US5962344A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plasma treatment method for PECVD silicon nitride films for improved passivation layers on semiconductor metal interconnections
Assignee: Vanguard International Semiconductor Corp
•
Filing: 1997-12-29
•
Granted: 1999-10-05
•
Expires: 2017-12-29
Abstract
Abstract A plasma treatment method used to form improved PECVD silicon nitride film passivation layers over metal interconnections on ULSI circuits is achieved. The process is carried out in a single PECVD reactor. After depositing a thin silicon oxide stress-release layer over the metal lines, a plasma-enhanced CVD silicon nitride layer is deposited, and subsequently a plasma treatment step is carried out on the silicon nitride layer. The use of a sufficiently thin silicon nitride layer eliminates photoresist trapping at the next photoresist process step that would otherwise be trapped in the voids (keyholes) that typically form in the silicon nitride passivation layer between the closely spaced metal lines, and can cause corrosion of the metal. The plasma treatment in He, Ar, or a mixture of the two, is then used to densify the silicon nitride layer and to substantially reduce pinholes that would otherwise cause interlevel metal shorts.
Inventors
- 👤 Yeur-Luen Tu
- 👤 Shiang-Peng Cheng
- 👤 Kwong-Jr Tsai
- 👤 Liang-Gi Yao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:58
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/694; H10P14/6943; H10P14/69433; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6532; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/662; H10P14/692; H10P14/6921; H10P14/69215
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
184 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer using an inert gas to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer; depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes while removing completely said photoresist without leaving photoresist residue between said metal lines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 2
Independent Claim
184 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer using an inert gas to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer; depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes while removing completely said photoresist without leaving photoresist residue between said metal lines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 3
Dependent Claim
24 words
The method of claim 1, wherein said metal layer is composed of aluminum/copper alloy having a thickness of between about 5000 and 9000 Angstroms.
Claim 4
Dependent Claim
44 words
The method of claim 1, wherein said silicon oxide is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of nitrous oxide (N 2 O) and silane (SiH 4 ), and is deposited to a thickness of between about 200 and 500 Angstroms.
Claim 5
Dependent Claim
48 words
The method of claim 1, wherein said silicon nitride layer is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of silane (SiH 4 ), ammonia (NH 3 ), and nitrogen (N 2 ), and is deposited to a thickness of between about 3000 and 5000 Angstroms.
Claim 6
Dependent Claim
87 words
The method of claim 1, wherein said plasma treatment in said inert gas is carried out in a plasma-enhanced chemical vapor deposition system comprising the steps of: a plasma treatment of said silicon nitride layer using said inert gas at a flow rate of between about 400 and 700 standard cubic centimeters per minute (sccm), at an RF power of between about 50 and 250 Watts, at a pressure of between about 2.5 and 4.0 milliTorr, and for a time of between about 50 and 100 seconds.
Claim 7
Dependent Claim
12 words
The method of claim 5, wherein said inert gas is helium (He).
Claim 8
Dependent Claim
12 words
The method of claim 5, wherein said inert gas is argon (Ar).
Claim 9
Dependent Claim
18 words
The method of claim 5, wherein said inert gas is a mixture of helium (He) and argon (Ar).
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein said via holes are etched using reactive ion etching (RIE) using a gas mixture of carbon tetrafluoride (CF 4 ) and trifluoromethane (CHF 3 ).
Claim 11
Dependent Claim
18 words
The method of claim 1, wherein said photoresist is stripped by plasma ashing in oxygen (O 2 ).
Claim 12
Dependent Claim
29 words
The method of claim 1, wherein said silicon oxide layer, said silicon nitride layer, and said plasma treatment are carried out consecutively in a plasma-enhanced chemical vapor deposition system.
Claim 13
Independent Claim
195 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer whereby said plasma treatment is in a plasma-enhanced chemical vapor deposition chamber using helium (He); depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes and removing completely said photoresist without leaving photoresist residue between said metal sines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 14
Independent Claim
195 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer whereby said plasma treatment is in a plasma-enhanced chemical vapor deposition chamber using helium (He); depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes and removing completely said photoresist without leaving photoresist residue between said metal sines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 15
Dependent Claim
24 words
The method of claim 12, wherein said metal layer is composed of aluminum/copper alloy having a thickness of between about 5000 and 9000 Angstroms.
Claim 16
Dependent Claim
44 words
The method of claim 12, wherein said silicon oxide is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of nitrous oxide (N 2 O) and silane (SiH 4 ), and is deposited to a thickness of between about 200 and 500 Angstroms.
Claim 17
Dependent Claim
47 words
The method of claim 12, wherein said silicon nitride is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of silane (SiH 4 ), ammonia (NH 3 ) and nitrogen (N 2 ), and is deposited to a thickness of between about 3000 and 5000 Angstroms.
Claim 18
Dependent Claim
63 words
The method of claim 12, wherein said plasma treatment using said helium is carried out at a flow rate of between about 400 and 700 standard cubic centimeters per minute (sccm), at an RF power of between about 50 and 250 Watts, at a pressure of between about 2.5 and 4.0 milliTorr, and for a time of between about 50 and 100 seconds.
Claim 19
Dependent Claim
31 words
The method of claim 12, wherein said via holes are etched using reactive ion etching (RIE) using a gas mixture of carbon tetrafluoride (CF 4 ) and trifluoromethane (CHF 3 ).
Claim 20
Dependent Claim
18 words
The method of claim 12, wherein said photoresist is stripped by plasma ashing in oxygen (O 2 ).
Claim 21
Independent Claim
202 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer whereby said plasma treatment is in a plasma-enhanced chemical vapor deposition chamber using a gas mixture of helium (He) and argon (Ar); depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes and removing completely said photoresist without cleaving photoresist residue between said metal lines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 22
Independent Claim
202 words
A method for fabricating an improved plasma-enhanced chemical vapor deposited passivation layer over metal interconnections on a substrate comprising the steps of: depositing a metal layer on said substrate; patterning said metal layer forming metal lines for said metal interconnections; depositing a silicon oxide layer on said patterned metal layer; depositing a silicon nitride layer on said silicon oxide layer by plasma-enhanced chemical vapor deposition at temperatures resulting in a nonconformal layer that is sufficiently thin to prevent keyholes in said silicon nitride layer between said metal lines; performing a plasma treatment on said silicon nitride layer to densify said silicon nitride layer, and thereby resulting in fewer pinholes in said silicon nitride layer whereby said plasma treatment is in a plasma-enhanced chemical vapor deposition chamber using a gas mixture of helium (He) and argon (Ar); depositing and patterning a photoresist layer to provide openings for via holes; etching said via holes in said silicon nitride layer and said silicon oxide layer to said metal lines; stripping said photoresist layer providing said via holes and removing completely said photoresist without cleaving photoresist residue between said metal lines, thereby completing said plasma-enhanced chemical vapor deposited passivation layer composed of said silicon nitride layer.
Claim 23
Dependent Claim
24 words
The method of claim 19, wherein said metal layer is composed of aluminum/copper alloy having a thickness of between about 5000 and 9000 Angstroms.
Claim 24
Dependent Claim
44 words
The method of claim 19, wherein said silicon oxide is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of nitrous oxide (N 2 O) and silane (SiH 4 ), and is deposited to a thickness of between about 200 and 500 Angstroms.
Claim 25
Dependent Claim
47 words
The method of claim 19, wherein said silicon nitride is deposited by plasma-enhanced chemical vapor deposition using a gas mixture of silane (SiH 4 ), ammonia (NH 3 ) and nitrogen (N 2 ), and is deposited to a thickness of between about 3000 and 5000 Angstroms.
Claim 26
Dependent Claim
68 words
The method of claim 19, wherein said plasma treatment using said gas mixture of He and Ar is carried out at a flow rate of between about 400 and 700 standard cubic centimeters per minute (sccm), at an RF power of between about 50 and 250 Watts, at a pressure of between about 2.5 and 4.0 milliTorr, and for a time of between about 50 and 100 seconds.
Claim 27
Dependent Claim
31 words
The method of claim 19, wherein said via holes are etched using reactive ion etching (RIE) using a gas mixture of carbon tetrafluoride (CF 4 ) and trifluoromethane (CHF 3 ).
Claim 28
Dependent Claim
18 words
The method of claim 19, wherein said photoresist is stripped by plasma ashing in oxygen (O 2 ).
References Cited (Backward Citations)
US5272361A
Cited
US5300460A
Cited
US5296404A
Cited
US5176790A
Cited
US5269879A
Cited
US5273920A
Cited
US5433823A
Cited
US5554418A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-04 | 2003-04-05 | 2003-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-04 | 2007-04-05 | 2007-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-04 | 2011-04-05 | 2011-10-05 | $7700.00 | Window Closed / Lapsed |