Low dielectric loss glasses
Assignee: Lighting Science Group Corp
•
Filing: 1997-06-18
•
Granted: 2000-01-25
•
Expires: 2017-06-18
Abstract
Abstract High magnesium-content magnesium aluminosilicate glasses are used to form green tape compositions that are fired stepwise, i.e., first to about 500 DEG C. to remove organic materials, then to a temperature 10-30 DEG C. above the glass transition temperature for a time sufficient to nucleate the glass, and finally to a higher temperature near but below the softening temperature to complete crystallization of the glass. The resultant glass-ceramic may include substantial amounts of the forsterite crystalline phase. Multilayer ceramic printed circuit boards are made that are useful for high frequency, microwave applications. The fired high magnesium oxide content glasses have low dielectric constant and low dissipation loss factors, and they have a thermal coefficient of expansion that is compatible with metal or ceramic support substrates that impart mechanical strength to the printed circuit boards and that are thermally conductive. The boards are compatible with gallium arsenide devices.
Inventors
- 👤 Ananda Hosakere Kumar
- 👤 Barry Jay Thaler
- 👤 Ashok Narayan Prabhu
- 👤 Ellen Schwartz Tormey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 22:20
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C10/0054; H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12597; Y10T428/12604
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
60 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to 35 percent by weight of magnesium oxide; from about 48-52 percent by weight of silicon oxide, and from 10-25 percent by weight of aluminum oxide, each layer having a circuit pattern thereon, on a copper clad metal or dielectric support substrate.
Claim 2
Dependent Claim
60 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to 35 percent by weight of magnesium oxide; from about 48-52 percent by weight of silicon oxide, and from 10-25 percent by weight of aluminum oxide, each layer having a circuit pattern thereon, on a copper clad metal or dielectric support substrate.
Claim 3
Dependent Claim
68 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to 35 percent by weight of magnesium oxide; from about 48-52 percent by weight of silicon oxide, and from 10-25 percent by weight of aluminum oxide, each layer having a circuit pattern thereon, on a copper clad metal support substrate, wherein said sintered glass further includes a forsterite crystalline phase.
Claim 4
Dependent Claim
68 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to 35 percent by weight of magnesium oxide; from about 48-52 percent by weight of silicon oxide, and from 10-25 percent by weight of aluminum oxide, each layer having a circuit pattern thereon, on a copper clad metal support substrate, wherein said sintered glass further includes a forsterite crystalline phase.
Claim 5
Dependent Claim
29 words
A ceramic multilayer printed circuit board according to claim 1 wherein said support substrate is a ceramic selected from the group consisting of aluminum-nitride, silicon carbide, alumina and diamond.
Claim 6
Dependent Claim
69 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to about 34 percent by weight of magnesium oxide, from about 12-18 percent by weight of barium oxide, from about 5-20 percent by weight of aluminum oxide, from about 20-26 percent by weight of silicon oxide and from about 10-16 percent by weight of boron oxide on a metal support substrate.
Claim 7
Dependent Claim
69 words
A multilayer ceramic circuit board comprising sintered glass layers of a glass comprising at least about 26 up to about 34 percent by weight of magnesium oxide, from about 12-18 percent by weight of barium oxide, from about 5-20 percent by weight of aluminum oxide, from about 20-26 percent by weight of silicon oxide and from about 10-16 percent by weight of boron oxide on a metal support substrate.
Claim 8
Dependent Claim
74 words
A ceramic multilayer printed circuit board according to claim 4 wherein said support substrate is a metal selected from the group consisting of molybdenum, tungsten, an alloy of 53.8 percent by weight of iron, 29 percent by weight of nickel, 17 percent by weight of cobalt and 0.2 percent by weight of manganese, and an alloy of 36 percent by weight of nickel and steel, said steel containing 0.2 percent by weight of carbon.
Claim 9
Dependent Claim
44 words
A multilayer ceramic circuit board according to claim 4 wherein said metal support substrate is of an alloy of 53.8 percent by weight of iron, 29 percent by weight of nickel, 17 percent by weight of cobalt and 0.2 percent by weight of manganese.
References Cited (Backward Citations)
US4256796A
Cited
US4624934A
Cited
US4749665A
Cited
US4764486A
Cited
JPS62278145A
Cited
EP0289222A1
Cited
US4997698A
Cited
US4965229A
Cited
EP0351097A1
Cited
US5099174A
Cited
US5079194A
Cited
US5250474A
Cited
US5216207A
Cited
US5356841A
Cited
US5256469A
Cited
US5277724A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-01-24 | 2003-07-26 | 2004-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-01-24 | 2007-07-26 | 2008-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-01-24 | 2011-07-26 | 2012-01-25 | $7700.00 | Window Closed / Lapsed |