Method for forming DRAM stacked capacitor
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1997-05-05
•
Granted: 1999-08-24
•
Expires: 2017-05-05
Abstract
Abstract The present invention discloses a method for forming DRAM stacked capacitors by utilizing a densified oxide layer as an etch-stop for the wet etching process of an upper oxide layer in forming a contact hole for the stacked capacitor and thus, eliminating the need of a silicon nitride etch-stop layer and the occurrence of numerous processing difficulties normally observed in such stacked capacitor forming process. The lower oxide layer can be formed by a BPTEOS chemistry while the upper oxide layer can be formed by an ozone-TEOS chemistry.
Inventors
- 👤 Julie Huang
- 👤 Shing-Long Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:35
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/01; H10D1/041; H10D1/042; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/714; H10D1/716
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
103 words
A method for forming stacked capacitors in a semiconductor device comprising the steps of: depositing a first oxide layer on a pre-processed wafer having transistors, forming a first contact window and depositing a first conductive layer forming a conductive plug for electrical communication with the wafer, depositing a second oxide layer on said conductive plug and said first oxide layer, said second oxide layer having a substantially higher wet-etch rate than said first oxide layer, forming a second contact window in said second oxide layer stopping at said first oxide layer, and depositing layers of conductive and dielectric material forming said stacked capacitors.
Claim 2
Independent Claim
103 words
A method for forming stacked capacitors in a semiconductor device comprising the steps of: depositing a first oxide layer on a pre-processed wafer having transistors, forming a first contact window and depositing a first conductive layer forming a conductive plug for electrical communication with the wafer, depositing a second oxide layer on said conductive plug and said first oxide layer, said second oxide layer having a substantially higher wet-etch rate than said first oxide layer, forming a second contact window in said second oxide layer stopping at said first oxide layer, and depositing layers of conductive and dielectric material forming said stacked capacitors.
Claim 3
Dependent Claim
25 words
A method according to claim 1 further comprising the step of densifying said first oxide layer prior to the formation of said first contact window.
Claim 4
Dependent Claim
30 words
A method according to claim 1, wherein the wet-etch rate for said second oxide layer is at least five times faster than the wet-etch rate for said first oxide layer.
Claim 5
Dependent Claim
14 words
A method according to claim 1, wherein said conductive layer is deposited of polysilicon.
Claim 6
Dependent Claim
30 words
A method according to claim 1, wherein said first oxide layer being formed from a borophosphor TEOS (BPTEOS) reactant and said second oxide layer being formed from an ozone-TEOS reactant.
Claim 7
Dependent Claim
17 words
A method according to claim 1, wherein said first and said second oxide layers are inter-poly-oxide layers.
Claim 8
Dependent Claim
30 words
A method according to claim 1 further comprising the step of densifying said first oxide layer in a planarization process conducted at a temperature of not less than 950° C.
Claim 9
Dependent Claim
48 words
A method according to claim 1, wherein said step of depositing layers of conductive and dielectric material comprises: depositing a second conductive layer forming a lower electrode, depositing a dielectric layer on top of said second conductive layer, and depositing a third conductive layer forming an upper electrode.
Claim 10
Dependent Claim
16 words
A method according to claim 8, wherein said dielectric material layer is an oxide-nitride-oxide composite film.
Claim 11
Dependent Claim
123 words
A method according to claim 1, wherein said step of depositing layers of conductive and dielectric material comprises: depositing a second conductive layer forming a lower electrode, depositing a third oxide layer on said second conductive layer, said third oxide layer having a substantially higher wet-etch rate than said first oxide layer, wet etching partially said third oxide layer and said second conductive layer exposing said second oxide layer and forming a lower electrode for said stacked capacitor, wet etching and removing a residual third oxide layer and a residual second oxide layer, depositing a dielectric layer on top of said second conductive layer and forming an insulator for said stacked capacitor, and depositing a third conductive layer and forming an upper electrode.
Claim 12
Dependent Claim
32 words
A method according to claim 1 further comprising the step of stopping the formation of said second contact window in said second oxide layer at an end point in a wet-etch process.
Claim 13
Dependent Claim
20 words
A method according to claim 1, wherein a top surface of said first oxide layer serves as an etch-stop surface.
Claim 14
Dependent Claim
14 words
A method according to claim 1, wherein said semiconductor device is a DRAM cell.
Claim 15
Dependent Claim
34 words
A method according to claim 1, wherein the wet-etch rate for said second oxide layer is substantially faster than the wet-etch rate for said first oxide layer when exposed to a 10:1 BOE etchant.
Claim 16
Independent Claim
98 words
A method for forming stacked capacitor in a DRAM cell comprising the steps of: depositing a first oxide layer from a borophosphor TEOS (BPTEOS) reactant on a pre-processed wafer including transistors, forming a first contact window and depositing a first polysilicon layer forming a polysilicon plug for electrical communication with the wafer, depositing a second oxide layer from an ozone-TEOS reactant on said polysilicon plug and said first oxide layer, forming a second contact window in said second oxide layer stopping at said first oxide layer, and depositing layers of polysilicon and dielectric material forming said stacked capacitor.
Claim 17
Independent Claim
98 words
A method for forming stacked capacitor in a DRAM cell comprising the steps of: depositing a first oxide layer from a borophosphor TEOS (BPTEOS) reactant on a pre-processed wafer including transistors, forming a first contact window and depositing a first polysilicon layer forming a polysilicon plug for electrical communication with the wafer, depositing a second oxide layer from an ozone-TEOS reactant on said polysilicon plug and said first oxide layer, forming a second contact window in said second oxide layer stopping at said first oxide layer, and depositing layers of polysilicon and dielectric material forming said stacked capacitor.
Claim 18
Dependent Claim
20 words
A method according to claim 15, wherein said first and said second contact windows are formed by a wet-etch method.
Claim 19
Dependent Claim
13 words
A method according to claim 15, wherein said first oxide layer is densified.
Claim 20
Dependent Claim
22 words
A method according to claim 15, wherein said first oxide layer is densified at a temperature of not less than 950° C.
Claim 21
Dependent Claim
27 words
A method according to claim 15, wherein said forming step for said second contact window in the second oxide layer is carried out in a wet-etch method.
Claim 22
Dependent Claim
31 words
A method according to claim 15, wherein said second contact window is formed by an etchant having substantially higher selectively for said second oxide layer than for said first oxide layer.
Claim 23
Dependent Claim
14 words
A method according to claim 20, wherein said etchant is a 10:1 BOE solution.
Claim 24
Dependent Claim
45 words
A method according to claim 15, wherein said forming step for said stacked capacitor comprises: depositing a second polysilicon layer forming a lower electrode, depositing a dielectric layer on top of said second polysilicon layer, and depositing a third polysilicon layer forming an upper electrode.
Claim 25
Dependent Claim
16 words
A method according to claim 22, wherein said dielectric material layer is an oxide-nitride-oxide composite film.
References Cited (Backward Citations)
US5273925A
Cited
US5403767A
Cited
US5270241A
Cited
US5543346A
Cited
US5716884A
Cited
US5627094A
Cited
US5736450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-08-23 | 2003-02-22 | 2003-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-08-23 | 2007-02-22 | 2007-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-08-23 | 2011-02-22 | 2011-08-24 | $7700.00 | Window Closed / Lapsed |