US5897363A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Shallow junction formation using multiple implant sources
Assignee: Round Rock Research LLC
•
Filing: 1997-12-02
•
Granted: 1999-04-27
•
Expires: 2017-12-02
Abstract
Abstract Disclosed is a process for forming a shallow junction with a variable concentration profile gradation of dopants. The process of the present invention comprises, first providing and masking a surface on an in-process integrated circuit wafer on which the shallow junction is to be formed. Next, a low ion velocity and low energy ion bombardment plasma doping or PLAD operation is conducted to provide a highly doped inner portion of a shallow junction. In a further step, a higher ion velocity and energy conventional ion bombardment implantation doping operation is conducted using a medium power implanter to extend the shallow junction boundaries with a lightly doped outer portion. An anneal step follows. The result is a shallow junction with a variable concentration profile gradation of dopant. The junction is suitable for forming source and drain regions in MOS transistors, especially where a contact or interconnect is intended to engage the source and drain regions. The variable concentration profile gradation of dopants helps to maintain proper threshold voltage levels and reduces reverse bias current leakage.
Inventors
- 👤 Fernando Gonzalez
- 👤 Randhir Thakur
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 19:58
CPC Classifications
H; H10; H10P; H10P30/00; H10P30/20; H10P30/21; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/60; H10D30/601; H10D30/605; H10P30/202; H10P30/204; H10P30/212; H10P32/00; H10P32/10; H10P32/12; H10P32/1204; Y; Y10; Y10S; Y10S257/00; Y10S257/90
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
133 words
A method of forming an electrical structure on a substrate, the method comprising: forming a first doped region in a substrate with a PLAD operation, the first doped region having a first dopant concentration and extending from a surface of the substrate to a first depth of less then about 1000 Å, the first doped region being bounded within the substrate by a periphery, including a portion at the first depth; and forming a second doped region in the substrate, the second doped region having a second dopant concentration that is less than the first dopant concentration, a portion of the second doped region being bounded by the periphery of the first doped region, the second doped region extending to a second depth within the substrate that is greater than the first depth.
Claim 2
Independent Claim
133 words
A method of forming an electrical structure on a substrate, the method comprising: forming a first doped region in a substrate with a PLAD operation, the first doped region having a first dopant concentration and extending from a surface of the substrate to a first depth of less then about 1000 Å, the first doped region being bounded within the substrate by a periphery, including a portion at the first depth; and forming a second doped region in the substrate, the second doped region having a second dopant concentration that is less than the first dopant concentration, a portion of the second doped region being bounded by the periphery of the first doped region, the second doped region extending to a second depth within the substrate that is greater than the first depth.
Claim 3
Dependent Claim
18 words
A method as recited in claim 1, further comprising annealing the substrate after forming the second doped region.
Claim 4
Dependent Claim
44 words
A method as recited in claim 2, wherein annealing the substrate is conducted for a predetermined period of time sufficient to cause a more uniform distribution of dopant across both the first doped region and the second doped region than prior to the annealing.
Claim 5
Dependent Claim
17 words
A method as recited in claim 1, wherein the second depth is less than about 1000 Å.
Claim 6
Dependent Claim
75 words
A method as recited in claim 1, wherein the substrate comprises a silicon-containing material and an oxide layer positioned on the silicon-containing material, the first doped region being formed by causing a substantial portion of a first dopant to pass through the oxide layer and into the silicon-containing material, the second doped region being formed by causing a substantial portion of a second dopant to pass through the oxide layer and into the silicon-containing material.
Claim 7
Dependent Claim
22 words
A method as recited in claim 1, wherein forming the first doped region is conducted prior to forming the second doped region.
Claim 8
Dependent Claim
22 words
A method as recited in claim 1, wherein forming the second doped region is conducted prior to forming the first doped region.
Claim 9
Dependent Claim
17 words
A method as recited in claim 1, wherein forming the first doped region comprises a PLAD operation.
Claim 10
Dependent Claim
52 words
A method as recited in claim 8, wherein the PLAD operation is conducted at an energy in a range from about 5 KeV to about 15 KeV such that the first dopant concentration is in a range from about 1×10 19 dopant atoms/cm 3 to about 5×10 21 dopant atoms/cm 3 .
Claim 11
Dependent Claim
21 words
A method as recited in claim 9, wherein forming the second doped region comprises ion bombardment implantation operating without a plasma.
Claim 12
Dependent Claim
76 words
A method as recited in claim 10, wherein the ion bombardment implantation is conducted at an energy in a range from about 10 KeV to about 25 KeV such that the second dopant concentration is in a range from about 1×10 16 dopant atoms/cm 3 to about 1×10 19 dopant atoms/cm 3 , the ion bombardment implantation being conducted in a medium power implanter operating in a range from about 0 KeV to about 200 KeV.
Claim 13
Dependent Claim
58 words
A method as recited in claim 1, wherein the first doped region and the second doped region together comprise a source/drain region of an MOS transistor, the method further comprising forming a gate region over the substrate, the gate region having sides that are free of spacers, the source/drain region being formed substantially without underlapping the gate region.
Claim 14
Dependent Claim
37 words
A method as recited in claim 7, further comprising forming an electrically insulating layer over the surface prior to forming the first doped region, such that the first doped region is formed through the electrically insulating layer.
Claim 15
Dependent Claim
37 words
A method as recited in claim 13, further comprising forming a gate region on the surface prior to forming the electrically insulating layer, the electrically insulating layer being formed over the surface and over the gate region.
Claim 16
Dependent Claim
30 words
A method as recited in claim 2, further comprising annealing the substrate after forming the first doped region in addition to annealing the substrate after forming the second doped region.
Claim 17
Independent Claim
183 words
A method of forming an electrical structure on a substrate, the method comprising: conducing a PLAD operation on a surface of a substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region extending from the surface to a first depth of less than about 1000 Å and having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 1×10 21 dopant atoms/cm 3 ; conducting ion bombardment implantation without a plasma at an energy in a range form about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter operating in a range from about 0 KeV to about 200 KeV, a second doped region being thereby formed in the substrate, the second doped region extending from to a second depth within the substrate that is greater than the first depth, the second doped region having a second dopant concentration that is less than the first dopant concentration; and annealing the substrate.
Claim 18
Independent Claim
183 words
A method of forming an electrical structure on a substrate, the method comprising: conducing a PLAD operation on a surface of a substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region extending from the surface to a first depth of less than about 1000 Å and having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 1×10 21 dopant atoms/cm 3 ; conducting ion bombardment implantation without a plasma at an energy in a range form about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter operating in a range from about 0 KeV to about 200 KeV, a second doped region being thereby formed in the substrate, the second doped region extending from to a second depth within the substrate that is greater than the first depth, the second doped region having a second dopant concentration that is less than the first dopant concentration; and annealing the substrate.
Claim 19
Independent Claim
247 words
A method of forming an electrical structure on a substrate, the method comprising: providing a gate region n a substrate, the gate region being free of sidewall spacers; providing an electrically insulating layer formed over a surface of the substrate and over the gate region; conducting a PLAD operation on the surface of the substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 5×10 21 dopant atoms/cm 3 , the first doped region extending from the surface to a first depth of less than about 1000 Å; and conducting ion bombardment implantation without a plasma at an energy i a range from about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter, a second doped region being thereby formed in the substrate, the second doped region extending to a second depth within the substrate that is greater than the first depth, the second doped region further having a second dopant concentration in a range from about 1×10 16 dopant atoms/cm 3 to about 1×10 19 dopant atoms/cm 3 , a source/drain region of an MOS transistor being formed in the substrate by both the first doped region and the second doped region, the source/drain region being formed substantially without underlapping the gate region.
Claim 20
Independent Claim
247 words
A method of forming an electrical structure on a substrate, the method comprising: providing a gate region n a substrate, the gate region being free of sidewall spacers; providing an electrically insulating layer formed over a surface of the substrate and over the gate region; conducting a PLAD operation on the surface of the substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 5×10 21 dopant atoms/cm 3 , the first doped region extending from the surface to a first depth of less than about 1000 Å; and conducting ion bombardment implantation without a plasma at an energy i a range from about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter, a second doped region being thereby formed in the substrate, the second doped region extending to a second depth within the substrate that is greater than the first depth, the second doped region further having a second dopant concentration in a range from about 1×10 16 dopant atoms/cm 3 to about 1×10 19 dopant atoms/cm 3 , a source/drain region of an MOS transistor being formed in the substrate by both the first doped region and the second doped region, the source/drain region being formed substantially without underlapping the gate region.
Claim 21
Independent Claim
171 words
A method for forming an electrical structure, the method comprising: providing a semiconductor substrate; and forming a doped active region within the semiconductor substrate, the doped active region having a concentration of dopants that generally decreases with increasing depth into the semiconductor substrate, wherein forming the doped active region includes: implanting into the semiconductor substrate first dopant ions having energies in a range from about 5 KeV with a PLAD operation to about 15 KeV, the first dopant ions being implanted into the semiconductor substrate at a first concentration and to a first maximum depth less than about 1,000 Å; and implanting into the semiconductor substrate second dopant ions having energies in a range from about 10 KeV to about 25 KeV, the second dopant ions being implanted into the semiconductor substrate at a second dopant concentration that is less than the first dopant concentration and to a second maximum depth that exceeds the first maximum depth by an amount in a range from about 250 Å to about 750 Å.
Claim 22
Independent Claim
171 words
A method for forming an electrical structure, the method comprising: providing a semiconductor substrate; and forming a doped active region within the semiconductor substrate, the doped active region having a concentration of dopants that generally decreases with increasing depth into the semiconductor substrate, wherein forming the doped active region includes: implanting into the semiconductor substrate first dopant ions having energies in a range from about 5 KeV with a PLAD operation to about 15 KeV, the first dopant ions being implanted into the semiconductor substrate at a first concentration and to a first maximum depth less than about 1,000 Å; and implanting into the semiconductor substrate second dopant ions having energies in a range from about 10 KeV to about 25 KeV, the second dopant ions being implanted into the semiconductor substrate at a second dopant concentration that is less than the first dopant concentration and to a second maximum depth that exceeds the first maximum depth by an amount in a range from about 250 Å to about 750 Å.
Claim 23
Dependent Claim
30 words
A method as defined in claim 18, wherein the second dopant ions are implanted such that the doped active region has a substantially planar periphery at the second maximum depth.
Claim 24
Dependent Claim
49 words
A method as defined in claim 18, wherein implanting the first dopant ions and implanting the second dopant ions are conducted such that the doped active region forms a portion of an electrical device that is selected from the group consisting of a diode, a resistor, and a transistor.
Claim 25
Dependent Claim
50 words
A method as defined in claim 18, wherein the doped active region is a source/drain region and wherein the method further comprises, prior to forming the doped active region, forming a transistor gate stack on the semiconductor substrate, the transistor gate stack including a volume of an electrically conductive material.
Claim 26
Independent Claim
244 words
A method for forming an electrical structure, the method comprising: providing a semiconductor substrate having a top surface; and providing a volume of an electrically conductive material on a portion of the top surface of the semiconductor substrate; forming a first active region and a second active region within the semiconductor substrate and separated one from another, both the first active region and the second active region being positioned adjacent opposite sides of the volume of electrically conductive material, each of the first active region and the second active region being doped with a concentration of dopants that generally decreases with increasing depth into the semiconductor substrate, wherein forming each of the first active region and the second active region includes: implanting into the semiconductor substrate first dopant ions having energies in a range from about 5 KeV to about 15 KeV with a PLAD operation, the first dopant ions being implanted into the semiconductor substrate at a first concentration and to a first maximum depth less than about 1,000 Å; and implanting into the semiconductor substrate second dopant ions a range having energies in a range from about 10 KeV to about 25 KeV, the second dopant ions being implanted into the semiconductor substrate at a second dopant concentration that is less than the first dopant concentration and to a second maximum depth that exceeds the first maximum depth by an amount in a range from about 250 Å to about 750 Å.
Claim 27
Independent Claim
244 words
A method for forming an electrical structure, the method comprising: providing a semiconductor substrate having a top surface; and providing a volume of an electrically conductive material on a portion of the top surface of the semiconductor substrate; forming a first active region and a second active region within the semiconductor substrate and separated one from another, both the first active region and the second active region being positioned adjacent opposite sides of the volume of electrically conductive material, each of the first active region and the second active region being doped with a concentration of dopants that generally decreases with increasing depth into the semiconductor substrate, wherein forming each of the first active region and the second active region includes: implanting into the semiconductor substrate first dopant ions having energies in a range from about 5 KeV to about 15 KeV with a PLAD operation, the first dopant ions being implanted into the semiconductor substrate at a first concentration and to a first maximum depth less than about 1,000 Å; and implanting into the semiconductor substrate second dopant ions a range having energies in a range from about 10 KeV to about 25 KeV, the second dopant ions being implanted into the semiconductor substrate at a second dopant concentration that is less than the first dopant concentration and to a second maximum depth that exceeds the first maximum depth by an amount in a range from about 250 Å to about 750 Å.
Claim 28
Dependent Claim
23 words
A method as defined in claim 22, wherein both the first doped active region and the second doped active region are formed simultaneously.
Claim 29
Independent Claim
154 words
A method of forming an electrical structure on a substrate, the method comprising: forming a first doped region in a substrate with a PLAD operation, the first doped region having a first dopant concentration and extending from a surface of the substrate to a first depth of less than about 1000 Å, the first doped region being bounded within the substrate by a periphery, including a portion at the first depth; and forming a second doped region in the substrate, the second doped region having a second dopant concentration that is less than the first dopant concentration, a portion of the second doped region being bounded by the periphery of the first doped region, the second doped region extending to a second depth within the substrate that is greater than the first depth, said second depth exceeding the first depth by an amount in a range from about 250 Å to about 750 Å.
Claim 30
Independent Claim
154 words
A method of forming an electrical structure on a substrate, the method comprising: forming a first doped region in a substrate with a PLAD operation, the first doped region having a first dopant concentration and extending from a surface of the substrate to a first depth of less than about 1000 Å, the first doped region being bounded within the substrate by a periphery, including a portion at the first depth; and forming a second doped region in the substrate, the second doped region having a second dopant concentration that is less than the first dopant concentration, a portion of the second doped region being bounded by the periphery of the first doped region, the second doped region extending to a second depth within the substrate that is greater than the first depth, said second depth exceeding the first depth by an amount in a range from about 250 Å to about 750 Å.
Claim 31
Independent Claim
193 words
A method of forming an electrical structure on a substrate, the method comprising: conducting a PLAD operation on a surface of a substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region extending from the surface to a first depth of less than about 1000 Å and having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 1×10 21 dopant atom/cm 3 ; conducting ion bombardment implantation without a plasma at an energy in a range from about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter operating in a range from about 0KeV to about 200 KeV, a second doped a second depth within the substrate, the second doped region extending from to a second depth within the substrate that exceeds the first depth by an amount in a range from about 250 Å to about 750 Å, the second doped region having a second dopant concentration that is less than the first dopant concentration; and annealing the substrate.
Claim 32
Independent Claim
193 words
A method of forming an electrical structure on a substrate, the method comprising: conducting a PLAD operation on a surface of a substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region extending from the surface to a first depth of less than about 1000 Å and having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 1×10 21 dopant atom/cm 3 ; conducting ion bombardment implantation without a plasma at an energy in a range from about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter operating in a range from about 0KeV to about 200 KeV, a second doped a second depth within the substrate, the second doped region extending from to a second depth within the substrate that exceeds the first depth by an amount in a range from about 250 Å to about 750 Å, the second doped region having a second dopant concentration that is less than the first dopant concentration; and annealing the substrate.
Claim 33
Independent Claim
259 words
A method of forming an electrical structure on a substrate, the method comprising: providing a gate region on a substrate, the gate region being free of sidewall spacers; providing an electrically insulating layer formed over a surface of the substrate and over the gate region; conducting a PLAD operation on the surface of the substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 5×10 21 dopant atoms/cm 3 , the first doped region extending from the surface to a first depth of less than about 1000 Å; and conducting ion bombardment implantation without a plasma at an energy in a range form about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter, a second doped region being thereby formed in the substrate, the second doped region extending to a second depth within the substrate that exceeds the first depth by an amount in a range from about 250 Å to about 750 Å, the second doped region further having a second dopant concentration in a range from about 1×10 16 dopant atoms/cm 3 to about 1×10 19 dopant atoms/cm 3 , a source/drain region of an MOS transistor being formed in the substrate by both the first doped region and the second doped region, the source/drain region being formed substantially without underlapping the gate region.
Claim 34
Independent Claim
259 words
A method of forming an electrical structure on a substrate, the method comprising: providing a gate region on a substrate, the gate region being free of sidewall spacers; providing an electrically insulating layer formed over a surface of the substrate and over the gate region; conducting a PLAD operation on the surface of the substrate at an energy in a range from about 5 KeV to about 15 KeV to form a first doped region in the substrate, the first doped region having a first dopant concentration in a range from about 1×10 19 dopant atoms/cm 3 to about 5×10 21 dopant atoms/cm 3 , the first doped region extending from the surface to a first depth of less than about 1000 Å; and conducting ion bombardment implantation without a plasma at an energy in a range form about 10 KeV to about 25 KeV, the ion bombardment implantation being conducted in a medium power implanter, a second doped region being thereby formed in the substrate, the second doped region extending to a second depth within the substrate that exceeds the first depth by an amount in a range from about 250 Å to about 750 Å, the second doped region further having a second dopant concentration in a range from about 1×10 16 dopant atoms/cm 3 to about 1×10 19 dopant atoms/cm 3 , a source/drain region of an MOS transistor being formed in the substrate by both the first doped region and the second doped region, the source/drain region being formed substantially without underlapping the gate region.
References Cited (Backward Citations)
US4907048A
Cited
US5045901A
Cited
US5006477A
Cited
US5091763A
Cited
US5434440A
Cited
US5352914A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-04-26 | 2002-10-26 | 2003-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-04-26 | 2006-10-26 | 2007-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-04-26 | 2010-10-26 | 2011-04-27 | $7700.00 | Window Closed / Lapsed |