Modified recessed locos isolation process for deep sub-micron device processes
Assignee: National Semiconductor Corp
•
Filing: 1998-03-20
•
Granted: 1999-12-07
•
Expires: 2018-03-20
Abstract
Abstract A trench is etched in a silicon substrate covered with an oxide/nitride stack and a field oxide layer is then grown through oxidation of the silicon in the substrate such that the trench is partly filled. There is reduced oxide encroachment into the active areas under the nitride layer because of the partial field oxide growth. Double oxide layers are deposited over the surface of the field oxide layer and the oxide/nitride stack such that the oxide layers fill the remainder of the trench and produce a nearly planar topology. The double oxide layers are then etched back to the nitride layer through chemical mechanical polishing, leaving the field isolation region. After stripping the oxide/nitride stack, a gate oxide layer is grown. A minimal amount of oxide is required to fill the trench because the trench is already almost filled with the field oxide layer and because of the shallow depth of the trench. Consequently, the etch back step causes minimal dishing. Further, the field oxide layer rounds the corner between the trench and the active area, obviating the need for a thin oxide liner in the trench.
Inventors
- 👤 Albert Bergemont
- 👤 Alexander H. Owens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:54
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/0124; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/05
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
129 words
A method of introducing an isolation region within a substrate, said method comprising: providing a substrate; etching a recessed trench in said substrate; growing a field oxide layer in said recessed trench, wherein said field oxide is grown to a thickness of not less than 2500 Å, and wherein said field oxide layer does not completely fill said recessed trench; depositing an oxide layer over the surface of said field oxide layer to completely fill said recessed trench, wherein said step of depositing an oxide layer over the surface of said field oxide layer further comprises: depositing a first oxide layer over said field oxide layer; and depositing a second oxide layer over said first oxide layer; and etching back said oxide layer to produce an approximately planar surface.
Claim 2
Independent Claim
129 words
A method of introducing an isolation region within a substrate, said method comprising: providing a substrate; etching a recessed trench in said substrate; growing a field oxide layer in said recessed trench, wherein said field oxide is grown to a thickness of not less than 2500 Å, and wherein said field oxide layer does not completely fill said recessed trench; depositing an oxide layer over the surface of said field oxide layer to completely fill said recessed trench, wherein said step of depositing an oxide layer over the surface of said field oxide layer further comprises: depositing a first oxide layer over said field oxide layer; and depositing a second oxide layer over said first oxide layer; and etching back said oxide layer to produce an approximately planar surface.
Claim 3
Dependent Claim
75 words
The method of claim 1, wherein said providing a substrate further comprises: providing a pad oxide layer over the surface of said substrate; providing a nitride layer over the surface of said pad oxide layer; providing a photoresist mask over the surface of said nitride layer, said photoresist mask exposing only the areas where it is desired to grow field oxide; and etching through said nitride layer and said pad oxide layer to said substrate.
Claim 4
Dependent Claim
35 words
The method of claim 2, further comprising: etching back said nitride layer and said pad oxide layer to said surface of said substrate; and growing a gate oxide layer over the surface of said substrate.
Claim 5
Dependent Claim
22 words
The method of claim 1, wherein growing a field oxide layer in said recessed trench is comprised of oxidation of said substrate.
Claim 6
Dependent Claim
16 words
The method of claim 1, wherein said first oxide is comprised of a high density plasma.
Claim 7
Dependent Claim
14 words
The method of claim 1, wherein the second oxide layer is comprised of TEOS.
Claim 8
Dependent Claim
16 words
The method of claim 1, wherein etching back said oxide layer comprises a chemical mechanical polishing.
Claim 9
Independent Claim
182 words
A method of introducing an isolation region within a substrate, said method comprising: providing an oxide layer above the surface of a substrate, wherein said oxide layer leaves said substrate surface exposed where an isolation region is desired; providing a nitride layer above the surface of said oxide layer, wherein said nitride layer leaves said substrate surface exposed where said isolation region is desired; etching a recessed region into said substrate where said isolation region is desired; providing a field oxide layer in said recessed region, wherein said field oxide layer is grown from silicon in said substrate, and wherein said field oxide layer does not completely fill said recessed region; providing an oxide layer over the surface of said field oxide layer, wherein said oxide layer fills in said recessed region, wherein said step of providing an oxide layer over the surface of said field oxide layer comprises: depositing a first oxide layer over said field oxide layer; and depositing a second oxide layer over said first oxide layer; and etching back said oxide layer to produce an approximately planar surface.
Claim 10
Independent Claim
182 words
A method of introducing an isolation region within a substrate, said method comprising: providing an oxide layer above the surface of a substrate, wherein said oxide layer leaves said substrate surface exposed where an isolation region is desired; providing a nitride layer above the surface of said oxide layer, wherein said nitride layer leaves said substrate surface exposed where said isolation region is desired; etching a recessed region into said substrate where said isolation region is desired; providing a field oxide layer in said recessed region, wherein said field oxide layer is grown from silicon in said substrate, and wherein said field oxide layer does not completely fill said recessed region; providing an oxide layer over the surface of said field oxide layer, wherein said oxide layer fills in said recessed region, wherein said step of providing an oxide layer over the surface of said field oxide layer comprises: depositing a first oxide layer over said field oxide layer; and depositing a second oxide layer over said first oxide layer; and etching back said oxide layer to produce an approximately planar surface.
Claim 11
Dependent Claim
21 words
The method of claim 8, wherein said field oxide layer is grown to a thickness of not less than 2500 Å.
Claim 12
Dependent Claim
89 words
The method of claim 8, wherein providing an oxide layer and providing a nitride layer further comprises: providing a photoresist masking layer over the surface of said nitride layer, said photoresist masking layer patterned to expose only the area of said nitride layer where an isolation region is desired; etching through said nitride layer to expose only the area of said oxide layer where an isolation region is desired; and etching through said oxide layer to expose only the area of said substrate where an isolation region is desired.
Claim 13
Dependent Claim
17 words
The method of claim 8, wherein said first oxide layer is comprised of a high density plasma.
Claim 14
Dependent Claim
14 words
The method of claim 8, wherein the second oxide layer is comprised of TEOS.
Claim 15
Dependent Claim
15 words
The method of claim 8, wherein etching back said oxide layer comprises chemical mechanical polishing.
Claim 16
Independent Claim
175 words
A method of introducing an isolation region within a substrate, said method comprising: providing an oxide layer above the surface of a substrate, wherein said oxide layer leaves said substrate surface exposed where an isolation region is desired; providing a nitride layer above the surface of said oxide layer, wherein said nitride layer leaves said substrate surface exposed where said isolation region is desired; etching a recessed region into said substrate where said isolation region is desired wherein said walls and bottom of said recessed region are exposed silicon; providing a field oxide layer in said recessed region, said field oxide layer is grown from said exposed silicon in said walls and bottom of said recessed region, and wherein said field oxide layer does not completely fill said recessed region; providing an oxide layer over and in direct contact with the surface of said field oxide layer and the surface of said nitride layer, wherein said oxide layer fills in said recessed region; and etching back said oxide layer to produce an approximately planar surface.
Claim 17
Independent Claim
175 words
A method of introducing an isolation region within a substrate, said method comprising: providing an oxide layer above the surface of a substrate, wherein said oxide layer leaves said substrate surface exposed where an isolation region is desired; providing a nitride layer above the surface of said oxide layer, wherein said nitride layer leaves said substrate surface exposed where said isolation region is desired; etching a recessed region into said substrate where said isolation region is desired wherein said walls and bottom of said recessed region are exposed silicon; providing a field oxide layer in said recessed region, said field oxide layer is grown from said exposed silicon in said walls and bottom of said recessed region, and wherein said field oxide layer does not completely fill said recessed region; providing an oxide layer over and in direct contact with the surface of said field oxide layer and the surface of said nitride layer, wherein said oxide layer fills in said recessed region; and etching back said oxide layer to produce an approximately planar surface.
Claim 18
Dependent Claim
89 words
The method of claim 14, wherein providing an oxide layer and providing a nitride layer further comprises: providing a photoresist masking layer over the surface of said nitride layer, said photoresist masking layer patterned to expose only the area of said nitride layer where an isolation region is desired; etching through said nitride layer to expose only the area of said oxide layer where an isolation region is desired; and etching through said oxide layer to expose only the area of said substrate where an isolation region is desired.
Claim 19
Dependent Claim
40 words
The method of claim 14, wherein providing an oxide layer over the surface of said field oxide layer comprises: depositing a first oxide layer over said field oxide layer; and depositing a second oxide layer over said first oxide layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-12-06 | 2003-06-07 | 2003-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-12-06 | 2007-06-07 | 2007-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-12-06 | 2011-06-07 | 2011-12-07 | $7700.00 | Window Closed / Lapsed |