Process for copper etch back
Assignee: Applied Materials Inc
•
Filing: 1998-03-13
•
Granted: 1999-10-19
•
Expires: 2018-03-13
Abstract
Abstract In the preparation of semiconductor structures having multilevel copper conductive features which must be interconnected, it is frequently desired to remove portions of a copper layer deposited over a substrate. In particular, where lines and contacts are created by depositing a copper layer to fill trenches and vias present in a dielectric layer, it is desired to remove the portion of the copper layer which does not form the desired line or contact. The present invention provides a method of etching a copper layer (film) to remove the portion of the film which is not part of the desired conductive interconnect structure, while avoiding over etching of the structure and the formation of corrosive surface contaminants on the surface of the etched copper. The method of etching is referred to as the etchback process, since, in a typical fabrication process, the deposited copper layer is etched back to the upper or "field" surface of a substrate containing trenches and vias which are filled by the copper. The copper layer etchback may be conducted on a substrate surface using a low temperature regime, below about 150° C. Within this low temperature regime, the etchback is preferably conducted using essentially physical bombardment of the copper surface. Or, the etchback may be carried out with the substrate surface at a temperature which falls within a high temperature regime, above about 150° C. Within this high temperature regime, three different etch chemistries may be used. The etch plasma may be formed solely from non-reactive gases; the etch plasma may be formed solely from gases which are produce a reactive species (such as a gas which is a source of chlorine or fluorine), or, the etch plasma may be formed from a combination of non-reactive and reactive gases which are tailored to adjust selectivity and etch rate. When the gas is a source of chlorine or fluorine, it is preferred that the gas be a compound comprising at least one other element in combination with chlorine or fluorine.
Inventors
- 👤 Yan Ye
- 👤 Diana Xiaobing Ma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:12
CPC Classifications
C; C23; C23F; C23F4/00; H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/062
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
118 words
A method useful in the etchback of copper interconnect layers at temperatures below about 150° C., said method comprising the steps of: a) supplying to a plasma etch process chamber at least one gas, which gas is chemically non-reactive with copper; b) creating a plasma from said at least one gas in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from said plasma toward a substrate surface comprising a layer of copper by applying an offset bias to said substrate; and d) removing at least portions of said copper layer deposited on said substrate surface while maintaining a portion of said copper layer interior of said substrate surface.
Claim 2
Independent Claim
118 words
A method useful in the etchback of copper interconnect layers at temperatures below about 150° C., said method comprising the steps of: a) supplying to a plasma etch process chamber at least one gas, which gas is chemically non-reactive with copper; b) creating a plasma from said at least one gas in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from said plasma toward a substrate surface comprising a layer of copper by applying an offset bias to said substrate; and d) removing at least portions of said copper layer deposited on said substrate surface while maintaining a portion of said copper layer interior of said substrate surface.
Claim 3
Dependent Claim
27 words
The method of claim 1, wherein said plasma created in step b) is sufficient to enable a copper etch rate of at least 1,000 Å per minute.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein said substrate temperature is about 80° C. or less.
Claim 5
Independent Claim
144 words
A method useful in the etchback of copper interconnect layers at temperatures higher than about 150° C., said method comprising the steps of: a) supplying to a plasma etch process chamber at least one gas, which gas is selected to provide the desired copper etch rate and selectivity for copper over adjacent substrate materials, while avoiding or reducing corrosion of the etched copper surface; b) creating a plasma from said gases described in step a) in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from the plasma toward a substrate surface which comprises a layer of copper, by applying an offset bias to said substrate; and d) removing at least a portion of said copper layer deposited on said substrate surface while maintaining a portion of said copper layer interior of said substrate surface.
Claim 6
Independent Claim
144 words
A method useful in the etchback of copper interconnect layers at temperatures higher than about 150° C., said method comprising the steps of: a) supplying to a plasma etch process chamber at least one gas, which gas is selected to provide the desired copper etch rate and selectivity for copper over adjacent substrate materials, while avoiding or reducing corrosion of the etched copper surface; b) creating a plasma from said gases described in step a) in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from the plasma toward a substrate surface which comprises a layer of copper, by applying an offset bias to said substrate; and d) removing at least a portion of said copper layer deposited on said substrate surface while maintaining a portion of said copper layer interior of said substrate surface.
Claim 7
Dependent Claim
27 words
The method of claim 4, wherein said plasma created in step b) is sufficient to enable a copper etch rate of at least 1,000 Å per minute.
Claim 8
Dependent Claim
15 words
The method of claim 4, wherein said at least one gas is a non-reactive gas.
Claim 9
Dependent Claim
23 words
The method of claim 4, wherein said at least one gas is a reactive gas which provides a species which reacts with copper.
Claim 10
Dependent Claim
20 words
The method of claim 4, wherein said at least one gas includes both a non-reactive gas and a reactive gas.
Claim 11
Dependent Claim
20 words
The method of claim 4, wherein the substrate temperature ranges from higher than about 150° C. to about 400° C.
Claim 12
Dependent Claim
29 words
The method of claim 4 or claim 5, including an additional step e) removing at a portion of a barrier layer exposed by the removal of said copper layer.
Claim 13
Dependent Claim
16 words
The method of claim 4, wherein said substrate is silicon dioxide or a low K dielectric.
Claim 14
Dependent Claim
16 words
The method of claim 10, wherein said substrate is silicon dioxide or a low K dielectric.
Claim 15
Dependent Claim
95 words
The method of claim 4, or claim 5, or claim 6, or claim 7, or claim 8, or claim 9, wherein said first portion of said copper layer is removed using a first at least one plasma source gas designed for rapid removal of a copper layer, while a second portion of said copper layer is removed using a second at least one gas designed for a less rapid removal of said copper layer, to selectively remove copper more rapidly than adjacent substrate and barrier materials, and to reduce corrosion of an etched copper surface.
Claim 16
Dependent Claim
22 words
The method of claim 4 or claim 5, including an additional step for removal of corrosive materials from an etched copper surface.
Claim 17
Dependent Claim
19 words
The method of claim 13, including an additional step for removal of corrosive materials from an etched copper surface.
Claim 18
Dependent Claim
42 words
The method of claim 4 or claim 5 or claim 7, wherein said at least one gas which is chemically reactive with copper is selected from the group consisting of HCl, HBr, HI, BCl 3 , SiCl 4 , and combinations thereof.
Claim 19
Dependent Claim
36 words
The method of claim 4 or claim 5 or claim 7, wherein said at least one gas which is chemically reactive with copper is selected from the group consisting of HCl, HBr, HI, and combinations thereof.
Claim 20
Independent Claim
182 words
A method useful in the etchback of copper interconnect layers comprising the steps of: a) supplying to a plasma etch process chamber at least one gas which gas is chemically non-reactive with copper and at least one gas which is chemically reactive with copper; b) creating a plasma from the gases described in step a) in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from the plasma toward the substrate surface by applying an offset bias to the substrate; and d) removing a first portion of a copper layer overlying said substrate surface while maintaining a second portion of said copper layer overlying said substrate surface and while a portion of said copper layer interior of said substrate surface; e) removing said second portion of said copper layer overlying said substrate surface while maintaining a portion of said copper layer interior of said substrate surface; and f) removing a barrier layer overlying said substrate surface while maintaining the portion of said copper layer and said barrier layer interior of the substrate surface.
Claim 21
Independent Claim
182 words
A method useful in the etchback of copper interconnect layers comprising the steps of: a) supplying to a plasma etch process chamber at least one gas which gas is chemically non-reactive with copper and at least one gas which is chemically reactive with copper; b) creating a plasma from the gases described in step a) in a manner which provides a uniform ion density across the substrate surface; c) attracting ions and excited atoms from the plasma toward the substrate surface by applying an offset bias to the substrate; and d) removing a first portion of a copper layer overlying said substrate surface while maintaining a second portion of said copper layer overlying said substrate surface and while a portion of said copper layer interior of said substrate surface; e) removing said second portion of said copper layer overlying said substrate surface while maintaining a portion of said copper layer interior of said substrate surface; and f) removing a barrier layer overlying said substrate surface while maintaining the portion of said copper layer and said barrier layer interior of the substrate surface.
Claim 22
Dependent Claim
27 words
The method of claim 18, wherein the plasma created in step b) is sufficient to enable a copper etch rate of at least 1,000 Å per minute.
Claim 23
Dependent Claim
15 words
The method of claim 18, wherein the substrate temperature is greater than about 150° C.
Claim 24
Dependent Claim
105 words
The method of claim 18 or claim 19 or claim 20, wherein said first portion of said copper layer is removed using a first combination of gases designed for rapid removal of the copper layer, while said second portion of the copper layer is removed using a second combination of gases designed for a less rapid removal of said copper layer and for selectivity toward copper, while avoiding corrosion of an etched copper surface, and further removing said barrier layer using a third combination of gases designed for removal of said barrier layer while avoiding the corrosion of or while passivating said etched copper surface.
Claim 25
Dependent Claim
104 words
The method of claim 18 or claim 19 or claim 20, wherein said at least one gas which is chemically reactive with copper during the removal of said first portion of said copper layer is selected from a first group consisting of HCl, HBr, HI, SiCl 4 , BCl 3 , CHF 3 , CF 4 , SF 6 , Cl 2 , and combinations thereof, and wherein said at least one gas which is chemically reactive with copper during the removal of said second portion of said copper layer is selected from a second group consisting of HCl, HBr, HI, and combinations thereof.
Claim 26
Dependent Claim
153 words
The method of claim 18 or claim 19 or claim 20, wherein said at least one gas which is chemically reactive with copper during the removal of said first portion of said copper layer is selected from a first group consisting of HCl, HBr, HI, SiCl 4 , BCl 3 , CHF 3 , CF 4 , SF 6 , Cl 2 , and combinations thereof, and wherein said at least one gas which is chemically reactive with copper during the removal of said second portion of said copper layer is selected from a second group of reactive gases consisting of HCl, HBr, HI, SiCl 4 , BCl 3 , and combinations thereof in the presence of at least one non-reactive gas selected from the group consisting of N 2 , H 2 , Ar, He, Xe, CH 4 , C 2 H 6 , C 3 H 8 , and combinations thereof.
References Cited (Backward Citations)
US4298443A
Cited
US5186718A
Cited
US5320728A
Cited
US5569627A
Cited
JPH05275388A
Cited
US5387315A
Cited
US5578166A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-18 | 2003-04-19 | 2003-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-18 | 2007-04-19 | 2007-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-18 | 2011-04-19 | 2011-10-19 | $7700.00 | Window Closed / Lapsed |