Method of forming a crystalline phase material
Assignee: Micron Technology Inc
•
Filing: 1996-11-14
•
Granted: 1999-12-07
•
Expires: 2016-11-14
Abstract
Abstract A method of forming a crystalline phase material includes, a) providing a stress inducing material within or operatively adjacent a crystalline material of a first crystalline phase; and b) annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase. The stress inducing material preferably induces compressive stress within the first crystalline phase during the anneal to the second crystalline phase to lower the required activation energy to produce a more dense second crystalline phase. Example compressive stress inducing layers include SiO 2 and Si 3 N 4 , while example stress inducing materials for providing into layers are Ge, W and Co. Where the compressive stress inducing material is provided on the same side of a wafer over which the crystalline phase material is provided, it is provided to have a thermal coefficient of expansion which is less than the first phase crystalline material. Where the compressive stress inducing material is provided on the opposite side of a wafer over which the crystalline phase material is provided, it is provided to have a thermal coefficient of expansion which is greater than the first phase crystalline material. Example and preferred crystalline phase materials having two phases are refractory metal silicides, such as TiSi x .
Inventors
- 👤 Gurtej S. Sandhu
- 👤 Sujit Sharan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:28
CPC Classifications
C; C30; C30B; C30B1/00; C30B1/02; C30B29/00; C30B29/10; C30B29/34; H; H10; H10D; H10D30/00; H10D30/60; H10D30/791; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/01312; H10D64/01354; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10P14/40; H10P14/412; H10P14/414
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
44 words
A method of forming a crystalline phase material comprising: providing a stress inducing material within a crystalline material of a first crystalline phase; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 2
Independent Claim
44 words
A method of forming a crystalline phase material comprising: providing a stress inducing material within a crystalline material of a first crystalline phase; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 3
Dependent Claim
18 words
The method of claim 1 comprising ion implanting the stress inducing material into the first crystalline phase material.
Claim 4
Dependent Claim
27 words
The method of claim 1 comprising in situ providing the stress inducing material into the first crystalline phase material during deposition of the first crystalline phase material.
Claim 5
Dependent Claim
27 words
The method of claim 1 comprising providing stress inducing atoms within the first crystalline phase material to a concentration from 10 16 -10 22 atoms/cm 3 .
Claim 6
Independent Claim
80 words
A method of forming a crystalline phase material comprising: providing a stress inducing material operatively adjacent a crystalline material of a first crystalline phase, the stress inducing material having a first thermal coefficient of expansion, the crystalline material of the first crystalline phase having a second thermal coefficient of expansion, the first coefficient being less than the second coefficient; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 7
Independent Claim
80 words
A method of forming a crystalline phase material comprising: providing a stress inducing material operatively adjacent a crystalline material of a first crystalline phase, the stress inducing material having a first thermal coefficient of expansion, the crystalline material of the first crystalline phase having a second thermal coefficient of expansion, the first coefficient being less than the second coefficient; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 8
Dependent Claim
17 words
The method of claim 5 comprising providing the stress inducing material over the first crystalline phase material.
Claim 9
Dependent Claim
17 words
The method of claim 5 comprising providing the stress inducing material under the first crystalline phase material.
Claim 10
Dependent Claim
29 words
The method of claim 5 comprising providing the stress inducing material to a thickness which is equal to or greater than a thickness of the first phase crystalline material.
Claim 11
Dependent Claim
21 words
The method of claim 5 comprising providing the stress inducing material over and in contact with the first crystalline phase material.
Claim 12
Dependent Claim
21 words
The method of claim 5 comprising providing the stress inducing material under and in contact with the first crystalline phase material.
Claim 13
Dependent Claim
14 words
The method of claim 5 wherein the stress inducing material comprises SiO 2 .
Claim 14
Dependent Claim
16 words
The method of claim 5 wherein the stress inducing material comprises Si 3 N 4 .
Claim 15
Dependent Claim
15 words
The method of claim 5 wherein the stress inducing material is provided before said annealing.
Claim 16
Independent Claim
103 words
A method of forming a crystalline phase material comprising: providing a semiconductor wafer having opposing first and second sides; forming a crystalline material of a first crystalline phase over the first side of the wafer; forming a stress inducing material over the second side of the wafer, the stress inducing material having a first thermal coefficient of expansion, the crystalline material of the first crystalline phase having a second thermal coefficient of expansion, the first coefficient being greater than the second coefficient; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 17
Independent Claim
103 words
A method of forming a crystalline phase material comprising: providing a semiconductor wafer having opposing first and second sides; forming a crystalline material of a first crystalline phase over the first side of the wafer; forming a stress inducing material over the second side of the wafer, the stress inducing material having a first thermal coefficient of expansion, the crystalline material of the first crystalline phase having a second thermal coefficient of expansion, the first coefficient being greater than the second coefficient; and annealing the crystalline material of the first crystalline phase under conditions effective to transform it to a second crystalline phase.
Claim 18
Dependent Claim
18 words
The method of claim 14 comprising forming the stress inducing material on the second side of the wafer.
Claim 19
Dependent Claim
21 words
The method of claim 14 wherein the crystalline material comprises a refractory metal silicide, and the stress inducing material comprises TiN.
Claim 20
Dependent Claim
32 words
The method of claim 14 wherein the crystalline material comprises TiSi x , the first crystalline phase is C49, the second crystalline phase is C54, and the stress inducing material comprises TiN.
Claim 21
Dependent Claim
26 words
The method of claim 14 wherein the crystalline material comprises TiSi x , the first crystalline phase is C49, and the second crystalline phase is C54.
Claim 22
Dependent Claim
15 words
The method of claim 14 wherein the stress inducing material is provided before said annealing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-12-06 | 2003-06-07 | 2003-12-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-12-06 | 2007-06-07 | 2007-12-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-12-06 | 2011-06-07 | 2011-12-07 | $7700.00 | Window Closed / Lapsed |