Method of forming dual damascene structure
Assignee: United Microelectronics Corp
•
Filing: 1998-08-20
•
Granted: 1999-12-28
•
Expires: 2018-08-20
Abstract
Abstract A method of forming a dual damascene structure includes providing a substrate having a metallic layer already formed thereon, and then forming a dielectric layer having a top-wide/bottom-narrow opening over the substrate to expose a portion of the metallic layer. Next, the metallic layer is over-etched by applying etchant through the opening to form a groove in the metallic layer so that additional metallic layer surface is exposed. Thereafter, a glue layer is formed over the opening and the groove surface. If the glue layer is a metal, a high-temperature operation is carried out to form a low resistance alloy at the junction between the metallic layer and the glue layer. Consequently, ohmic contact area and reliability of the device are increased. Finally, conventional processes are used to deposit metal into the opening followed by the planarization of the newly deposited metallic layer.
Inventors
- 👤 Tzung-Han Li
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:20
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/049; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10W20/071; H10W20/081; H10W20/083; H10W20/084; H10W20/086
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
134 words
A method of forming a dual damascene structure, the method comprising: providing a substrate; forming a patterned first conductive layer in the substrate; forming a dielectric layer over the substrate and the first conductive layer; forming a top-wide/bottom-narrow opening in the dielectric layer that exposes a portion of the first conductive layer; removing a portion of the exposed first conductive layer at the bottom of the opening to form a groove without forming a hole through the first conductive layer; forming a glue layer over the exposed first conductive layer and the surface of the dielectric layer; and forming a second conductive layer filling the opening and the groove so that the top surface of the second conductive layer is at least at the same height as the top surface of the dielectric layer.
Claim 2
Independent Claim
134 words
A method of forming a dual damascene structure, the method comprising: providing a substrate; forming a patterned first conductive layer in the substrate; forming a dielectric layer over the substrate and the first conductive layer; forming a top-wide/bottom-narrow opening in the dielectric layer that exposes a portion of the first conductive layer; removing a portion of the exposed first conductive layer at the bottom of the opening to form a groove without forming a hole through the first conductive layer; forming a glue layer over the exposed first conductive layer and the surface of the dielectric layer; and forming a second conductive layer filling the opening and the groove so that the top surface of the second conductive layer is at least at the same height as the top surface of the dielectric layer.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein the step of forming the first conductive layer includes depositing metallic material.
Claim 4
Dependent Claim
18 words
The method of claim 1, wherein the step of forming the second conductive layer includes depositing metallic material.
Claim 5
Dependent Claim
27 words
The method of claim 1, wherein the groove in the first conductive layer provides a larger than conventional surface area for contact with the second conductive layer.
Claim 6
Dependent Claim
84 words
The method of claim 1, wherein the step of forming a second conductive layer filling the opening and the groove further includes the substeps of: forming a second conductive layer over the substrate that extends over the top surface of the dielectric layer; and using a chemical-mechanical polishing method to remove the second conductive layer above the dielectric layer so that the top surface of the second conductive layer is at least at the same height as the top surface of the dielectric layer.
Claim 7
Independent Claim
145 words
A method of forming a dual damascene structure, the method comprising the steps of: providing a substrate; forming a patterned first metallic layer in the substrate; forming a dielectric layer over the substrate and the first metallic layer; forming a top-wide/bottom-narrow opening in the dielectric layer the exposes a portion of the first metallic layer; removing a portion of the exposed first metallic layer at the bottom of the opening to form a groove without forming a hole through the first metallic layer; forming a glue layer at least covering the exposed first metallic layer and the interior surface of the opening; performing a high-temperature processing operation; and forming a second metallic layer filling the opening and the groove so that the top surface of the second metallic layer is at least at the same height level as the top surface of the dielectric layer.
Claim 8
Independent Claim
145 words
A method of forming a dual damascene structure, the method comprising the steps of: providing a substrate; forming a patterned first metallic layer in the substrate; forming a dielectric layer over the substrate and the first metallic layer; forming a top-wide/bottom-narrow opening in the dielectric layer the exposes a portion of the first metallic layer; removing a portion of the exposed first metallic layer at the bottom of the opening to form a groove without forming a hole through the first metallic layer; forming a glue layer at least covering the exposed first metallic layer and the interior surface of the opening; performing a high-temperature processing operation; and forming a second metallic layer filling the opening and the groove so that the top surface of the second metallic layer is at least at the same height level as the top surface of the dielectric layer.
Claim 9
Dependent Claim
27 words
The method of claim 6, wherein the groove in the first metallic layer provides a larger than conventional surface area for contact with the second metallic layer.
Claim 10
Dependent Claim
41 words
The method of claim 6, wherein the step of performing the high-temperature processing is to allow the glue layer and the first metallic layer to react, forming an improved ohmic contact between the second metallic layer and the first metallic layer.
Claim 11
Dependent Claim
17 words
The method of claim 6, wherein the step of forming the glue layer includes depositing metallic material.
Claim 12
Dependent Claim
19 words
The method of claim 6, wherein the step of performing the high-temperature processing operation includes a rapid thermal processing.
Claim 13
Dependent Claim
18 words
The method of claim 6, wherein the step of performing the high-temperature processing operation includes an annealing operation.
Claim 14
Dependent Claim
84 words
The method of claim 6, wherein the step of forming a second metallic layer filling the opening and the groove further includes the substeps of: forming a second metallic layer over the substrate that extends over the top surface of the dielectric layer; and using a chemical-mechanical polishing method to remove the second metallic layer above the dielectric layer so that the top surface of the second metallic layer is at least at the same height as the top surface of the dielectric layer.
Claim 15
Dependent Claim
17 words
The method of claim 6, wherein the step of forming the second metallic layer includes depositing copper.
References Cited (Backward Citations)
US5753967A
Cited
US5900672A
Cited
US5918150A
Cited
US5916011A
Cited
US5939334A
Cited
US5935762A
Cited
US5939788A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-12-27 | 2003-06-28 | 2003-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-12-27 | 2007-06-28 | 2007-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-12-27 | 2011-06-28 | 2011-12-28 | $7700.00 | Window Closed / Lapsed |