Prepreg, and a fiber reinforced composite material
Assignee: Toray Industries Inc
•
Filing: 1995-12-04
•
Granted: 1999-11-16
•
Expires: 2015-12-04
Abstract
Abstract A prepreg comprising (a) reinforcing fibers and (b) a matrix resin which comprises specific epoxy resin composition, a curing agent with a specific structure and a highly heat resistant thermoplastic resin, the cured product of which has a low water absorption. An interlayer toughened prepreg containing reinforcing fibers and a matrix resin comprising a specific epoxy resin composition, a hardening agent with a specific structure and a highly heat resistant thermoplastic resin is also provided. In addition, a cured product can be obtained by curing any of the above prepregs, which product satisfies both impact resistance (residual compressive strength after impact) and heat and wet property (compressive strength of notched coupon at high temperature and high humidity) at high levels, even though these properties have been in contradictory relation in the conventional techniques.
Inventors
- 👤 Hiroki Oosedo
- 👤 Atsushi Ozaki
- 👤 Hideo Nagata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:38
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/32; C08G59/3227; C08G59/38; C08G59/40; C08G59/50; C08G59/5033; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/243; C08L; C08L63/00; C08J2363/00; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/25; Y10T428/254; Y10T428/31504; Y10T428/31511; Y10T428/31721; Y10T428/31725; Y10T428/31728; Y10T428/31786; Y10T428/31942
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
126 words
A prepreg comprising reinforcing fibers and a matrix resin, said matrix resin comprising: (a) an epoxy resin composition (A) of which 80 wt % or more is tetraglycidyldiaminodiphenylmethane, (b) a diamine compound (B) having 1 to 3 phenyl groups in its skeleton, at least one of said phenyl groups having a bonded group at a meta position, said bonded group comprising an amino group wherein said diamine compound (B) is 3,3'-diaminodiphenylsulfone, and (c) a film, particles, fibers or composites of said film, particles or fibers of a thermoplastic resin (D), wherein 90 wt % or more of the thermoplastic resin (D) is localized in an area from a surface of the prepreg to a depth from said surface of 15% of a thickness of the prepreg.
Claim 2
Dependent Claim
126 words
A prepreg comprising reinforcing fibers and a matrix resin, said matrix resin comprising: (a) an epoxy resin composition (A) of which 80 wt % or more is tetraglycidyldiaminodiphenylmethane, (b) a diamine compound (B) having 1 to 3 phenyl groups in its skeleton, at least one of said phenyl groups having a bonded group at a meta position, said bonded group comprising an amino group wherein said diamine compound (B) is 3,3'-diaminodiphenylsulfone, and (c) a film, particles, fibers or composites of said film, particles or fibers of a thermoplastic resin (D), wherein 90 wt % or more of the thermoplastic resin (D) is localized in an area from a surface of the prepreg to a depth from said surface of 15% of a thickness of the prepreg.
Claim 3
Dependent Claim
25 words
A prepreg according to claim 1, said matrix resin further comprising a thermoplastic resin (C) having a glass transition temperature of 180° C. or higher.
Claim 4
Dependent Claim
30 words
A prepreg according to claim 1, wherein the molar ratio of said diamine compound (B) to the epoxy groups in said epoxy resin composition (A) is from 0.15 to 0.2.
Claim 5
Dependent Claim
47 words
A prepreg according to claim 1, wherein 90 wt % or more of said 3,3'-diaminodiphenylsulfone is in the form of powder particles of 40 μm or less in particle diameter, 1 wt % or less of said powder particles being 1 μm or less in particle diameter.
Claim 6
Dependent Claim
43 words
A prepreg according to claim 1, wherein said 3,3'-diaminodiphenylsulfone is in the form of powder particles of 15 μm or less in median particle diameter and 2.0 or less in σg value calculated from the following equation: σg=[(Mean particle diameter+Standard deviation)/(Mean particle diameter)].
Claim 7
Dependent Claim
26 words
A prepreg according to claim 2, wherein the thermoplastic resin (C) is a resin selected from the group consisting of polysulfones, polyimides, polyketones and aromatic polyesters.
Claim 8
Dependent Claim
21 words
A prepreg according to claim 2, wherein the thermoplastic resin (C) is a polysulfone with ether bonds in the main chain.
Claim 9
Dependent Claim
21 words
A prepreg according to claim 2, wherein the thermoplastic resin (C) is a polyimide with ether bonds in the main chain.
Claim 10
Dependent Claim
32 words
A prepreg according to claim 2, wherein the thermoplastic resin (C) is present in an amount of 1 to 15 wt %, based on the weight of the epoxy resin composition (A).
Claim 11
Dependent Claim
19 words
A prepreg according to claim 2, wherein the thermoplastic resin (C) is soluble in the epoxy resin composition (A).
Claim 12
Dependent Claim
30 words
A prepreg according to claim 1, wherein the reinforcing fibers are fibers selected from the group consisting of carbon fibers, graphite fibers, boron fibers, tungsten carbide fibers and glass fibers.
Claim 13
Dependent Claim
33 words
A prepreg according to claim 11, wherein the carbon fibers are high strength and high elongation carbon fibers of 4.4 GPa or more in tensile strength and 1.7% or more in tensile elongation.
Claim 14
Dependent Claim
29 words
A prepreg according to claim 1, wherein the thermoplastic resin (D) is a resin selected from the group consisting of polyamides, polyimides, polysulfones, polyether sulfones, polyamidimides and polyether imides.
Claim 15
Dependent Claim
25 words
A prepreg according to claim 1, wherein the thermoplastic resin (D) in the prepreg is particles of 30 μm or less in median particle diameter.
Claim 16
Dependent Claim
112 words
A prepreg comprising reinforcing fibers and a matrix resin, said matrix resin comprising: (a) an epoxy resin composition of which 80 wt % or more is tetraglycidyldiaminodiphenylmethane, (b) a diamine compound (B) having 1 to 3 phenyl groups in its skeleton, at least one of said phenyl groups having a bonded group at a meta position, said bonded group comprising an amino group wherein said diamine compound (B) is 3,3'-diaminodiphenylsulfone, and (c) a semi-interpenetrating polymer network comprising particles, wherein 90 wt % or more of the particles are localized in an area from a surface of the prepreg to a depth from said surface of 15% of a thickness of the prepreg.
Claim 17
Dependent Claim
112 words
A prepreg comprising reinforcing fibers and a matrix resin, said matrix resin comprising: (a) an epoxy resin composition of which 80 wt % or more is tetraglycidyldiaminodiphenylmethane, (b) a diamine compound (B) having 1 to 3 phenyl groups in its skeleton, at least one of said phenyl groups having a bonded group at a meta position, said bonded group comprising an amino group wherein said diamine compound (B) is 3,3'-diaminodiphenylsulfone, and (c) a semi-interpenetrating polymer network comprising particles, wherein 90 wt % or more of the particles are localized in an area from a surface of the prepreg to a depth from said surface of 15% of a thickness of the prepreg.
Claim 18
Dependent Claim
25 words
A prepreg according to claim 15, said matrix resin further comprising a thermoplastic resin (C) having a glass transition temperature of 180° C. or higher.
Claim 19
Dependent Claim
19 words
A prepreg according to claim 15, wherein the semi-interpenetrating polymer network comprises a thermosetting resin and a thermoplastic resin.
Claim 20
Dependent Claim
22 words
A prepreg according to claim 17, wherein the semi-interpenetrating polymer network comprises an epoxy resin or a bismaleimide resin and a polyamide.
Claim 21
Dependent Claim
158 words
A composite material obtained from the prepreg of claim 1, having a compressive strength of 275 MPa or more, said compressive strength being measured by a test carried out in the following manner: (a) laminating 16 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 305 mm in 0° direction and 38 mm in 90° direction; (d) drilling a hole of 6.35 mm at the center of said rectangular coupon to produce a notched rectangular coupon; (e) drying said notched rectangular coupon at 120° C. for 24 hours to produce a dry sample; (f) immersing said dry sample in 71° C. water for 2 weeks to produce a water absorbed sample; and (g) measuring the compression strength of said water absorbed sample at 82° C.
Claim 22
Dependent Claim
158 words
A composite material obtained from the prepreg of claim 2, having a compressive strength of 275 MPa or more, said compressive strength being measured by a test carried out in the following manner: (a) laminating 16 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 305 mm in 0° direction and 38 mm in 90° direction; (d) drilling a hole of 6.35 mm at the center of said rectangular coupon to produce a notched rectangular coupon; (e) drying said notched rectangular coupon at 120° C. for 24 hours to produce a dry sample; (f) immersing said dry sample in 71° C. water for 2 weeks to produce a water absorbed sample; and (g) measuring the compression strength of said water absorbed sample at 82° C.
Claim 23
Dependent Claim
158 words
A composite material obtained from the prepreg of claim 15, having a compressive strength of 275 MPa or more, said compressive strength being measured by a test carried out in the following manner: (a) laminating 16 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 305 mm in 0° direction and 38 mm in 90° direction; (d) drilling a hole of 6.35 mm at the center of said rectangular coupon to produce a notched rectangular coupon; (e) drying said notched rectangular coupon at 120° C. for 24 hours to produce a dry sample; (f) immersing said dry sample in 71° C. water for 2 weeks to produce a water absorbed sample; and (g) measuring the compression strength of said water absorbed sample at 82° C.
Claim 24
Dependent Claim
118 words
A composite material obtained from the prepreg of claim 1, having a residual-compressive-strength-after-impact of 275 MPa or more, said residual-compressive-strength-after-impact being measured by a test carried out in the following manner: (a) laminating 24 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 152.4 mm in 0° direction and 101.6 mm in 90° direction; (d) providing a drop impact of 30.5 N at the center of said rectangular coupon to produce an impacted test piece; and (e) measuring the residual-compressive-strength-after-impact of said impacted test piece.
Claim 25
Dependent Claim
118 words
A composite material obtained from the prepreg of claim 2, having a residual-compressive-strength-after-impact of 275 MPa or more, said residual-compressive-strength-after-impact being measured by a test carried out in the following manner: (a) laminating 24 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 152.4 mm in 0° direction and 101.6 mm in 90° direction; (d) providing a drop impact of 30.5 N at the center of said rectangular coupon to produce an impacted test piece; and (e) measuring the residual-compressive-strength-after-impact of said impacted test piece.
Claim 26
Dependent Claim
118 words
A composite material obtained from the prepreg of claim 15, having a residual-compressive-strength-after-impact of 275 MPa or more, said residual-compressive-strength-after-impact being measured by a test carried out in the following manner: (a) laminating 24 sheets of the prepreg to form a quasi-isotropic laminate; (b) curing said quasi-isotropic laminate at 180° C. under a pressure of 0.588 MPa for 2 hours to produce a cured laminate; (c) cutting said cured laminate to produce a rectangular coupon of 152.4 mm in 0° direction and 101.6 mm in 90° direction; (d) providing a drop impact of 30.5 N at the center of said rectangular coupon to produce an impacted test piece; and (e) measuring the residual-compressive-strength-after-impact of said impacted test piece.
Claim 27
Dependent Claim
44 words
A composite material obtained by curing a laminate of sheets of prepreg according to claim 1, 2, 15, or 16, having a percentage of water absorption of 1% or less following curing and immersion in 71° C. water for 2 weeks of said prepreg.
References Cited (Backward Citations)
US3472730A
Cited
GB1299177A
Cited
US4661559A
Cited
US4517321A
Cited
US4579885A
Cited
US4604319B1
Cited
US4604319A
Cited
JPS6229316A
Cited
JPS62297312A
Cited
US4863787A
Cited
US5028478A
Cited
US4868050A
Cited
JPH01104624A
Cited
US4874661A
Cited
US4992325A
Cited
US5025045A
Cited
US4956411A
Cited
US4908088A
Cited
US5169710A
Cited
EP0351028A2
Cited
EP0351026A2
Cited
EP0351025A2
Cited
EP0351027A2
Cited
US5242748A
Cited
US4954195A
Cited
US5248711A
Cited
US5037689A
Cited
US5087657A
Cited
US5057353A
Cited
EP0486044A2
Cited
US5334662A
Cited
JPH0778138A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-11-15 | 2003-05-17 | 2003-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-11-15 | 2007-05-17 | 2007-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-11-15 | 2011-05-17 | 2011-11-16 | $7700.00 | Window Closed / Lapsed |