as obtained through melt viscoelastometry, and has a molecular weight distribution index (PDI) of from 1 to 18, which is represented by ω 2 /10ω 1 where ω 1 indicates an angular frequency at which the modulus of stored elasticity, G', as obtained through melt viscoelastometry is 2×10 2 Pa, and ω 2 indicates an angular frequency at which G' is 2×10 4 Pa; (3) The fragment (b) has a limiting viscosity [η] in decalin at 135° C. of from 2.0 to 10 dl/g; and (4) The ethylene unit content of (A) is from 1 to 17% by weight.
Claim 4
Dependent Claim
30 words
The propylene-based resin composition as claimed in claim 1, wherein the ethylene-C 3-18 α-olefin copolymer of the component (B) has an α-olefin content of from 20 to 70% by weight.
Claim 5
Dependent Claim
15 words
An automobile trim member as produced by injection-molding the propylene-based resin composition of claim 1.
Claim 6
Dependent Claim
15 words
An automobile trim member as produced by injection-molding the propylene-based resin composition of claim 3.
Claim 7
Dependent Claim
32 words
The propylene-based resin composition as claimed in claim 2, wherein the ethylene-C 3 -C 18 α-olefin copolymer of the component (B) has an α-olefin content of from 20 to 70% by weight.
Claim 8
Dependent Claim
15 words
An automobile trim member as produced by injection-molding the propylene-based resin composition of claim 2.
Claim 9
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 1, wherein the component (A) has a melt index of from 1 to 100 g/10 min.
Claim 10
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 8, wherein the component (A) has a melt index of from 5 to 70 g/10 min.
Claim 11
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 9, wherein the component (A) has a melt index of from 10 to 40 g/10 min.
Claim 12
Dependent Claim
55 words
The propylene-based resin composition as claimed in claim 1, wherein the component (A) is a mixture of a propylene-based resin having a melt index of larger than 8 g/10 min, and of from 5 to 30% by weight of said mixture, of a propylene-based resin having a melt index of smaller than 5 g/10 min.
Claim 13
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 1, wherein the component (B) has a density of from 0.855 to 0.870 g/cm 3 .
Claim 14
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 1, wherein the component (B) has a melt index of from 0.01 to 6 g/10 min.
Claim 15
Dependent Claim
24 words
The propylene-based resin composition as claimed in claim 13, wherein the component (B) has a melt index of from 0.01 to 1 g/10 min.
Claim 16
Dependent Claim
39 words
The propylene-based resin composition as claimed in claim 1, wherein the talc is in the form of grains having a mean grain size of from 1 to 8 μm and a mean aspect ratio of not smaller than 4.
References Cited (Backward Citations)
JPH01204946A
Cited
US5219913A
Cited
JPH04311748A
Cited
JPH06322191A
Cited
JPH06340782A
Cited
JPH07145298A
Cited
EP0696616A2
Cited
EP0784074A1
Cited
JPH0931268A
Cited
JPH0971691A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-03-07 | 2003-09-06 | 2004-03-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-03-07 | 2007-09-06 | 2008-03-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-03-07 | 2011-09-06 | 2012-03-07 | $7700.00 | Window Closed / Lapsed |