Magnetic float polishing processes and materials therefor
Assignee: Oklahoma State University
•
Filing: 1997-09-30
•
Granted: 1999-08-03
•
Expires: 2017-09-30
Abstract
Abstract A methodology for finishing of HIP'ed Si3N4 balls from the as-received condition by magnetic fluid polishing. It involves mechanical removal of material initially using harder abrasives with respect to the work material (of different materials of progressively lower hardnesses and finer grain sizes) followed by final chemo-mechanical polishing (CMP) using preferably a softer abrasive for obtaining superior finish with minimal surface or subsurface defects, such as scratches, microcracks, or pits on the Si3N4 balls. High material removal rates (1 mu m/min) with minimal subsurface damage is obtained with harder abrasives, such as B4C or SiC (relative to Si3N4) due to the use of a flexible support system, small polishing loads (1N/ball), and fine abrasives but high polishing speeds (compared to conventional polishing) by rapid accumulation of minute amounts of material removed by microfracture. Final polishing of the Si3N4 balls using a softer abrasive, such as CeO2 (that chemo-mechanically react with the Si3N4 work material) results in high quality Si3N4 balls of bearing quality with a superior surface finish and damage-free surface.
Inventors
- 👤 Ranga Komanduri
- 👤 Ming Jiang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:12
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/30; F16C33/32; B; B24; B24B; B24B1/00; B24B1/005; B24B11/00; B24B11/02; C; C09; C09K; C09K3/00; C09K3/14; C09K3/1454; C09K3/1463
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
88 words
A process for finishing a workpiece to a desired size, sphericity and surface roughness, comprising placing the workpiece in a float chamber of a magnetic fluid polishing apparatus in contact with an appropriate quantity of magnetic fluid, said magnetic fluid containing an effective amount of a chemo-mechanical abrasive agent capable of forming a reaction layer upon said workpiece, said chemo-mechanical abrasive agent being of a hardness similar to that of the reaction layer but less than that of said workpiece, and polishing said workpiece to the desired specifications.
Claim 2
Dependent Claim
88 words
A process for finishing a workpiece to a desired size, sphericity and surface roughness, comprising placing the workpiece in a float chamber of a magnetic fluid polishing apparatus in contact with an appropriate quantity of magnetic fluid, said magnetic fluid containing an effective amount of a chemo-mechanical abrasive agent capable of forming a reaction layer upon said workpiece, said chemo-mechanical abrasive agent being of a hardness similar to that of the reaction layer but less than that of said workpiece, and polishing said workpiece to the desired specifications.
Claim 3
Dependent Claim
27 words
The process according to claim 1 where-in said chemo-mechanical abrasive agent is of a conventional hardness on a linear scale, of about 1/3 that of said workpiece.
Claim 4
Dependent Claim
15 words
The process according to claim 1 wherein said chemo-mechanical abrasive agent is CeO 2 .
Claim 5
Dependent Claim
191 words
A process for finishing a workpiece to a desired size, sphericity and surface roughness, comprising: (a) placing the workpiece in a float chamber of a magnetic fluid polishing apparatus in contact with an appropriate quantity of magnetic fluid, said magnetic fluid containing an effective amount of an abrasive agent; (b) in an initial polishing stage to achieve high removal rates with minimal subsurface damage, polishing said workpiece at a load of approximately 1N utilizing a first selected abrasive agent of a relatively coarse grit (400-500) and of a hardness greater than that of the workpiece at a high speed in the range of 2000-4000 rpm; (c) in an intermediate or semifinishing stage to achieve a desired sphericity, polishing said workpiece at a load of approximately 1N utilizing a second selected abrasive agent of a finer grit size than said first selected abrasive agent and of a hardness greater than that of said workpiece at a speed in the range of 1000-2000 rpm; and (d) in a final stage to achieve a desired surface finish, finishing said workpiece utilizing a chemo-mechanical abrasive agent having a hardness lower than that of said workpiece.
Claim 6
Dependent Claim
191 words
A process for finishing a workpiece to a desired size, sphericity and surface roughness, comprising: (a) placing the workpiece in a float chamber of a magnetic fluid polishing apparatus in contact with an appropriate quantity of magnetic fluid, said magnetic fluid containing an effective amount of an abrasive agent; (b) in an initial polishing stage to achieve high removal rates with minimal subsurface damage, polishing said workpiece at a load of approximately 1N utilizing a first selected abrasive agent of a relatively coarse grit (400-500) and of a hardness greater than that of the workpiece at a high speed in the range of 2000-4000 rpm; (c) in an intermediate or semifinishing stage to achieve a desired sphericity, polishing said workpiece at a load of approximately 1N utilizing a second selected abrasive agent of a finer grit size than said first selected abrasive agent and of a hardness greater than that of said workpiece at a speed in the range of 1000-2000 rpm; and (d) in a final stage to achieve a desired surface finish, finishing said workpiece utilizing a chemo-mechanical abrasive agent having a hardness lower than that of said workpiece.
Claim 7
Dependent Claim
19 words
The process according to claim 4 wherein said workpiece comprises a hard and brittle workmaterial including ceramics and glasses.
Claim 8
Dependent Claim
35 words
The process according to claim 4 wherein said workpiece comprises a ceramic workmaterial selected from the group consisting of Si 3 N 4 , SiC, ZrO 2 , Al 2 O 3 and ceramic composites.
Claim 9
Dependent Claim
15 words
The process according to claim 6 wherein said workpiece comprises Si 3 N 4 .
Claim 10
Dependent Claim
24 words
The process according to claim 4 wherein said first selected abrasive agent is selected from the group consisting of B 4 C and SiC.
Claim 11
Dependent Claim
24 words
The process according to claim 8 wherein said second selected abrasive agent is selected from the group consisting of B 4 C and SiC.
Claim 12
Dependent Claim
43 words
The process according to claim 4 wherein said chemo-mechanical abrasive agent is selected from the group consisting of CeO 2 , CaCO 3 , MgO, SiO 2 , Fe 2 O 3 , Fe 3 O 4 and Cr 2 O 3 .
Claim 13
Dependent Claim
15 words
The process according to claim 10 wherein said chemo-mechanical abrasive agent is CeO 2 .
Claim 14
Dependent Claim
25 words
The process according to claim 4 wherein said workpiece is an Si 3 N 4 ball and said chemo-mechanical abrasive agent is CeO 2 .
References Cited (Backward Citations)
US3695934A
Cited
US4306386A
Cited
US4821466A
Cited
US5070658A
Cited
US5048238A
Cited
US4965967A
Cited
US5185957A
Cited
US5214884A
Cited
US5449313A
Cited
US5577948A
Cited
US5460566A
Cited
US5384989A
Cited
US5575706A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-08-02 | 2003-02-01 | 2003-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-08-02 | 2007-02-01 | 2007-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-08-02 | 2011-02-01 | 2011-08-03 | $7700.00 | Window Closed / Lapsed |