US5891528A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Printed circuit board process using plasma spraying of conductive metal
Assignee: Individual
•
Filing: 1996-10-02
•
Granted: 1999-04-06
•
Expires: 2016-10-02
Abstract
Abstract A printed circuit board is formed by selectively conditioning at least one surface of a substrate with a pattern including selected areas conditioned to receiving metal, and non-selected areas to which metal will not adhere; the surface is then plasma sprayed with metal to coat the selectively prepared areas.
Inventors
- 👤 Joe Turek
- 👤 Dan Gosselin
- 👤 Nanu Vahora
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:55
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/10; H05K3/14; H05K3/143; C; C23; C23C; C23C4/00; C23C4/01; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
143 words
A method for forming a printed circuit board, comprising: a) selectively conditioning at least one surface of a substrate to form a pattern including selected areas conditioned to receive copper and non-selected areas to which copper will not adhere, the conditioning step including roughening said surface sufficiently to render it receptive to copper from a plasma spray, thereafter applying to the roughened surface an adhesion-resistant material which is smooth/glossy such that copper does not adhere thereto, thereafter patterning the adhesion-resistant material by selectively removing said adhesion-resistant material to form the pattern, the layer of adhesion-resistant material being sufficiently thin such that the selected and non-selected areas are substantially coplanar without any grooves or ridges defining the pattern; b) plasma spraying the at least one surface with copper to coat the selected areas with copper while the non-selected areas remain substantially free of copper.
Claim 2
Independent Claim
143 words
A method for forming a printed circuit board, comprising: a) selectively conditioning at least one surface of a substrate to form a pattern including selected areas conditioned to receive copper and non-selected areas to which copper will not adhere, the conditioning step including roughening said surface sufficiently to render it receptive to copper from a plasma spray, thereafter applying to the roughened surface an adhesion-resistant material which is smooth/glossy such that copper does not adhere thereto, thereafter patterning the adhesion-resistant material by selectively removing said adhesion-resistant material to form the pattern, the layer of adhesion-resistant material being sufficiently thin such that the selected and non-selected areas are substantially coplanar without any grooves or ridges defining the pattern; b) plasma spraying the at least one surface with copper to coat the selected areas with copper while the non-selected areas remain substantially free of copper.
Claim 3
Dependent Claim
18 words
The method of claim 1, wherein the steps of conditioning the substrate surface comprises mechanically roughening the surface.
Claim 4
Dependent Claim
38 words
The method of claim 1, wherein the steps of conditioning comprises chemically treating the surface of the substrate, the surface having a surface activation energy level, wherein the step of chemically treating raises the surface activation energy level.
Claim 5
Dependent Claim
18 words
The method of claim 1, wherein steps a) and b) are performed on both surfaces of the substrate.
Claim 6
Independent Claim
113 words
A method for forming a printed circuit board, comprising the steps of: a) conditioning at least one surface of a substrate to form a conditioned surface to which copper will adhere; thereafter b) applying a layer of resist to the conditioned surface, the resist, after application, having a surface which is smooth/glossy such that copper does not adhere thereto; c) patterning the resist but not the underlying conditioned surface to expose areas of the conditioned surface to be coated with copper; and thereafter d) plasma spraying the at least one surface with copper to coat the exposed areas of the conditioned surface with copper while leaving the unexposed areas substantially free of copper.
Claim 7
Independent Claim
113 words
A method for forming a printed circuit board, comprising the steps of: a) conditioning at least one surface of a substrate to form a conditioned surface to which copper will adhere; thereafter b) applying a layer of resist to the conditioned surface, the resist, after application, having a surface which is smooth/glossy such that copper does not adhere thereto; c) patterning the resist but not the underlying conditioned surface to expose areas of the conditioned surface to be coated with copper; and thereafter d) plasma spraying the at least one surface with copper to coat the exposed areas of the conditioned surface with copper while leaving the unexposed areas substantially free of copper.
Claim 8
Dependent Claim
24 words
The method of claim 5, wherein the step of conditioning the at least one surface comprises mechanically roughening the surface by grit--blasting the surface.
Claim 9
Dependent Claim
38 words
The method of claim 5, wherein the step of conditioning comprises chemically treated the surface of the substrate, the surface having a surface activation energy level, wherein the step of chemically treating raises the surface activation energy level.
Claim 10
Dependent Claim
29 words
The method of claim 5, wherein the step of applying a layer of resist to the at least one surface comprises silk-screening a liquid film resist onto the surface.
Claim 11
Dependent Claim
31 words
The method of claim 5, wherein the step of applying a layer of resist to the at least one surface comprises hot roll laminating a dry film resist onto the surface.
Claim 12
Dependent Claim
50 words
The method of claim 5, wherein the step of applying a layer of resist comprises applying a photo-imagable resist to the at least one surface, and wherein the step of patterning the resist comprises selectively exposing areas of the photo-imagable resist to electromagnetic radiation, and developing the photo-imagable resist layer.
Claim 13
Dependent Claim
22 words
The method of claim 5, and including the further step of removing the resist from the substrate after the plasma spraying step.
Claim 14
Dependent Claim
16 words
The method of claim 5, wherein steps a)-d) are preformed on both surfaces of a substrate.
Claim 15
Independent Claim
151 words
A method for forming a printed circuit board with plated through holes, comprising: a) forming an hour-glass shaped opening in a substrate, the opening including angled sidewalls extending from each substrate surface and meeting intermediate the surfaces to form an hour-glass shaped opening through the substrate; b) roughening the substrate surfaces and the angled sidewalls sufficiently to render them conditioned for receipt of copper; thereafter c) coating onto the roughened substrate surfaces a layer of adhesion-resistant material having a smooth/glossy surface to which copper does not adhere; thereafter d) patterning the adhesion-resistant material but not the underlying roughened surface to expose the selected areas including the angled sidewalls for receipt of copper; and thereafter directing plasma spray of copper onto the at least one substrate surface, whereby the copper of the plasma spray coats the angled sidewalls of the opening with copper while the non-selected areas remain substantially free of copper.
Claim 16
Independent Claim
151 words
A method for forming a printed circuit board with plated through holes, comprising: a) forming an hour-glass shaped opening in a substrate, the opening including angled sidewalls extending from each substrate surface and meeting intermediate the surfaces to form an hour-glass shaped opening through the substrate; b) roughening the substrate surfaces and the angled sidewalls sufficiently to render them conditioned for receipt of copper; thereafter c) coating onto the roughened substrate surfaces a layer of adhesion-resistant material having a smooth/glossy surface to which copper does not adhere; thereafter d) patterning the adhesion-resistant material but not the underlying roughened surface to expose the selected areas including the angled sidewalls for receipt of copper; and thereafter directing plasma spray of copper onto the at least one substrate surface, whereby the copper of the plasma spray coats the angled sidewalls of the opening with copper while the non-selected areas remain substantially free of copper.
Claim 17
Dependent Claim
22 words
The method of claim 13, wherein the opening is formed with the sidewalls having an angle greater than 10° from the vertical.
Claim 18
Dependent Claim
22 words
The method of claim 13, wherein the hour-glass shaped opening is formed by drilling vertically-aligned holes in first and second substrate surfaces.
Claim 19
Dependent Claim
22 words
The method of claim 13, wherein the step of roughening the angled sidewalls for receiving copper is accomplished by grit-blasting the sidewalls.
Claim 20
Dependent Claim
22 words
The method of claim 13, wherein the step of roughening the angled sidewalls for receiving metal is accomplished by etching the sidewalls.
References Cited (Backward Citations)
US2599710A
Cited
US4263341A
Cited
US4424408A
Cited
US4678738A
Cited
US4921721A
Cited
US4940623A
Cited
US5391404A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-04-05 | 2002-10-05 | 2003-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-04-05 | 2006-10-05 | 2007-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-04-05 | 2010-10-05 | 2011-04-06 | $7700.00 | Window Closed / Lapsed |