US6033962A — Method of fabricating sidewall spacers for a self…

Claim 1

Independent Claim 245 words

A method for fabricating a self-aligned contact, (SAC), opening, for a semiconductor device, on a semiconductor substrate, comprising the steps of: providing an isolation region, in said semiconductor substrate; providing a gate insulator layer on regions of said semiconductor substrate, not occupied by said isolation region; forming gate structures on said gate insulator layer; forming source/drain regions, in said semiconductor substrate, in regions of said semiconductor substrate not covered by said gate structures; depositing a first insulator layer; performing an anisotropic reactive ion etching, (RIE), procedure, removing a top portion of said first insulator layer, leaving a thin first insulator layer on said source/drain region, between said gate structures, leaving a thin first insulator layer on the top surface of said gate structures, and leaving a thin first insulator layer on the top surface of a portion of said isolation region, while forming partial first insulator spacers on the top sides of said gate structures; depositing a second insulator layer; planarizing said second insulator layer; forming a first SAC opening, in said second insulator layer, exposing the top surface of said thin first insulator layer, overlying said source/drain regions, and exposing said partial first insulator spacers; removing said thin first insulator layer, exposed in said first SAC opening, creating a second SAC opening, exposing said source/drain region, and creating complete first insulator spacers, on the entire sides of said gate structures; and forming SAC structures, contacting said source/drain regions, exposed in said second SAC opening.

Claim 2

Independent Claim 245 words

A method for fabricating a self-aligned contact, (SAC), opening, for a semiconductor device, on a semiconductor substrate, comprising the steps of: providing an isolation region, in said semiconductor substrate; providing a gate insulator layer on regions of said semiconductor substrate, not occupied by said isolation region; forming gate structures on said gate insulator layer; forming source/drain regions, in said semiconductor substrate, in regions of said semiconductor substrate not covered by said gate structures; depositing a first insulator layer; performing an anisotropic reactive ion etching, (RIE), procedure, removing a top portion of said first insulator layer, leaving a thin first insulator layer on said source/drain region, between said gate structures, leaving a thin first insulator layer on the top surface of said gate structures, and leaving a thin first insulator layer on the top surface of a portion of said isolation region, while forming partial first insulator spacers on the top sides of said gate structures; depositing a second insulator layer; planarizing said second insulator layer; forming a first SAC opening, in said second insulator layer, exposing the top surface of said thin first insulator layer, overlying said source/drain regions, and exposing said partial first insulator spacers; removing said thin first insulator layer, exposed in said first SAC opening, creating a second SAC opening, exposing said source/drain region, and creating complete first insulator spacers, on the entire sides of said gate structures; and forming SAC structures, contacting said source/drain regions, exposed in said second SAC opening.

Claim 3

Dependent Claim 78 words

The method of claim 1, wherein said isolation region, is a silicon oxide filled, shallow trench, where shallow trench is formed in said semiconductor substrate via an anisotropic RIE procedure, using Cl 2 as an etchant, and the silicon oxide, in shallow trench, is obtained via LPCVD or PECVD procedures, and removed from the top surface of said semiconductor substrate, via an anisotropic RIE procedure, using CHF 3 as an etchant, or via a chemical mechanical polishing procedure.

Claim 4

Dependent Claim 27 words

The method of claim 1, wherein said gate insulator layer is silicon dioxide, obtained via thermal oxidation procedures, to a thickness between about 50 to 100 Angstroms.

Claim 5

Dependent Claim 72 words

The method of claim 1, wherein said gate structures are comprised of a silicon nitride capped, polycide structures, in which the polycide structures are comprised of an overlying metal silicide layer, such as tungsten silicide or titanium silicide, obtained via LPCVD or R.F. sputtering procedures, at a thickness between about 500 to 1000 Angstroms, and an underlying polysilicon layer, obtained using LPCVD procedures, at a thickness between about 500 to 1000 Angstroms.

Claim 6

Dependent Claim 46 words

The method of claim 1, wherein said silicon nitride capped, gate structures, are formed via an anisotropic RIE procedure, using CF 4 --CHF 3 --Ar--O 2 as an etchant for silicon nitride, while using Cl 2 as an etchant for the metal silicide and polysilicon layers.

Claim 7

Dependent Claim 30 words

The method of claim 1, wherein said first insulator layer is silicon nitride, obtained using an LPCVD or a PECVD procedure, to a thickness between about 400 to 1000 Angstroms.

Claim 8

Dependent Claim 56 words

The method of claim 1, wherein said partial first insulator spacers are formed via an anisotropic RIE procedure, applied to said first insulator layer, using CHF 3 --Ar as an etchant, resulting in said thin first insulator layer, at a thickness between about 100 to 200 Angstroms, remaining on said source/drain region, between said gate structures.

Claim 9

Dependent Claim 66 words

The method of claim 1, wherein said second insulator layer is comprised of a boro-phosphosilicate glass, (BPSG), layer, obtained using an LPCVD or a PECVD procedure, to a thickness between about 5000 to 10000 Angstroms, with said second insulator layer containing between about 3 to 8 weight % B 2 O 3 , and between about 3 to 10 weight % P 2 O 5 .

Claim 10

Dependent Claim 33 words

The method of claim 1, wherein said second insulator layer is an undoped silicon oxide layer, obtained via an LPCVD or a PECVD procedure, at a thickness between about 5000 to 10000 Angstroms.

Claim 11

Dependent Claim 52 words

The method of claim 1, wherein said first SAC opening, is formed in said second insulator layer via an anisotropic RIE procedure, using C 4 F 8 --CO--Ar--O 2 as an etchant, with an etch rate selectivity between said second insulator layer, and said first insulator layer, of about 20 to 1.

Claim 12

Dependent Claim 61 words

The method of claim 1, wherein said second SAC opening is formed via an anisotropic RIE procedure, using CH 2 F 2 --CHF 3 --Ar--O 2 as an etchant, applied to said thin first insulator layer, exposed in said first SAC opening, with an etch rate selectivity between said first insulator layer, and said second insulator layer, of 20 to 1.

Claim 13

Dependent Claim 62 words

The method of claim 1, wherein said SAC structure is formed via deposition of a metal such as tungsten, or a polycide such as tungsten silicide on polysilicon, or a polysilicon layer, using an LPCVD procedure, at a thickness between about 3000 to 6000 Angstroms, followed by an anisotropic RIE patterning procedure, using Cl 2 --SF 6 --BCl 3 --Ar an etchant.

Claim 14

Independent Claim 309 words

A method of using a two step, anisotropic RIE procedure, and partial silicon nitride spacers, to create a self-aligned contact, (SAC), opening, in a composite insulator layer, for a semiconductor device, on a semiconductor substrate, comprising the steps of: forming a shallow trench isolation region in said semiconductor substrate; growing a silicon dioxide gate insulator layer, on said semiconductor substrate; depositing a polysilicon layer; depositing a tungsten silicide layer; depositing a first silicon nitride layer; forming a polycide, (tungsten silicide-polysilicon), gate structure, capped by said first silicon nitride layer, on said silicon dioxide gate insulator layer; forming source/drain regions in areas of said semiconductor substrate, not covered by silicon nitride capped, said polycide gate structures; depositing a second silicon nitride layer; performing an anisotropic RIE procedure, on said second silicon nitride layer, creating said partial silicon nitride spacers, on the top sides of said polycide gate structures, while leaving a thin second silicon nitride layer, on said source/drain regions, leaving a thin second silicon nitride layer on the top surface of said polycide gate structures, and leaving a thin second silicon nitride layer on the top surface of a portion of said shallow trench isolation region; depositing a boro-phosphosilicate glass, (BPSG), layer; planarizing said BPSG layer; performing a first step, of said two step anisotropic RIE procedure, selectively removing said BPSG layer, and creating a first SAC opening in said BPSG layer, exposing said thin second silicon nitride layer, and exposing said partial silicon nitride spacers; performing a second step, of said two step anisotropic RIE procedure, selectively removing said thin second silicon nitride layer, exposed in said first SAC opening, and creating a second SAC opening, exposing said source/drain region, while forming complete silicon nitride spacers, on the entire sides of said polycide gate structures; and forming SAC structures, contacting said source/drain region, in said second SAC opening.

Claim 15

Independent Claim 309 words

A method of using a two step, anisotropic RIE procedure, and partial silicon nitride spacers, to create a self-aligned contact, (SAC), opening, in a composite insulator layer, for a semiconductor device, on a semiconductor substrate, comprising the steps of: forming a shallow trench isolation region in said semiconductor substrate; growing a silicon dioxide gate insulator layer, on said semiconductor substrate; depositing a polysilicon layer; depositing a tungsten silicide layer; depositing a first silicon nitride layer; forming a polycide, (tungsten silicide-polysilicon), gate structure, capped by said first silicon nitride layer, on said silicon dioxide gate insulator layer; forming source/drain regions in areas of said semiconductor substrate, not covered by silicon nitride capped, said polycide gate structures; depositing a second silicon nitride layer; performing an anisotropic RIE procedure, on said second silicon nitride layer, creating said partial silicon nitride spacers, on the top sides of said polycide gate structures, while leaving a thin second silicon nitride layer, on said source/drain regions, leaving a thin second silicon nitride layer on the top surface of said polycide gate structures, and leaving a thin second silicon nitride layer on the top surface of a portion of said shallow trench isolation region; depositing a boro-phosphosilicate glass, (BPSG), layer; planarizing said BPSG layer; performing a first step, of said two step anisotropic RIE procedure, selectively removing said BPSG layer, and creating a first SAC opening in said BPSG layer, exposing said thin second silicon nitride layer, and exposing said partial silicon nitride spacers; performing a second step, of said two step anisotropic RIE procedure, selectively removing said thin second silicon nitride layer, exposed in said first SAC opening, and creating a second SAC opening, exposing said source/drain region, while forming complete silicon nitride spacers, on the entire sides of said polycide gate structures; and forming SAC structures, contacting said source/drain region, in said second SAC opening.

Claim 16

Dependent Claim 51 words

The method of claim 13, wherein said shallow trench isolation regions are formed by creating a shallow trench, in said semiconductor substrate, via an anisotropic RIE procedure, using Cl 2 as an etchant, and filling the shallow trench with a silicon oxide layer, obtained via an LPCVD or a PECVD procedure.

Claim 17

Dependent Claim 28 words

The method of claim 13, wherein said silicon dioxide gate insulator layer is formed using a thermal oxidation procedure, to a thickness between about 50 to 100 Angstroms.

Claim 18

Dependent Claim 55 words

The method of claim 13, wherein said polycide gate structures are comprised of an overlying tungsten silicide layers, obtained via an LPCVD, or a R.F. sputtering procedure, at a thickness between about 500 to 1000 Angstroms, and an underlying polysilicon layer, obtained using an LPCVD procedure, at a thickness between about 500 to 1000 Angstroms.

Claim 19

Dependent Claim 27 words

The method of claim 13, wherein said first silicon nitride layer is deposited using LPCVD or PECVD procedures, to a thickness between about 1000 to 2500 Angstroms.

Claim 20

Dependent Claim 57 words

The method of claim 13, wherein said polycide gate structures, capped with said first silicon nitride layer, are formed via an anisotropic RIE procedure, using CF 4 --CHF 3 --Ar--O 2 as an etchant for said first silicon nitride layer, while using Cl 2 as an etchant for said tungsten silicide layer, and for said polysilicon layer.

Claim 21

Dependent Claim 39 words

The method of claim 13, wherein said source/drain regions are formed via ion implantation of arsenic or phosphorous ions, at an energy between about 20 to 40 KeV, at a dose between about 1E12 to 1E14 atoms/cm 2 .

Claim 22

Dependent Claim 27 words

The method of claim 13, wherein said second silicon nitride layer is deposited using LPCVD or PECVD procedures, to a thickness between about 400 to 1000 Angstroms.

Claim 23

Dependent Claim 34 words

The method of claim 13, wherein said partial silicon nitride spacers are formed on the top sides of said polycide gate structures, via an anisotropic RIE procedure, using CHF 3 --Ar as an etchant.

Claim 24

Dependent Claim 21 words

The method of claim 13, wherein said thin second silicon nitride layer, has a thickness between about 100 to 200 Angstroms.

Claim 25

Dependent Claim 53 words

The method of claim 13, wherein said BPSG layer is deposited using LPCVD or PECVD procedures, to a thickness between about 5000 to 10000 Angstroms, and comprised of between about 3 to 8 weight % B 2 O 3 , and between about 3 to 10 weight % P 2 O 5 .

Claim 26

Dependent Claim 58 words

The method of claim 13, wherein said first SAC opening, is created in said BPSG layer, via a first step, of said two step anisotropic RIE procedure, using C 4 F 8 --CO--Ar--O 2 as an etchant, with an etch rate ratio of said BPSG layer, to said thin second silicon nitride layer, of about 20 to 1.

Claim 27

Dependent Claim 73 words

The method of claim 13, wherein said second SAC opening, is created in said thin second silicon nitride layer, via a second step, of said two step anisotropic RIE procedure, using CH 2 F 2 --CHF 3 --Ar--O 2 as an etchant, with an etch rate ratio of said thin second silicon nitride layer, to said BPSG layer, or to silicon oxide, in said shallow trench isolation region, of about 20 to 1.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	2003-03-07	2003-09-06	2004-03-07	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2007-03-07	2007-09-06	2008-03-07	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2011-03-07	2011-09-06	2012-03-07	$7700.00	Window Closed / Lapsed

Method of fabricating sidewall spacers for a self-aligned contact hole

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag